Sikagard 706 Thixo, New Product Showcase

GREG DOLENC

NEW PRODUCT SHOWCASESIKAGARD 706 THIXO

May 3, 20232

SIKAGARD®-706 THIXO

Thixotropic consistency, Non-drip Low volatility, Outstanding

penetration Low evaporation, water-based, Low VOC, High alkaline

resistance Freeze and thaw with de-icing

salt stress resistant

Silane based, cream type

May 3, 20233

SIKAGARD®-706 THIXO

Immediately after application 30 minutes after application

Silane based, cream type

Problem-free “overhead” application

Already treated areas are clearly visible

Low operation cost Problem-free cleaning of

equipment Application by airless spray

brush or rollerMay 3, 20234

SIKAGARD®-706 THIXO

Low wastage when working overhead

No visible traces after application

Loss-free application High coverage rates Single step application

up to 400 / 500 g/m²

Silane based, cream type

May 3, 20235

SIKAGARD®-706 THIXO

Silane based, cream type

May 3, 20236 New Product Showcase / BCRAO Skagard 706 Thixo

SIKAGARD®-706 THIXO

Corporate Brochures Technology & Concept, for

Designer & Contractor

Technical ArticlesSika & Third Parties

Technical & Commercial Presentations

Silane based, cream type

Hydrophobic Impregnations

8Marketing & Technical Tools

Technical Articles(Sika & Third Parties)

Corporate Brochures (Technology & Concept, for

Designer & Contractor)

Technical & commercial presentations

9Value Selling for Specifiers

Hydrophobic engineering

Specification support

Supporting documentation

Compatible systems (coatings and corrosion inhibitor)

Sika references

Long term experience (>15 years)

10Value Selling for Contractors

Application engineering

Method statement

Job site support

Testing facilities

Compatible systems (coatings and corrosion inhibitor)

Sika references

11

12

Influence of Cracks[3]

• Objective of the Study:• To show the influence of crack in the effectiveness

of hydrophobic treatment using different types of product (high active content silane liquid or cream, low active content silane/siloxane)

• Summary of the results: Importance of the type of product used in the durability

behaviour Best performance achieved with cream Silane No long term protection achieved with low active

silane/siloxane Effective protection achieved even if the treatment occurs

before the crack appears

13For Different Substrates

Concrete Brick Natural & Artificial Stone

14

15

Standard Tests (Alberta B388)Requirement (example)

Sealer Type Water uptake in % to a control non treated

Before Abrasion After Abrasion

Type 1a 82,5% 75%

Type 1b - 86%

Type 1c - 85%*

Note*: 144 grams abrasion instead of usual 72 grams for type 1a & 1b

16

StandardsCanada (Alberta B388):

Requirements: Reduction of water uptake after surface abrasion Reduction of water uptake after alkali exposure Water vapour transmission Etc.

Other Standards: Quebec Department of Transport MTQ Standard 3601

17

In general, there are three different levels of these Sika protection systems:

System 1:Durable concrete protection

System 2:Durable concrete andreinforcement protection

System 3:High performance protectionfor extreme conditions

Sikagard deep penetratinghydrophobic impregnation

Sika FerroGard corrosion inhibitorSikagard deep penetratinghydrophobic impregnation

Sika FerroGard corrosion inhibitorSikagard deep penetratinghydrophobic impregnationSikagard protective coating

Sika Competence in Complete Concrete Protection

For exposed concrete structuresshowing no visible concrete defects(crack width < 0.3 mm)

For severely exposed or weakconcrete with a high risk of steelcorrosion

For severely exposed or weakconcrete with a high risk of cracking

1

1

2

1

23

12

12

3

1

18

Standard Tests (Alberta B388)Classification:

Type 1: Penetrating sealers for use of traffic bearing exposed to abrasion

Type 1a: for sheltered conditions – relative moisture content of substrate not

exceeding 55% Type 1b: for outdoor condition where the relative

moisture content of substrate not exceeding 70%

Type 1c: low VOC, high performance. For application in outdoor

conditions to new bridges and overlays cast with low water cement ratio

(0,30 – 0,45) where the relative moisture content is maximum 80%

For more information contact one of our specialists: