Oligomer remover and dye machine cleaner for polyester textiles
Citation preview
Oligomer is a smaller chain length of polyester made up of two or more molecules of basic ethylene terephthlate i.e. dimer or trimer, produced as a side reaction during the manufacture of polyester. The Oligoester because of its smaller chain length is in the form of a fine powder which is entrapped is basic polymer and migrates to the surface during high temperature polyester dyeing.
cyclic tris (ethylene terephthalate)
Higher the depth more is the
displacement of Oligomer to the fibre
surface. Typically polyester fibres
contain between 1.5-3.5% by mass of
low molecular esters, the principal
oligomer being cyclic tris (ethylene
terephthalate) with smaller quantities of
dimer, pentamer & other compounds.
Approximately 0.1 % to 1.0 % of
Oligomer is produced as a side reaction
in the manufacture of basic polyester.cyclic tris (ethylene terephthalate)
Spinning characteristics impaired. Filtration effect (inside – out variation) due to build up of
Oligomers in package. Reduced liquor flow through package of yarn because
spindle perforations are choked & improper pump pressure due to deposits on pump.
Variation in rate of rise of temperature due to deposits on heating elements
Dusting during coning & white particle deposits cause dulling of the yarn/ fabric especially in dark shades i.e. black & navy etc.
Higher energy costs Presence can cause nucleation & growth of dye crystals
or agglomeration of dye particles & hence dye spots, Duller shades, unlevelness & poor fastness.
Need for more frequent cleaning of dyeing & winding machines, hence increased down time & lower efficiency.
Those skilled in the art have therefore tried to remove oligomers from polyester by means of various after-treatment methods.
For example, it is known that oligomers may partly be eliminated by rinsing the polyester with hot water or by subjecting the polyester to an alkaline reductive after-treatment in the presence of a tenside, for example a fatty acid polyglycol ester, at elevated temperatures.
However, cyclic oligomers may be difficult to remove and resistant to such an alkaline post treatment. Therefore, to be effective, alkaline treatment must be severe, which results in a significant loss of polyester fiber material.
Organic solvents have also been used to try to remove oligomers from polyester but it is difficult to find one that is compatible with and non-injurious to the textile material.
Chlorinated hydrocarbons, fluorinated hydrocarbons and hydrocarbons themselves have also been used in the art to remove oligomer deposits.
All of the before-mentioned treatments used in the art pose production problems along with time and cost issues.
Accordingly, there is a need in the art for removing oligomer deposits that results in minimal interruptions in production and poses little threat to the quality of the polyester or polyester textile product.
Cyclic tris (ethylene terephthalate) is insoluble in water. Solubility is increased in presence of carriers like Dylev-EC, Dylev-CB , Dylev-DIF promotes migration of the trimer to the surface of fibre. But a dispersing agent like Dytec-DAN should be present to prevent crystallization & deposition of the oligomers.The longer the dyeing time the more oligomers will be released. Dark shades may produce more oligomer than paler shades because the dyeing time is longer.
When oligomers are released from polyester fibre, after some time at 130ºC, there will not be an efficient dispersing agent in the bath to prevent crystillization of the oligomers, and to prevent small particles of oligomers coming together to form agglomerates, & depositing on the yarn & the machine. Altrasperse-OLG liquid will maintain the oligomers in fine dispersion form & prevent redepositing of the trimers on the fabric so that when the machine is drained more oligomer goes down the drain.
Receipe during dyeing:In the case of dark shades and/ or long dyeing times, the following formulation is recommended :0.5 – 2 g/l Altrasperse-OLG liquid0.5-1.0g/l Dylev DIF / Dylev-CB0.5 g/l Dytec-DAN
Receipe during alkaline weight reduction of polyester:During alkaline weight reduction of polyester terephthalic acid is generated & to keep it in dispersion form Altranol-OR is very effective. Altranol-OR act as a effective micronizer & disperser of terephthalic acid.
Altranol-OR 1-2 g/l 75-80ºC for 20-30 mins
100-130ºC Warm rinsing
Weight reductionNeutralization
Altranol-OR(75-80ºC)
The dyeing machine to be cleaned is filled with water and the following is added:
3-5 g/l Altranol-ORM
4-6 ml/l Caustic soda solution 50%
1-2g/l Sodium hydrosulphite
Then heated upto 135ºC and treated for 20-40 mins. If possible, drain
immediately and rinse. Otherwise, cool to approx. 90ºC, drain and rinse.
On dyeing machines such as jets and overflows the additional use of a CO
back cloth has proved of advantage to increase the cleaning effect further.
In order to assess performance in dispersing oligomers, the degree of dispersion was compared with and without Altranol-OR in the black paper filtration of oligomers, extracted with the use of dioxane into an acidic or alkaline solution.
1. Test on dispersion in acidic solution (to simulate oligomer remaining during dyeing)
Oligomer solution 10 cc/200 ccAltrasperse-OLG 1-2 g/lAcetic acid pH=5
The dispersing agent was add to the test solution with pH adjusted to 5 using acetic acid while being stirred. After the temperature was raised to 130 ゜ C then cooled to 80 ゜ C, suction filtration was carried out using black filter paper.
2. Test on dispersion during weight reduction Test Purpose: Dispersion of terephthalic acid generated by weight
reductionSpecimen: Liquor after weight reductionTest items: Vacuum filter(Using black coloured filter paperTest condition
Products Blank 1 Test No-1 Blank-2 Test No-2
Liquor after weight reduction
20% solution
20% solution
5% solution
5% solution
Altranol-OR
--- 2 g/l --- 2 g/l
Acetic acidpH
4.5-5.5 4.5 - 5.5 4.5 – 5.5 4.5 – 5.5
Blank
20% liquid of caustic treatment
20% liquid of caustic treatment
Altranol-OR(2 g/l)
OFFICE ADDRESS :-403, “Antariksh”, Makwana Road,Marol Naka, Andheri (E), Mumbai – 400 059
Tel.- 91-22-4221 6789 (30 Lines) 91-22-6692 4112Fax - 91-22-2836 6434
Email ID – ketan@lnchem.in lnchem@vsnl.com
FACTORY ADDRESS :-D- 14 /10, T.T.C. M.I.D.C Industrial area,Turbhe , P.O. K.U.Bazar,Navi Mumbai – 400 705
Tel.-91- 22- 4141 9899 (30 Lines)Fax -91- 22- 4141 9888
Recommended