Synthesis of Graphene on Gold
Tuba Oznuluer1
, Ercag Pince2
, Emre O. Polat2
, Osman Balci2
, Omer Salihoglu2
,Coskun Kocabas2,*
1 Ataturk University, Department of Chemistry, Erzurum, Turkey
1Advanced Research Laboratories, Department of Physics,Bilkent University, 06800, Ankara,Turkey
ABSTRACT: Here we report chemical vapor deposition of graphene on gold surface at
ambient pressure. We studied effects of the growth temperature, pressure and cooling process
on the grown graphene layers. The Raman spectroscopy of the samples reveals the essential
properties of the graphene grown on gold surface. In order to characterize the electrical
properties of the grown graphene layers, we have transferred them on insulating substrates
and fabricated field effect transistors. Owing to distinctive properties of gold, the ability to
grow graphene layers on gold surface could open new applications of graphene in
electrochemistry and spectroscopy.
7/30/2019 Synthesis of Graphene on Gold - ArXiv
2/12
Graphene, the two-dimensional (2D) crystal of sp2 hybridized carbon, provides unique
electronic1 and mechanical properties2. Recent progress on synthesis of graphene on large
area substrates3 fosters new applications of the 2D crystal. High speed electronics4 and
macroelectronics5 are two examples of these emerging applications. Catalytic decomposition
of hydrocarbons on transition metals provides a more promising method for large area growth
of high quality graphene layers. Various methods such as chemical vapor deposition (CVD)3,
surface segregation6, solid carbon source7 and ion implantation8 have been used to synthesis
of graphene layers on metal surfaces. Nickel9 and copper10 are the most commonly used metal
substrates for the growth. Other metals such as ruthenium, iridium, platinum, palladium, and
cobalt have also been used as a substrate for chemical vapor deposition of graphene10-13.
Ability to grow graphene on different metals provides opportunities for new applications and
more inside to understand the growth mechanism. In this Letter we show a method to directly
grow graphene layers on gold surface in various forms such as thin films, foils and wires. The
Raman spectroscopy reveals the essential features of the grown graphene layers. In order to
characterize the electrical properties of the grown graphene layers, we have transferred them
on insulating substrates and fabricated back gated field effect transistors (FET) that use the
graphene as an effective semiconductor.
7/30/2019 Synthesis of Graphene on Gold - ArXiv
3/12
electrochemistry15,16 and spectroscopy17. It is known that gold surface has no catalytic
activity. Gold nanoparticles, however, show some diameter dependent catalytic activity for
oxidation of carbon monoxide and alcohols18. It is found that the smaller particles are more
active for oxidation. Furthermore growing single-walled (SWNT) and multi-walled carbon
nanotubes (MWNT) over gold nanoparticles also shows catalytic activity of the gold
nanoparticles. Bhaviripudi et al.19 grew SWNTs on SiO2 substrates using Au nanoparticles.
More recently Yuan et al.20 showed the growth of well aligned SWNT using Au particles.
This catalytic activity could be due to the solubility of carbon in gold clusters21. The
mechanism of catalytic activity of Au particles during CVD process still remains unclear. We
believe that the role of gold nanoparticle during the CVD process could provide more inside
to understand the growth mechanism of graphene layers on gold surface.
Figure 1 shows the schematic representation of the steps of the preparation of the gold
foils, deposition and transfer process of the graphene layers on dielectric substrates. We used
25 m thick gold foils obtained by pressing high purity gold plates (99.99% from Vakf
Bank). In order to remove impurities and reconstruct the single crystalline surface, the gold
foils were annealed with a hydrogen flame for 20 minutes before use. Owing to the fast
heating and cooling rates, hydrogen flame annealing provides more complete crystalization
of the gold foil than the furnace annealing22. The result of this treatment was a polycrystalline
7/30/2019 Synthesis of Graphene on Gold - ArXiv
4/12
stamp PDMS (Polydimethylsiloxane) is applied on the graphene coated gold foil. The gold
layer is etched by diluted gold etchant (type TFA, Transene Company Inc.). After complete
etching of the gold foil, the graphene layer on PDMS is applied on a 100 nm SiO2 coated
silicon wafers. Peeling the PDMS releases the graphene on the dielectric surface.
We grew graphene layers on gold surface in various forms such as thin films, foils and
wires. After the growth, we inspect the grown graphene layers using optical microscope and
scanning electron microscope. Figure 2(a) shows scanning electron micrograph of the
graphene on gold foils, respectively. The inset in Figure 2(a) shows the optical micrograph of
the graphene on the gold foil. The grain boundaries and wrinkles on the polycrystalline gold
surface are clearly seen.
Raman spectroscopy provides clear finger prints of graphene layers. Raman spectrum
of the samples was measured using a confocal microraman system (Horiba Jobin Yvon) in
back-scattering geometry. A 532 nm diode laser is used as an excitation source and the
Raman signal is collected by a cooled CCD camera. Figure 2(b) and 2(c) shows the Raman
spectrum of the graphene as grown on gold and after the transferring on SiO2 wafer. The
expected Raman peaks of D, G, D`, and 2D can be seen on the graph. The position of D, G,
D`, and 2D peaks are 1371, 1600, 1640, and 2743 cm-1 on gold and 1339, 1584, 1620 and
1
7/30/2019 Synthesis of Graphene on Gold - ArXiv
5/12
In order to find the optimum growth conditions we performed Raman spectroscopy on
samples grown at temperatures between 8500C and 10500C (See Figure 2(d)). At low
temperatures around 8500C, we do not observe a significant 2D peak. On the other hand at
very high temperatures there is a significant D and G peaks which indicates formation of
multilayer defective graphene layers. For the samples grown at temperatures between 850 0C
and 10000C, the Raman spectra look relatively the same. We have also studied the effect of
the cooling process on the grown graphene layers. However we do not observe any significant
change in the Raman spectra for cooling rates between 10 C/sec to 0.5 C/sec.
Figure 3(a) and 3(b) shows micro-Raman mapping images of the graphene layers on
SiO2. The micro-Raman mapping images are measured using confocal microraman system
with a spatial resolution of 300nm. Figure 3(a) shows the 2D map of the Lorentzian width of
2D peak obtained by scanning the sample and Lorentzian curve fitting for each point. The
intensity ratio mapping images of 2D and G peaks is shown in Fig.3(b). The histogram of the
Lorentzian width and I2D/IG peaks are given in Fig. 3(c) and 3(d), respectively. The average
width and the intensity ratio is around 40 cm-1 and 1.5, respectively. The distributions of the
histograms further support high percentage of single layer graphene.
To further characterize the grown graphene layers, we have fabricated field effect
7/30/2019 Synthesis of Graphene on Gold - ArXiv
6/12
channel length of 8 m and channel width of 100 m at a drain bias of 1 V. The Dirac point
of the device is around -20 V which is likely because of the trapped charges on the dielectric
layer or unintentional doping during the fabrication process. The on-off ratio of the device is
around 2. The calculated field effect mobility of the device is around 20 cm2/Vs. The output
characteristics are given in Figure 4(d). The modulation of the channel conductivity is clearly
seen from the graph.
The Raman spectra together with the transport measurements provide solid evidence
that gold surface can be used as a substrate for graphene. Graphene growth on metal
substrates shows different growth mechanism depending on the solubility of carbon in the
metal. Two different growth mechanisms have been proposed for nickel and copper substrate.
Very recently, using sequentially introduced isotopic carbon, Li et al.23 demonstrated that the
growth mechanism on nickel is based on diffusion and precipitation, however, the growth
mechanism on copper is based on surface adsorption. Maximum solubility values of carbon
in nickel, copper and gold are 2.7, 0.04 and 0.06 % respectively24. The solubility in gold is
slightly more than copper and much less than nickel. Based on these solubility values and the
observed minor effect of cooling rates, we speculate that the growth mechanism of graphene
on gold surface could be similar with copper.
7/30/2019 Synthesis of Graphene on Gold - ArXiv
7/12
Acknowledgement : This work was supported by the Scientific and Technological Research
Council of Turkey (TUBITAK) grant no. 109T259, and Marie Curie International
Reintegration Grant (IRG) grant no 256458 . Raman measurements were performed in part at
UNAM-Institute of Materials Science and Nanotechnology.
References:
1K. S. Novoselov, A. K. Geim, S. V. Morozov, D. Jiang, Y. Zhang, S. V. Dubonos, I. V. Grigorieva,
and A. A. Firsov, Science 306, 666-669 (2004).2
A. H. Castro Neto, F. Guinea, N. M. R. Peres, K. S. Novoselov, and A. K. Geim, Reviews of
Modern Physics 81, 109-162 (2009).3
X. S. Li, W. W. Cai, J. H. An, S. Kim, J. Nah, D. X. Yang, R. Piner, A. Velamakanni, I. Jung, E.
Tutuc, S. K. Banerjee, L. Colombo, and R. S. Ruoff, Science 324, 1312-1314 (2009).4
Y. M. Lin, C. Dimitrakopoulos, K. A. Jenkins, D. B. Farmer, H. Y. Chiu, A. Grill, and P. Avouris,Science 327, 662-662 (2010).
5J. A. Rogers, Nature Nanotechnology 3, 254-255 (2008).
6N. Liu, L. Fu, B. Dai, K. Yan, X. Liu, R. Zhao, Y. Zhang, and Z. Liu, Nano Letters 11, 297-303
(2010).7
Z. Sun, Z. Yan, J. Yao, E. Beitler, Y. Zhu, and J. M. Tour, Nature 468, 549-552 (2010).8
S. Garaj, W. Hubbard, and J. A. Golovchenko, Applied Physics Letters97, 183103 (2010).9
A. Reina, X. Jia, J. Ho, D. Nezich, H. Son, V. Bulovic, M. S. Dresselhaus, and J. Kong, Nano
Letters 9, 30-35 (2008).
10 L. Gao, J. R. Guest, and N. P. Guisinger, Nano Letters 10, 3512-3516 (2010).11
J. Coraux, A. T. N'Diaye, M. Engler, C. Busse, D. Wall, N. Buckanie, F. Heringdorf, R. van
Gastei, B. Poelsema, and T. Michely, New Journal of Physics 11, 023006 (2009).12
E. Sutter, P. Albrecht, and P. Sutter, Applied Physics Letters 95, 133109 (2009).13
J. Wintterlin and M. L. Bocquet, Surface Science 603, 1841-1852 (2009).14
M. Treier, P. Ruffieux, R. Schillinger, T. Greber, K. Mullen, and R. Fasel, Surface Science 602,
L84-L88 (2008).15
C. S. Shan, H. F. Yang, J. F. Song, D. X. Han, A. Ivaska, and L. Niu, Analytical Chemistry 81,
7/30/2019 Synthesis of Graphene on Gold - ArXiv
8/12
Figure Captions:
Figure 1: Schematic representation of the steps of deposition and transfer process of graphene
growth on gold film.
Figure 2: (a) Scanning electron micrograph of the graphene coated gold foils. The inset
shows the optical micrograph of the same area. (b) Raman spectra of the graphene as grown
on gold surface. (c) Raman spectra of the graphene on SiO2 substrate. The inset shows the
zoomed spectrum of the 2D peak and Lorentzian fit. The width of the Lorentzian is around 37
cm-1. (d) Raman spectra of the graphene samples grown at a range of temperatures between
8500C and 10500 C.
Figure 3: The micro-Raman mapping images of (a) the Lorentzian width of the 2D peak and
(b) intensity ratio (I2D/IG) of 2D and G peaks of the graphene on SiO2 layer. The Lorentzian
7/30/2019 Synthesis of Graphene on Gold - ArXiv
9/12
7/30/2019 Synthesis of Graphene on Gold - ArXiv
10/12
7/30/2019 Synthesis of Graphene on Gold - ArXiv
11/12
7/30/2019 Synthesis of Graphene on Gold - ArXiv
12/12
Recommended