Evaluation of the thermal comfort performance ofdifferent knitted fabrics and fibre blends suitable for skin
layer of firefighters protective clothing
Nazia Nawaz, OlgaTroynikov
Royal Melbourne Institute of Technology, Australia
1Corresponding author: [email protected]
8/6/2019 1-nazia
2/24
RMIT University2008 Information Technology Services 2
Introduction
Protective clothing is required to shield the wearers from a variety of
hazardous environments or extreme conditions encountered by humans in
some industries, military or firefighting.
Firefighters protective clothing Firefighters protective clothing plays a vital role for their protection against
heat, hot liquids, chemicals and mechanical impacts.
The protective clothing facilitates the firefighter to approach the fire to
rescue people from fire and to fight the fire.
Modern firefighters clothing is a multi-layered garment assembly which isusually worn over an undergarment (skin layer).
8/6/2019 1-nazia
3/24
8/6/2019 1-nazia
4/24
RMIT University2008 Information Technology Services 4
Firefighting and thermal comfort
To provide thermal comfort to the human body the garment next to skin must
have three important attributes: to absorb
Heat
Vapour
Liquid perspiration from skin and
then transfer these to the outside of the garment
Thermal comfort and fabric propertiesThermal comfort properties of textile fabrics are actually influenced by
the type of fibre
spinning method of yarns
yarn count
yarn twist yarn hairiness
fabric thickness,
fabric cover factor
fabric porosity and finish
8/6/2019 1-nazia
5/24
RMIT University2008 Information Technology Services 5
Background
Milenkovic et al. (2009) demonstrated that fabric thickness, enclosed still air
and external air movement are the major factors that affect the heat transfer
through fabric.Ozdil (2007) experimentally verified that yarn properties such as yarn count,
yarn twist and spinning process influence thermal comfort properties of 11 rib
knitted fabrics. He verified that,
The 1 1 rib fabrics produced from finer yarns showed lower thermal
conductivity and higher water vapour permeability values than coarser
yarns counts.
Combed yarn showed the higher water vapour permeability
By increasing yarn twist used for 1 1 rib fabrics , thermal and water
vapour permeability of the fabrics was also increased.
Thermal resistance values decreased as the twist coefficient of yarn
increased. Thermal resistance values of fabrics knitted with combed
cotton yarns were lower than the fabrics knitted with carded cotton yarns.Milenkovic, L., Skundric, P., Sokolovic, R., Nikolic, T., (1999). "comfort Properties of Defence Protective clothing." The scientific Journal FactaUniversities 1(4): 101-106.zdil, N., A. MarmaralI, et al. (2007). "Effect of yarn properties on thermal comfort of knitted fabrics." International Journal of Thermal Sciences
46(12): 1318-1322.
8/6/2019 1-nazia
6/24
RMIT University2008 Information Technology Services 6
Background
Arzu Marmarali (2009) studied thermal comfort properties of blended yarns
and knitted fabrics of Cotton /Soybean fibres and Cotton/Seacell fibres in
different blend ratios and found that,
The thermal resistance value of 100% cotton fabric was significantly
higher than whole blended materials.
50/50% blend ratio of both fabrics (Co/Seacell, Co/Soybean) had the
lowest thermal resistance values than the other blend ratios and that was
due to lower fabric thickness value of 50/50% Co/SeaCell and
Co/Soybean fabrics. Therefore with the decreasing of fabric thickness,
thermal resistance decreases.
Troynikov et.al (2011) studied moisture management properties of wool/
polyester and wool/bamboo knitted in single jersey fabrics for the
sportswear base layers and concluded that,
Blending wool fibre with polyester fibre and, in particular, wool fibre with
regenerated bamboo fibre, improved moisture management properties
than fabrics in wool fibre or regenerated bamboo fibre without blending.
Troynikov, O., et all, Wiah, W., (2011). "Moisture management properties of wool/polyester and wool/bamboo knitted fabrics for sportswear baselayer." Textile Research Journal 0: 1-11.Arzu Marmarali, M. B., Tuba Bedez Ute, Gozde Damci (2009). Thermal comfort Properties of Blended Yarns Knitted Fabrics. ITMC. Casablanca,
Morocco.
8/6/2019 1-nazia
7/24
RMIT University2008 Information Technology Services 7
Objective of the study
The Objective of present study is:
To evaluate thermal and moisture management properties of six commercially
available knitted fabrics of different fibre blends and knitted structures for
skin layer garments of firefighters protective clothing The assessment and ranking of their thermal and moisture management
performance.
8/6/2019 1-nazia
8/24
RMIT University2008 Information Technology Services 8
Materials and methods
Following are six commercially available knitted fabrics having different
fibre content and knit structure that were evaluated
100% Merino wool
60% Merino Wool/ 40% Bamboo
100%Cotton
94% Merino wool/ 6% spandex
100%Polyester
52% Merino wool / 48% Biophyl
8/6/2019 1-nazia
9/24
RMIT University2008 Information Technology Services 9
Fabric physical properties
Fabric mass per unit area (gram / meter square)
Fabric thickness (mm)
Fabric density (No. of wales/cm and No. of courses/cm)
Fabric Moisture management properties
For evaluation of fabrics moisture management properties Moisture
Management Tester (MMT) was used according to American Association
of Textile Chemists and Colourists (AATCC) Test Method 1952009.
Figure 1. Moisture management tester Figure 2. Schematic view of tester sensors
8/6/2019 1-nazia
10/24
RMIT University2008 Information Technology Services 10
Moisture management tester indices
A series of indexes are defined and calculated to characterize liquid
moisture management performance of the test sample by using moisture
management tester, which are as follow;
Top wetting time WTt and bottom wetting time WTb Top absorption rate (ARt) and bottom absorption rate (ARb)
Top max wetted radius (MWRt) and bottom max wetted radius (MWRb)
Top spreading speed (SSt) and bottom spreading speed (SSb)
Accumulative one-way transport index (AOTI) and overall moisture
management capacity (OMMC)
8/6/2019 1-nazia
11/24
RMIT University2008 Information Technology Services 11
The OMMC is an index indicating the overall capacity of the fabric to manage
the transport of liquid moisture, which includes three aspects1. Average moisture absorption rate at the bottom surface
2. One-way liquid transport capacity
3. Maximum moisture spreading speed on the bottom surface
The larger the OMMC is the higher the overall moisture management ability of
the fabric is.According to AATCC Test Method 1952009, the indices are graded and
converted from value to grade based on a five grade scale (15). The five
grades of indices represent:
1 Poor
2 Fair3 Good
4 Very good
5 Excellent
Moisture management tester indices
8/6/2019 1-nazia
12/24
RMIT University2008 Information Technology Services 12
Table 1. Grading of MMT indices
8/6/2019 1-nazia
13/24
RMIT University2008 Information Technology Services 13
Fabric thermal properties (Thermal and water vapour resistance)
Thermal resistance and water vapour resistance of fabrics were
evaluated using sweating guarded hot plate according to ISO 11092.
Sweating guarded hot plate is able to simulate both heat and moisture
transfer from the body surface through the clothing layers to the
environment. It measures both the thermal resistance (insulation
value) and water vapour resistance of fabrics.
Figure 3. Sweating Guarded Hot Plate Figure 4. Schematic diagram of sweating guarded hot plate
8/6/2019 1-nazia
14/24
RMIT University2008 Information Technology Services 14
Fabrics thermal resistance
For the determination of thermal resistance of the sample, the air
temperature is set to 20 rC and the relative humidity is controlled at 65%.
Air speed generated by the air flow hood is 1 m/s. After the system
reaches steady state, total thermal resistance of the fabric is governed by:
HTaTsARct /)( ! (1)
Where,
Rctis the total thermal resistance plus the boundary air layer measured
in m K/W,
A, the area of the test section in m
Ts, the surface temperature of the plate in K
Ta, the temperature of ambient air in K
H, the electrical power in Watts
8/6/2019 1-nazia
15/24
RMIT University2008 Information Technology Services 15
Fabrics water vapour resistance
To measure the water vapour resistance of the fabric air temperature is set
at 35 rC and relative humidity is controlled at 40%.After a steady state isreached, the total evaporative resistance of the fabric is calculated by:
HPaPst /)(Re !
Where,Ret, is total vapour resistance provided by liquid barrier, fabric and
boundary air layer measured in m2KPa/W)
A, the area of test section in m2
Ps, the water vapour pressure at plate surface in Pa
Pa, the water vapour pressure of the air on PaH, the electrical power in Watts
(2)
8/6/2019 1-nazia
16/24
RMIT University2008 Information Technology Services 16
Fabriccode
Fibrecomposition
Construction Fabricweight(g/m2)
Fabricthickness
(mm)
No. ofwales/c
m
No. ofcourses
/cm
SJ1 100% Merinowool
Single Jersey 139 0.35 18 18
SJ2 60% Merino
Wool/ 40%Bamboo
Single Jersey 156 0.34 16 16
SJ3 100%Cotton Single Jersey 149 0.47 19 15
SJ4 94% Merinowool/ 6%spandex
Single Jersey 185 0.55 20 20
IM1 100%Polyest
er
Interlock based mock mesh 168 0.61 16 16
IM2 52% Merinowool / 48%
Biophyl
Interlock based mock mesh 216 0.97 16 12
Results and discussion
Table 2. Physical and structural properties of sample fabrics
8/6/2019 1-nazia
17/24
RMIT University2008 Information Technology Services 17
MoistureManagement Properties of sample fabrics
Table 3. MMT results in value
Fabric code WTt(sec)
WTb(sec)
ARt(%/sec)
ARb(%/sec)
MWRt(mm)
MWRb(mm)
SSt(mm/sec)
SSb(mm/sec)
AOTI(%)
OMMC
SJ1CV
63.3121.265
50.5151.343
3.6711.414
5.1170.290
2.51.414
51.414
0.3651.414
0.9591.414
319.1820.011
0.4480.112
SJ2CV
7.8830.071
5.0000.137
8.1520.236
5.9250.114
12.50.282
12.50.282
1.2860.097
3.1020.098
133.3960.251
0.3790.030
SJ3CV
41.2550.249
5.4160.979
8.0610.194
14.2860.276
13.333
0.216
13.3330.216
0.3490.419
1.6000.614
102.1180.394
0.2440.383
SJ4
CV
3.281
1.084
29.274
1.064
7.153
0.046
6.853
0.181
5
0
10
0
3.131
1.035
1.154
0.043
500.714
0.033
0.521
0.057
IM1CV
30.6171.165
47.0631.242
39.8940.953
5.2000.548
7.50.471
7.50.471
0.9471.280
0.9411.329
102.3990.283
0.2030.397
IM2CV
119.9530
3.8350.250
00
5.0690.561
00
7.50.471
00
0.8980.091
434.1050.184
0.4870.036
Results and discussion
8/6/2019 1-nazia
18/24
RMIT University2008 Information Technology Services 18
0
1
2
3
4
5
Gra
e
Top
Tt rade 2 3 2 4 2 1 5
ottom
Tb rade 2 3 5 3 5 2 2 4
S 1 S 2 S 3 S 4 IM1 IM2
Figure 5 Tt and Tb grades of sample fabrics
0
0 51
15
2
25
3
35
Gra
e
Top
Rt grade 1 1 1 1 3 1
ottom
Rb grade 1 1 2 1 1 1
S
1 S
2 S
3 S
4 IM1 IM2
Figure 6 Rt and Rb (%/sec) grades of sample fabrics
Results an iscussion
8/6/2019 1-nazia
19/24
8/6/2019 1-nazia
20/24
RMIT University2008 Information Technology Services 20
0
2Grade
A TI
MM 2 2 2
S S 2 S S IM IM2
Figure 9. A TI and MM grades for sample fabrics
These results show that S , S and IM2 have better moisture managementproperties as compared to the other sample fabrics of the study. These threefabrics are composed of 00 wool, wool/spandex and wool/biophyl and
having single jersey structures
Results and discussion
8/6/2019 1-nazia
21/24
RMIT University2008 Information Technology Services 21
Thermal properties (Thermal and vapour resistance)
Results and discussion
0.00 0.008 0.00
0.0110.01
0.02
0
0.00
0.01
0.010.02
0.02
0.0
0.0
S 1 S 2 S S IM1 IM2
Fabric code
MeanR
ct
Mean Rct (m / )
Figure 10. Thermal resistance (Rct) of sample fabrics
8/6/2019 1-nazia
22/24
RMIT University2008 Information Technology Services 22
2.0 . 2. 22.
2.8
.
0
2
SJ SJ2 SJ SJ IM IM2
Fab i e
MeanRet
Mean Ret m a/
Results an is ussi n
Figure . ater vapour resistance Ret of sample fabrics
8/6/2019 1-nazia
23/24
RMIT University2008 Information Technology Services 23
Conclusion
The results and discussions demonstrate that
wool and wool blends are the most suitable fabric to be used next to
skin to achieve thermal comfort
The fibre content, fabric construction and fabric thickness influence
thermal comfort significantly.
Therefore it can be concluded that 100% wool and wool blends with
spandex and bamboo (SJ1, SJ2 and SJ4) in single jersey structure are more
suitable to use next to skin than SJ4, IM1 and IM2.
100% cotton in single jersey structure can also be a good choice because it
has lower thermal and water vapour resistance like SJ1, SJ2, and SJ3 but
not in extremely hot environments like firefighting where body perspiresheavily in liquid form and cotton is unable to provide better liquid moisture
transfer properties like wool and wool blends to keep skin dry.