QUEENSLAND UNIVERSITY OF TECHNOLOGY
FACULTY OF SCIENCE AND TECHNOLOGY
APPLIED OPTICS AND NANOTECHNOLOGY PROGRAM
Propagation of Low Power Low Divergence Gaussian
Fields in Unbiased Self-defocusing Photorefractive
Media and their Interactions
Submitted by Michael William Jones, to the Faculty of Science and Technology,
Queensland University of Technology, in partial fulfilment of the requirements
of the degree of Doctor of Philosophy.
2011
ii
Key Words
Photorefractive media, nonlinear optics, solitons, soliton interactions, self-focusing,
self-defocusing, unbiased photorefractive media, Gaussian beam optics, GRIN lens,
intensity dependent absorption, intensity dependent transparency, Ce:BaTiO3.
iii
Abstract
Many optical networks are limited in speed and processing capability due to the
necessity for the optical signal to be converted to an electrical signal and back again.
In addition, electronically manipulated interconnects in an otherwise optical network
lead to overly complicated systems. Optical spatial solitons are optical beams that
propagate without spatial divergence. They are capable of phase dependent
interactions, and have therefore been extensively researched as suitable all optical
interconnects for over 20 years. However, they require additional external
components, initially high voltage power sources were required, several years later,
high power background illumination had replaced the high voltage. However, these
additional components have always remained as the greatest hurdle in realising the
applications of the interactions of spatial optical solitons as all optical interconnects.
Recently however, self-focusing was observed in an otherwise self-defocusing
photorefractive crystal. This observation raises the possibility of the formation of
soliton-like fields in unbiased self-defocusing media, without the need for an applied
electrical field or background illumination.
This thesis will present an examination of the possibility of the formation of
soliton-like low divergence fields in unbiased self-defocusing photorefractive media.
The optimal incident beam and photorefractive media parameters for the formation
of these fields will be presented, together with an analytical and numerical study of
the effect of these parameters. In addition, preliminary examination of the
interactions of two of these fields will be presented.
In order to complete an analytical examination of the field propagating
through the photorefractive medium, the spatial profile of the beam after propagation
through the medium was determined. For a low power solution, it was found that an
iv
incident Gaussian field maintains its Gaussian profile as it propagates. This allowed
the beam at all times to be described by an individual complex beam parameter,
while also allowing simple analytical solutions to the appropriate wave equation.
An analytical model was developed to describe the effect of the
photorefractive medium on the Gaussian beam. Using this model, expressions for the
required intensity dependent change in both the real and imaginary components of
the refractive index were found. Numerical investigation showed that under certain
conditions, a low powered Gaussian field could propagate in self-defocusing
photorefractive media with divergence of approximately 0.1 % per metre.
An investigation into the parameters of a Ce:BaTiO3 crystal showed that the
intensity dependent absorption is wavelength dependent, and can in fact transition to
intensity dependent transparency. Thus, with careful wavelength selection, the
required intensity dependent change in both the real and imaginary components of
the refractive index for the formation of a low divergence Gaussian field are
physically realisable.
A theoretical model incorporating the dependence of the change in real and
imaginary components of the refractive index on propagation distance was
developed. Analytical and numerical results from this model are congruent with the
results from the previous model, showing low divergence fields with divergence less
than 0.003 % over the propagation length of the photorefractive medium. In addition,
this approach also confirmed the previously mentioned self-focusing effect of the
self-defocusing media, and provided an analogy to a negative index GRIN lens with
an intensity dependent focal length. Experimental results supported the findings of
the numerical analysis.
v
Two low divergence fields were found to possess the ability to interact in a
Ce:BaTiO3 crystal in a soliton-like fashion. The strength of these interactions was
found to be dependent on the degree of divergence of the individual beams.
This research found that low-divergence fields are possible in unbiased self-
defocusing photorefractive media, and that soliton-like interactions between two of
these fields are possible. However, in order for these types of fields to be used in
future all optical interconnects, the manipulation of these interactions, together with
the ability for these fields to guide a second beam at a different wavelength, must be
investigated.
vi
Publication List
Journal Articles:
Jaatinen, E. & Jones, M.W. Theoretical description of low divergence Gaussian
fields in self-defocusing photorefractive media. Opt Commun. 281 (11) 2008,
3201-3207
Jones, M. W. & Jaatinen, E. Transition from intensity dependent absorption to
transparency in Ce:BaTiO3. Opt. Matter. 31 (2) 2008, 122-125
Jones, M. W., Jaatinen, E., & Michael, G. Propagation of low-intensity Gaussian
fields in photorefractive media with real and imaginary intensity-dependent
refractive index components. Appl. Phys. B. doi: 10.1007/s00340-010-4309-y
Jones, M. W., Jaatinen, E., & Michael, G. Soliton-like interactions of bright low-
power low-divergence Gaussian fields in an unbiased self-defocusing
photorefractive BaTiO3 crystal. Opt Eng. 50 (1) 2011, 019701-1-019701-3
Conferences:
Jones, M. W. & Jaatinen, E. Field propagation with nearly constant Gaussian beam
parameters in unbiased self-defocusing photorefractive media. Proc. SPIE.
6801, 2008, 68011P-1-68011P-9
Jones M. W., Jaatinen, E., & Michael, G. (Peer Reviewed) Experimental
investigation of bright photovoltaic spatial soliton-like fields in unbiased self-
defocusing photorefractive BaTiO3. AIP Congress, ISBN 1-876346-57-4,
2008, 184-187.
vii
Jones M. W., Jaatinen, E., & Michael, G. Analysis of the interactions of bright
photovoltaic low-divergence soliton-like fields in unbiased self-defocusing
photorefractive BaTiO3. Proc. SPIE. 7197, 2009, 719711P-1-719711P-8
Jaatinen, E., Jones, M. W. Numerical modeling fields with forced Gaussian spatial
distributions when they propagate through nonlinear media. ACOLS, 2009, 97-
98.
viii
Statement of Original Authorship
The research contained in this thesis has not been previously submitted to meet
requirements for an award at this or any other higher education institution. To the
best of my knowledge and belief, the thesis contains no material previously published
or written by another person except where due reference is made
Signature
Date
ix
Acknowledgement
This thesis would not have eventuated without the assistance of many people. First
and foremost, I would like to thank my supervisory team, Esa Jaatinen and Greg
Michael. The fountain of knowledge of all things optical that is Esa was drawn upon
many times, and his insight and support was greatly appreciated. With thousands of
images to analyse, Greg provided the means to a streamlined and automated process,
which not only allowed me to concentrate on interpreting the results, but also cut
months, possibly years, off the analysis.
I am indebted to the entire Applied Optics and Nanotechnology Program at
QUT. Each member of the group provided untold amounts of assistance and support.
The community spirit within the group goes a long way in such a large project.
A PhD thesis does not stay out of the home, and I would like to thank my
wonderful wife, Rachel, for her support throughout the process. I know she’ll miss
hearing about the adventures of BaTiO3. I would also like to thank my family, who
were always there to support me, and my friends, who were always there for
distraction.
x
Table of Contents
Key Words................................................................................................................... ii Abstract....................................................................................................................... iii Publication List............................................................................................................vi Statement of Original Authorship ............................................................................ viii Acknowledgement.......................................................................................................ix Table of Contents .........................................................................................................x Table of Figures......................................................................................................... xii 1. Introduction ............................................................................................................1
1.1 Research problem ..................................................................................1 1.2 Overall aims of the study.......................................................................3 1.3 Specific objectives of the study and linking the research papers ..........3
2. Theory and background information .................................................................11
2.1 Introduction .........................................................................................11 2.2 Interaction of light with matter............................................................12
2.2.1 Linear response..........................................................................13 2.2.2 Nonlinear response ....................................................................14
2.3 The photorefractive effect ...................................................................15 2.3.1 Charge migration .......................................................................17
2.3.1.2 Bulk photovoltaic current ......................................18 2.3.1.3 Diffusion current ...................................................19
2.3.2 Charge transportation ................................................................20 2.3.2.1 Single centre model ...............................................20 2.3.2.2 Hole-electron competition .....................................23 2.3.2.3 Two centre model ..................................................24
2.3.3 Effective charge carrier density.................................................27 2.3.4 Light induced absorption...........................................................28 2.3.5 Complex refractive index ..........................................................30
2.4 Photorefractive materials.....................................................................31 2.4.1 Self-focusing photorefractive media .........................................32 2.4.2 Self-defocusing photorefractive media......................................33 2.4.3 Biased photorefractive media ....................................................34
2.6 Gaussian Beam Optics.........................................................................35 2.6.1 Lenses ........................................................................................38
2.6.1.1 Thick Lenses..........................................................41 2.6.1.2 GRIN Lenses .........................................................42
2.7 Gaussian beam propagation in inhomogeneous media .......................44 2.8 Spatial optical solitons.........................................................................47
2.8.1 PR screening solitons ................................................................50 2.8.2 Photovoltaic solitons .................................................................51 2.8.3 Soliton Waveguides...................................................................52 2.8.4 Soliton Interactions....................................................................53
2.9 Methods of analysis .............................................................................56
xi
2.9.1 Far field image analysis.............................................................57 2.9.2 Z-scan ........................................................................................59 2.9.3 Numerical wavefront study .......................................................60
3. Theoretical description of low divergence Gaussian fields in self-defocusing photorefractive media ..............................................................................................62
4. Transition from intensity dependent absorption to transparency in Ce:BaTiO3 .................................................................................................................71
5. Propagation of low-intensity Gaussian fields in photorefractive media with real and imaginary intensity-dependent refractive index components ...............77
6. Soliton-like interactions of bright, low power, low-divergence Gaussian fields in unbiased self-defocusing photorefractive BaTiO3 crystal ................................86
Soliton-like interactions of bright, low power, low-divergence Gaussian fields in unbiased self-defocusing photorefractive BaTiO3 crystal ....................................87
7. Conclusion.............................................................................................................91
References ..................................................................................................................95
xii
Table of Figures
Figure 2.1: Schematic of charge migration due to the drift current (a) and the
diffusion current (b), with arrows representing the migration of charge carriers from
areas of illumination………………………………..…………………….…………19
Figure 2.2: Band diagram for the single centre model, with arrows indicating
excitation and recombination of electrons and the photorefractive centre C− /C 0
……………………………………………………….……………………………...21
Figure 2.3: Band diagram for the two centre model, with arrows indicating
excitation and recombination of electrons at the photorefractive centres and
……………………………………………………………………….…......25
Figure 2.4: Phase fronts of a normally diffracting Gaussian beam (dashed lines), and
a Gaussian beam propagating in self-focusing media (solid line). ……………........32
Figure 2.5: Phase fronts of a normally diffracting Gaussian beam (dashed lines), and
a Gaussian beam propagating in self-defocusing media (solid line)………………..33
Figure 2.6: Profile and phase fronts of a Gaussian beam as functions of the
propagation distance, z, from the waist position, w(0). The beam divergence in the
far field is given by θ. …………………………………………………………...…38
Figure 2.7: Transformation of a Gaussian beam due to a thin lens, where q10 and q20
are the complex beam parameters before and after propagating through the thin lens.
…………………………………………………………………………………...…40
xiii
Figure 2.8: Transformation of a Gaussian beam due to a thick lens, where q10 and
q20 are the complex beam parameters before and after propagating through the thick
lens. ………………………..…………………….………………………….………41
Figure 2.9: Transformation of a Gaussian beam due to a GRIN lens, where q10 and
q20 are the complex beam parameters before and after propagating through the thick
lens. ………………………………………………………………..…………..……42
Figure 2.10: Comparison between a spatial optical soliton (a) and a normally
diffracting beam (b) ……………………………………………………....………...48
Figure 2.11: Images and beam profiles illustrating one-dimensional PR screening
soliton interactions in a 6 mm long SBN crystal; a, parallel input beams with 18 µm
separation; b, output under normal diffraction; c, output when beams launched
separately; d, output for in-phase soliton collision showing soliton fusion; e, output
for soliton collision with phase difference showing energy transfer and slight
repulsion, with separation equal to 35 µm; f, output for out of phase soliton collision
showing repulsion, with separation equal to 46 µm ………………………..…..…..54
Figure 2.12: Sample far field image (left) with the cross section (dots) taken at the
horizontal line, and fitted Gaussian profile (line, right). …….………………..........59
1
1. Introduction
1.1 Research problem
Optical devices, which use light to control light, have long been declared as one
possible solution to improve information processing capacity and speed, as well as
offering the possibility to be completely reconfigurable when created in
photosensitive media[1-3]. These devices would utilise the ability of low divergence
beams to create a waveguide that could then be used to guide a second wavelength
where the material is insensitive. In addition, these devices would display optically
manipulated interactions controlled by the light itself, removing the need for
additional electronic circuitry.
As with electronic circuitry, the functionality and operating speed of such
devices would increase if the size of the device was reduced[4-6]. Optically, this
requires minimising the divergence of each beam over the distance it travels to avoid
crosstalk and to maintain uniform waveguides. One example of a suitable low
divergence field that can be used for devices where light controls light is a
photorefractive (PR) spatial optical soliton[7]. PR spatial solitons display phase
dependent interactions, and can be configured into ‘X’ and ‘Y’ junctions by
manipulating the relative phases of the two soliton beams[8].
To integrate with existing communications technology, these low-divergence
fields will be required to operate at low powers, and be capable of controlling light at
optical wavelengths in the infrared[9]. Running at low optical power would not only
lower overall electrical power consumption resulting in low heat generation, but
additionally reduce safety concerns. Current optical communications use low power
compact semiconductor lasers, with Gaussian intensity profile outputs[9]. As such, to
2
create low divergence waveguides capable of light controlled interactions, the effect
that nonlinear media has on low power beams with a Gaussian spatial profile is of
importance.
PR media is one type of medium where the refractive index has a component
that is intensity dependent, allowing low divergence fields such as spatial solitons to
be created. Photorefractive spatial optical solitons are available in many varieties
such as bright, grey, and dark, all of which have been investigated over many years
and have many common fundamental similarities[10, 11]. In a PR medium where
the refractive index is increased in regions where light is present, it is possible for the
converging effects of the medium to exactly counteract natural beam divergence,
resulting in a beam that propagates with a constant planar wavefront and without
divergence as a single bright spatial soliton[11]. These types of solitons are
theoretically described by exact solutions to the wave equation which incorporates
the self-focusing nonlinearity of the medium[11, 12]. However, if the beam intensity
is too high, the beam can overly self-focus, causing irreversible damage to the PR
medium.
In self-defocusing PR media however, a planar field will propagate with
increased divergence, with the defocusing effects of the medium exacerbating the
natural divergence of the beam. As a consequence of this, single bright spatial
solitons with planar wavefronts do not exist in unbiased self-defocusing media.
However, in 2006, self-focusing was observed in both doped and undoped unbiased
self-defocusing BaTiO3 where the PR media was placed at the beam waist position
of a tightly focused TEM00 Gaussian field[13]. This apparent self-focusing of
Gaussian beams in unbiased self-defocusing PR media has not been theoretically
explained, and could offer the potential for single bright spatial solitons to be realised
3
in self-defocusing PR media. This is advantageous, as unlike self-focusing, self-
defocusing cannot result in catastrophic over-focusing of the optical radiation
causing irreparable damage to the medium.
1.2 Overall aims of the study
As discussed in the section 1.1, low divergence fields in PR media created with low
power Gaussian beams could provide a solution for increasing the speed and capacity
of current information processing. A simple solution that avoided the possibility for
destructive self-focusing would be ideal, as it would be more likely to survive spikes
in laser power. The recent observation of self-focusing effects in unbiased self-
defocusing PR media[13] has lead to the possibility of stable bright low divergence
fields being created in such media. This study therefore aims specifically to
investigate the possibility of generating such fields in unbiased self-defocusing PR
media, and more generally, to gain a greater understanding of the propagation of low
power Gaussian beams in PR media in order to theoretically explain, for example,
the previously observed apparent self-focusing.
1.3 Specific objectives of the study and linking the
research papers
Investigation of the formation of stable bright low power, low divergence fields in
unbiased self-defocusing PR media comprises of a series of integrated analytical,
numerical, and experimental studies. Initially, a general analytical approximation of
low Gaussian beams propagating in nonlinear media was developed, and applied to
several scenarios. One such scenario was the main objective of the study - the
4
generation of low divergence fields in self-defocusing media. Additional scenarios
were investigated to test the analytical approximation against known outcomes.
Following this, several conditions arose from the development of the analytical
approximation that required experimental investigation. To fully explain the
observations, comprehensive numerical and analytical models were developed. The
predictions of this model were compared to the experimental observations of the
defined scenarios. This is described in the chapters of this thesis:
• Determination of the effect of self-defocusing PR media on the spatial
intensity profile of an incident Gaussian beam (Chapter 3).
Methods and outcomes:
After propagating through the self-defocusing PR medium, the far field
intensity profile of a low power Gaussian beam was measured. Far field
profiles were obtained for the medium was placed at various distances from
the beam waist position. In all cases under low power illumination, the
incident Gaussian beam was found to maintain its Gaussian profile after
propagating through the medium. This result allows the beam within the
medium to be described by a complex beam parameter that uniquely
describes the diameter and wavefront curvature of the Gaussian field. An
important consequence of this is that it allows the refractive index variation
inside the medium to be treated as a quadratic function of distance from the
beam axis - greatly simplifying the wave equation and its solution.
5
• General analytical approximation of low power Gaussian beams propagating
in nonlinear media with a quadratic refractive index profile with low
divergence. The case for both self-focusing PR media and self-defocusing
media are examined (Chapter 3).
Methods and outcomes:
The real and imaginary parts of the intensity dependent refractive index
required to form a low divergence field in unbiased self-defocusing and self-
focusing PR media are obtained by substituting the Gaussian field into the
quadratic form of the nonlinear wave equation. In the absence of an
imaginary component of the intensity dependent refractive index, a stable
non-diverging Gaussian field with a plane wavefront is obtained in self-
focusing PR media, as predicted elsewhere[14]. Following this analysis, the
intensity dependent part of the refractive index was expanded to contain both
real and imaginary parts. In this case, the conditions for low divergence fields
from converging incident Gaussian beams in self-defocusing PR media were
obtained for both one and two transverse dimensions. Although the fields
predicted were not true spatial optical solitons, numerical simulations
revealed that they could propagate over relatively long distances with
divergences several orders of magnitude smaller than that of a comparable
Gaussian field propagating in a homogeneous medium.
Stable low divergence fields are predicted to occur for a converging
Gaussian beam in self-defocusing PR media where the imaginary part of the
change in refractive index is negative. The feasibility of realising these fields
in a typical self-defocusing PR medium was investigated in Chapter 4.
6
• Determination of whether the PR Ce:BaTiO3 crystal possesses the required
real and imaginary intensity dependent refractive index for the formation of
bright low divergence fields. In particular, this part of the research project
aims to characterise the wavelength dependence of intensity dependent
absorption, which is related to the imaginary component of the change in
refractive index, of the PR crystal (Chapter 4).
Methods and outcomes
Unbiased Ce:BaTiO3 is a self-defocusing PR crystal. When irradiated with
light at a wavelength of 532 nm, it exhibits an absorption that increases as the
intensity of the incident light increases. An increasing intensity dependent
absorption corresponds to a positive change in the imaginary part of the
refractive index. By comparing the intensity of the beam before and after
propagating through the PR crystal, the absorption was calculated using the
Beer-Lambert law[15, 16]. Unwanted PR effects, such as beam fanning, were
minimised by careful selection of the incident angle relative to the optical c-
axis of the PR crystal, allowing the intensity dependent change in absorption
to be calculated. Results from this study showed that at an incident
wavelength of 532 nm, Ce:BaTiO3 displays an absorption that increases with
incident field intensity, while at an incident wavelength of 790 nm, the same
crystal displays an increase in transparency as the intensity increases. This
result shows that the conditions required for the formation of bright low
divergence fields in self-defocusing PR media are physically realisable
through choice of wavelength.
7
• Development of a theoretical description of the complex beam parameter of a
Gaussian beam propagating in nonlinear media with a quadratic refractive
index profile with real and imaginary parts of the intensity dependent change
in refractive index (Chapter 5).
Methods and outcomes
While previous sections of the research project (Chapter 3), dealt with an
approximation of the problem, this section aimed to develop a more complete
theoretical description of the propagation of a Gaussian beam in nonlinear
media with a quadratic refractive index profile. In this approach, the Gaussian
complex beam parameter, q, is obtained as a function of the propagation
distance through the PR media. Using boundary conditions obtained from the
incident beam parameters, and appropriate values for the real and imaginary
parts of the intensity dependent refractive index, the evolution of the
Gaussian beam through the medium can be completely described as a
function of the propagation distance, z. This theoretical description was then
applied analytically and numerically to the same scenarios described in
Chapter 3. In addition it was also shown that a PR medium under low power
illumination could be described as an intensity dependent gradient-index
(GRIN) lens. This model was also able to explain the previously observed
apparent self-focusing of Gaussian beams in unbiased self-defocusing PR
media[13], as being a direct result of the imaginary component of the
intensity dependent refractive index.
8
In implementing the analytical model, it was assumed that the change
in intensity over the medium length was small, this allows the intensity
dependent change in the refractive index to be treated as constant throughout
the medium. Under this approximation, the model accurately described the
well-known scenario of the formation of bright spatial solitons in self-
focusing PR media, and confirmed the conditions for the formation of bright
low divergence Gaussian fields in self-defocusing PR media found in Chapter
3. In addition, when an imaginary intensity dependent refractive index
component was included, the analytical solution also explains the apparent
self-focusing in unbiased self-defocusing PR media previously
experimentally observed[13]. The self-defocusing PR media was also found
to behave as a GRIN lens with an intensity dependent negative focal length
within a range of incident intensities.
While the analytical treatment gives good qualitative agreement with
experimental observations a numerical model, that includes variations in
intensity as a function of the propagation distance, is necessary to provide an
accurate quantitative description. The results of this research were congruent
with the previous analytical results in Chapter 2 and Chapter 3. Of particular
interest, the numerical model differed from the theoretical model in the GRIN
lens analogy, with the numerical model providing a much better fit to
experimental results (discussed in the following research section) over a
wider range of incident intensities than the analytical model. In addition, the
numerical model predicted a greater degree of apparent self-focusing than the
analytical model.
9
• Experimental verification of the output of the numerical model (Chapter 5).
Methods and outcomes
To verify the results obtained from the numerical model, an experimental and
numerical z-scan was undertaken using an unbiased self-defocusing
Ce:BaTiO3 PR crystal and a 532 nm Nd:YAG laser. This combination was
selected due to the well documented PR response of the material to light at a
wavelength of 532 nm. Under similar incident beam parameters, and with
appropriate values for the intensity dependent refractive indices (real and
imaginary) of the PR medium, both the experimental and numerical results
showed good agreement. This agreement was demonstrated for an array of
experimental conditions, such as, changes in incident beam power and
incident beam waist size. This outcome showed that the numerical model, and
by extension, the theoretical description, accurately described the low power
light propagation through PR media.
• Investigation into the possible interactions of two bright low divergence
fields in unbiased self-defocusing PR media.
Methods and outcomes
Bright solitons in self-focusing PR media interact with each other, attracting
or repelling each other depending on the relative phase of the two beams[17].
Therefore, this section of the research project aimed to determine if soliton-
like interactions between two bright low divergence fields in unbiased self-
defocusing PR media were possible. A thin wedge was used to create two
10
beams, which crossed within the PR medium. The angle between the two
beams was less than the beam divergence, resulting in a interference pattern
forming in the far field intensity profile of the beam. Shifts in the band
spacing in the interference pattern allowed any change in the angle that the
two beams exited the PR medium to be calculated. These results showed a
small increase in the angle with which the beams exited the PR medium for a
small range of z positions, relative to the incident beam waist, where low
divergence fields could exist. The increase in angle indicates that the two
fields interacted within the PR medium, repelling each other. This result is
important as it suggests that bright low divergence Gaussian fields, although
not considered classical spatial solitons, are capable of soliton-like
interactions.
11
2. Theory and background information
2.1 Introduction
Controlling the propagation of light within matter requires an understanding of the
interactions that light has with matter. When the incident light has a relatively high
intensity, such as a laser beam, the response of the material can be a nonlinear
function of the incident intensity[18]. These nonlinear interactions can result in a
light induced change in the refractive index of the material, which in turn alters the
direction and divergence of the light as it propagates through the medium.
Photorefractive (PR) media is one class of material that has a light induced change in
refractive index, called the PR effect, which could be used in a variety of ways to
control the propagation of laser beams through the media.
The PR effect is a result of charges (electrons or holes) being excited into the
conduction or valance band, and then migrating to areas of lower intensity before de-
exciting and becoming trapped again[19, 20]. This causes an electric field to develop
within the medium, called a space-charge field, which modulates the refractive index
through the Pockels effect[21]. Charge carriers become excited from traps at a range
of energy levels, with their excitation dependent on the intensity and wavelength of
the incident light[22-24]. As a result, the change in refractive index is also dependent
on these parameters. The charge excitation and transportation process responsible for
the space-charge field is also responsible for the light induced absorption of a PR
medium[16, 25]. Like the change in refractive index, the light induced absorption
can be positive or negative, and is intensity and wavelength dependent[26-28].
By altering the incident beam parameters, the PR effect can be exploited for a
variety of purposes such as creating phase conjugate mirrors, holographic storage of
12
data, and creating PR spatial solitons to be used as waveguides[14]. Of particular
interest to this research are PR spatial solitons. PR spatial solitons are optical beams
that propagate in PR media without spatial divergence. They are formed when the
intensity dependent change in refractive index causes the beam to self-focus, exactly
counteracting the beams natural divergence[29].
Spatial solitons have many interesting properties. As they manipulate the
refractive index of the medium they propagate through, they can be used to fabricate
waveguides. In addition, the wavelength dependence of the PR effect leads to the
possibility of the spatial soliton to guide a second beam of a different wavelength at
much greater intensity[30, 31]. Multiple spatial solitons propagating through the
same medium have displayed phase dependent interactions, with any guided beams
taken along with their respective soliton waveguide in the interaction[32-34].
2.2 Interaction of light with matter
The interaction of light with matter has received both academic and public interest
for centuries. Various phenomena such as using a prism to split white light into a
spectrum of colours, magnification through microscopes, and data transmission
through fibre optics all utilise a light-matter interaction. When the incident light has a
relatively low intensity, the material responds in a way that is linearly dependent of
the intensity of the incident light. However, when the incident light power is
increased to relatively high levels, the response of the material can become
nonlinearly dependent on the intensity of the incident light. The study of the
nonlinear response of materials to light, called nonlinear optics, is of particular
interest to researchers at present, with its application to optical computing coming
close to being physically realised.
13
2.2.1 Linear response
Visible light is an electromagnetic wave that can interact with individual atoms in a
material. The response of a material to light can thus be explained in the same way as
the response of a material to an applied oscillatory electric field. When an electric
field is applied to an atom, an induced dipole moment (p) is produced as a result of
the separation of the positive and negative charge within the atom. Put simply, at
visible wavelengths, the applied field drives the electrons bound to nuclei as simple
harmonic oscillators. When an electric field is applied to a large number (N) of
identical atoms, their individual induced dipole moments combine, resulting in a
macroscopic polarisation (P) of the material[9]:
P = Np (2.1)
If the electric field is relatively weak, the polarisation of the material is proportional
to the strength of the local electric field multiplied by the electric susceptibility (χ) of
the material[35];
P = ε0χE (2.2)
where ε0 is the permittivity of free space. When an oscillating electric field such as
light is applied to the material, the individual dipole moments of the atom will
oscillate. These oscillating dipoles then act as secondary radiators with the same
frequency as the incident radiation. The electric field inside the medium will
therefore be a combination of the applied electric field and the electric field resulting
from the polarisation[35].
14
The interaction between the incident field and the dipoles is not instantaneous
but occurs over a finite time interval. As a result the subsequent dipole radiation can
be shifted in phase to the applied field, which alters the phase speed of the local field
to some fraction of the speed in a vacuum. This retardation of the plane wave is
given by the refractive index, n, of the medium[18, 35];
n2 = c2
u2= 1+ χ( )µr (2.3)
where c is the speed of light in a vacuum, u is the speed of light in the medium, and
µr is the relative permeability. If the medium contains no magnetic response; the
relative permeability is one, and the refractive index reduces to:
n2 = 1+ χ (2.4)
Therefore, the refractive index of the material is a parameter that completely captures
the materials linear response to the dipole inducing applied field.
2.2.2 Nonlinear response
As the applied electric field strength increases, electrons behave much more
energetically and their oscillations become anharmonic. As a result the polarisation
of the material becomes a nonlinear function of the field strength[18, 35];
P = ε0 χE + χ2EE + χ3EEE + ...( )= PL + P2
NL + P3NL + ...
(2.5)
15
where the nonlinear susceptibility coefficients χ2 ,χ3...are constants that describe the
materials’ response to the field, and the superscripts L and NL refer to linear and
nonlinear terms. In most materials, one nonlinear polarisation term will dominate all
others, and the polarisation can therefore be reduced to[35];
P = PL + PjNL (2.6)
where PjNL is the dominate jth order term of the nonlinear polarisation.
An inspection of equation (2.5) reveals that each nonlinear polarisation term
is dependent on the intensity of the incident light field, with the refractive index
dependence on the polarisation given by the following relationship:
(2.7)
It is therefore evident that the effective refractive index is intensity dependent when
the nonlinear effects are included. The photorefractive effect is one example of an
intensity dependent refractive index.
2.3 The photorefractive effect
The photorefractive effect is a light induced change in the refractive index of electro-
optic materials. The effect was first observed in LiNbO3 and BaTiO3 in 1966 with
focused green and blue laser beams[36]. Ashkin et al observed that this effect
occurred at different rates in different materials and was wavelength dependent, in
that at some wavelengths, light induced refractive index inhomogeneities failed to
16
materialise[36]. The effect was initially called ‘optical damage’, as it was thought of
as a hindrance to common nonlinear applications of electro-optic materials[21, 37,
38]. In the late 1960’s, the inhomogeneous change in refractive index was attributed
to the excitation and redistribution of charges due to inhomogeneous illumination,
resulting in the formation of space-charge fields[19, 20]. It was observed that the
change in refractive index (Δn) was proportional to the space charge field (ESC) that
was in turn proportional to the density of excited free charge carriers (Neff)[20]:
Δn ∝ ESC ∝ Neff (2.8)
At relatively low intensities, the space charge fields modulate the refractive index of
the medium through the linear electro-optic Pockels effect[18, 21, 39-41];
(2.9)
where n is the background or dark refractive index and rijk is the electrooptic tensor.
The Pockels effect had been used for many years to phase modulate fields in electro-
optic materials by creating a time varying refractive index by applying an oscillatory
electric field. The materials used for these modulators, (eg. LiNbO3) were chosen for
their large electro-optic properties. It is therefore, little wonder that 'optical damage'
was first observed in electro-optic phase modulators.
The space charge field and therefore the change in refractive index are a
result of a three step charge migration process of charges excited from donor ions.
Free charge carriers are excited by inhomogeneous illumination and transported from
17
donor ions to the conduction band. Once in the conduction band, the free charge
carriers migrate to other areas of the electro-optic material, where they are trapped by
acceptor ions[42]. There are several processes by which charges can migrate within
the conduction band, and several models that explain various aspects of the charge
transportation processes, which will be dealt with individually.
2.3.1 Charge migration
Free charge carriers redistribute due to either one or a combination of charge
migration currents within the electro-optic material. The charge migration process
that occurs within the electro-optic crystal is dependent on the characteristics of the
individual crystal, and any applied external electric field or illumination[21, 39]. The
three charge migration currents are drift current, bulk photovoltaic current, and
diffusion current.
2.3.1.1 Drift current
When a homogeneous electric field is applied to the electro-optic crystal, charge
carriers that have been excited by the incident light are forced to move in the
direction dictated by the field, as shown in Figure 2.1 (a). The applied field interacts
with the free charge carriers through Coulomb interactions[21], and the resulting
current obeys Ohms’ law and is given by[21, 39];
jdrift = σ̂E (2.10)
18
where σ̂ = eµ̂e,hNe,h , and E is the electric field, consisting of the applied electric
field, the space charge field, and the pyroelectric field; e is the electron charge,
is the free charge carrier mobility, and Ne,h is the density of free charge carriers. The
drift current is therefore directly proportional to the strength and direction of the
applied external electric field.
2.3.1.2 Bulk photovoltaic current
The bulk photovoltaic current is due to free charge carriers moving in a preferred
direction due to the anisotropic nature of the crystal. Therefore, it is the dominant
effect in highly non-centrosymmetric photorefractive crystals like LiNbO3 [21]. The
magnitude and direction of the photovoltaic current is given by[39];
jphv( )i =12
βijkE j*Ek + c.c.( )
(2.11)
where βijk is the third rank bulk photovoltaic tensor, and Ej and Ek are components of
the incident light. The magnitude and direction of bulk photovoltaic current is
therefore proportional to the bulk photovoltaic tensor and the intensity of the incident
light.
19
2.3.1.3 Diffusion current
The diffusion current is due to the thermal movement of free charge carriers from
areas of high intensity to areas of low intensity due to inhomogeneous illumination,
as shown in Figure 2.1 (b). In this case, the excited charge carriers move as a result
of thermal energy. Charge carriers that move away from areas of high intensity
become re-trapped as their energy is lost. This results in a spatial variation of free
charge carriers, with a current given by[39];
jdiff = −QD̂∇Ne,h (2.12)
where is the diffusion tensor, related to the mobility of free charges and the
temperature, T, through D̂ = µ̂e,hkBTe−1 . Q is the charge of the carrier, equal to either
–e for electron migration, or +e for hole migration. The diffusion current is therefore
proportional to the thermal energy transferred to the crystal from the incident light.
Figure 2.1: Schematic of charge migration due to the drift current (a) and the
diffusion current (b), with arrows representing the migration of charge carriers from
areas of illumination.
20
2.3.2 Charge transportation
Several charge transportation models have been developed to explain the origin of
the charge carriers, and also their dynamics under various experimental scenarios
such as the electro-optic medium under inhomogeneous illumination. Examples of
these models that are relevant to the work discussed here are: the single centre
model, hole electron competition, and two centre model. The energy levels from
where the free charge carriers are excited from within the band gap influence bulk
material properties such as light induced change in absorption, conductivity, and
holographic sensitivity[39]. Free charge carriers can be electrons, holes, or both. In
this thesis, the charge carrier will be assumed to be electrons when there is only one
charge carrier present.
2.3.2.1 Single centre model
The single centre model of the photorefractive effect was the first charge
transportation model used to describe the excitation and recombination of free charge
carriers in electro-optic materials[41]. In this model, electrons are excited into the
conduction band from a single filled centre, C- in the band gap, as can be seen in
Figure 2.2.
21
Figure 2.2: Band diagram for the single centre model, with arrows indicating
excitation and recombination of electrons ad the photorefractive centre C− /C 0 [39].
Initially, these centres were thought to result from Iron (Fe2+/Fe3+) impurities
in LiNbO3, with free charges resulting from the reaction[21]:
Fe2+ + hυ = Fe3+ + free carrier (2.13)
These centres were later attributed to a host of other impurities including copper
(Cu1+/Cu2+) and manganese (Mn2+/Mn3+)[21]. The free electrons are then trapped out
of the conduction band by unfilled centres, C0[39]. The energy level C-/C0
corresponds to the thermal excitation energy required to excite an electron from C-
into the conduction band, creating C0. Depending on the impurity, either electrons or
holes can be charge carriers in the single centre model, with each being excited into
the conduction or valance band respectively.
22
Using terms for the recombination of charges first used in 1971[43], rate
equations for the charge migration process in a single level model were formalised in
1975[44];
dN −
dt= − SI + β( )N − + γ RN
0Ne
(2.14)
N = N − + N 0 (2.15)
where N- and N0 are the concentrations of the donor centres C- and C0, β is the
thermal generation rate, S is the photon absorption cross section, I is the light
intensity, γR is the recombination coefficient, Ne is the concentration of electrons in
the conduction band, and N is the total concentration of electrons in the
photorefractive centre.
The single centre model for the excitation of charge carriers in the
photorefractive effect agrees well with experiments in both copper and iron doped
LiNbO3[39], pure BSO and BaTiO3[41], and Rhodium doped BaTiO3[45]. However,
anomalies were observed in some photorefractive crystals which could not be
explained by the single centre model. For example, multiple dark decay rates of
photorefractive gratings[46], signal gratings changing sign as a function of the
grating period[47], and intensity dependent factors[39, 48].
Extending the single centre model to include two different photorefractive
centres, as shown in Figure 2.3, related to two different impurities, allows for the two
dark decay rates observed in Ce:BaTiO3[46, 49]. Since the energy levels
corresponding to these impurities may differ, the relative effect of each dopant is
wavelength dependent, leading to wavelength dependent dark decay rates. Therefore,
23
to explain this and other anomalies, additional terms need to be included in the single
centre model.
2.3.2.2 Hole-electron competition
To explain some of the anomalies observed in some electrooptic crystals, the single
centre model was expanded to include the simultaneous excitation of both electrons
and holes. In this model, the wavelength of the incident light determines the relative
contribution of each electron and hole excitation to the space charge field[50].
Including two species into the charge transportation process also helps explain how
photorefractive grating erasure rates could occur over two different time scales[46,
49].
In 1986, two models for the inclusion of simultaneous hole-electron
excitation in the single level model were proposed[51, 52]. In the first model, holes
and electrons are produced from a single set of recombination centres. For example,
electrons are photoionised from donors (Fe2+) and recombine with traps (Fe3+), while
holes follow the opposite path, photoionised from hole donors (Fe3+) and
recombining with hole traps (Fe2+) in LiNbO3[52]. In this model, the strength and
direction of the space charge field are dependent on the grating wave vector,
allowing the signal grating to change sign as a function of the grating period[51].
However, it fails to explain the two time scales observed in grating erasure rates,
since the model leads to an erasure rate that is proportional to intensity[52].
In the second model of simultaneous hole-electron competition, electrons and
holes are photoionised from separate recombination centres. In this model, the
parameters such as the light excitation cross section, recombination cross section,
and charge density of one species favours electrons, while those for the other favours
24
holes. The competition between two separate recombination centres, with each
favouring a different charge carrier, allows for two time scales observed in grating
erasure rates[52].
While both simultaneous hole-electron competition models correctly explain
photorefractive phenomena under certain conditions[53], neither model allows for
observations where the grating erasure rate is proportional to a fractional power of
the optical intensity (ie. has a sublinear dependence on intensity) [52]. Simultaneous
hole-electron competition models also fail to predict light induced absorption or a
nonlinear dependence of the space charge field on incident intensity[39]. In 1987,
Motes and Kim[27, 54] suggested that the light induced change in absorption plays a
role in the photorefractive effect, while others suggest that a second set of traps exist
between the donor (acceptor) level and conduction (valence) band[52, 55-57].
2.3.2.3 Two centre model
A secondary trap at an energy level between the donor level and conduction band
was formally developed in 1988[16] as shown in Figure 2.3. In this model, the
shallow traps at the intermediate energy level are partially unfilled at room
temperature. Electrons can therefore be excited into the conduction band from either
the shallow trap level or the deep donor site level. Electrons can also be excited from
the deep donor sites to the shallow trap energy level and then re-excited into the
conduction band. Therefore, charge carriers can be both excited or trapped at two
separate energy levels, where the shallow traps compete with the deep sites for
excited charge carriers[16, 25].
25
The rate equations for the transfer of the concentration of free carriers in the
two centre model is given by[16];
dN1dt
= − S1I + β1( )N1 + γ 1 N1T − N1( )Ne (2.16)
dN2
dt= − S2I + β2( )N2 + γ 2 N2T − N2( )Ne
(2.17)
where Ne is the concentration of free carriers, which will be assumed in this case to
be electrons, and N1, S1 and N2, S2 are the charge concentrations and light excitation
cross-sections of the deep and shallow sites respectively. The addition of the shallow
level traps correctly allows for two dark decay rates observed in a range of
photorefractive materials, such as BSO, BaTiO3[25], reduced KNbO3[58], and
Bi12SiO20[57].
Figure 2.3: Band diagram for the two centre model, with arrows indicating
excitation and recombination of electrons at the photorefractive centres and
[39].
26
The light excitation cross section of the shallow traps and therefore the
shallow trap charge concentration is intensity dependent[25, 59], leading to the
intensity dependence of the photorefractive effect[16, 25]. If the charge density of
the shallow traps is comparable to that of the dark density of the deep sites, then the
photorefractive effect will be a function of intensity, however, if the shallow trap
charge density is relatively low, then the photorefractive effect will not be a function
of intensity[25].
The light excitation cross sections of the deep sites and shallow traps are
wavelength dependent, with their dependence given by[23];
S1 λ( ) = λN1T hc
αwi λ( ) (2.18)
S2 λ( ) = λN1hc
α li λ( ) + S1 λ( ) (2.19)
where αwi and αli are the weak-intensity and light-induced photo absorption
coefficients, respectively. The wavelength dependence of the two levels has been
attributed to different shallow energy levels becoming more active at different
wavelengths[26]. As will be seen in Chapters 3 and 4 the two centre model plays a
key role in ensuring that the imaginary component of the intensity dependent
refractive index has the appropriate sign and magnitude to form low divergence
fields.
27
2.3.3 Effective charge carrier density
The magnitude of the photo-induced refractive index change is determined by the
effective charge carrier density, Neff, which has been shown to be strongly
wavelength dependent in Ce:BaTiO3[24] and other photorefractive crystals[60].
This is not a surprising result, since the energy of the photon that is absorbed must
have sufficient energy to excite the electron (hole) into the conduction (valence)
band. Therefore, it is expected that a cut-off photon frequency will exist, below
which no photorefractive effect is observed. Between wavelengths of 500nm and
750nm, the effective charge carrier density rapidly decreases with increasing
wavelength in Ce:BaTiO3[23]. The effective charge carrier density increases with
intensity[22], to a point where the shallow traps become saturated, after this point,
the effective charge carrier density is independent of intensity as the charge carriers
no longer redistribute[23].
Doping has been shown to increase the total effective trap density[61, 62],
due to the additional charges that are available to be excited. It has been suggested
that this could be due to the increased shallow trap densities causing the deep centres
to become more active[23].
28
2.3.4 Light induced absorption
While the single centre model predicts no light induced absorption, in doped BaTiO3
and LINbO3, light-induced absorption has been attributed to transition metal
impurities at deep donor sites[63-65]. The absorption in this case is related to both
the incident intensity, impurity concentration, and directly related to the absorption
band of the impurity[64].
In the two centre model, the secondary shallow traps are responsible for the
intensity dependent absorption[16, 66], with the light induced absorption given
by[16];
α li = S1 N1 − N1 0( )⎡⎣ ⎤⎦ + S2 N2 − N2 0( )⎡⎣ ⎤⎦ (2.30)
where N1(0) and N2(0) are the dark concentrations of the deep and shallow traps
respectively. The light induced absorption generalised for many different energy
levels, which can exist due to a range of impurities, as[28]:
α li = Sk Nk − Nk 0( )⎡⎣ ⎤⎦k=0,1,2∑ (2.31)
The absorption was further investigated by Tayebati and Mahgerefteh[25],
who gave the total absorption of the photorefractive media as;
α = S1N1 0( ) + S2 − S1( )N2⎡⎣ ⎤⎦hν (2.32)
29
where the first term is the absorption in thermal equilibrium, or the dark absorption,
and the second term accounts for the light induced change in absorption. The relative
magnitudes and intensity dependence of the light excitation cross sections of the
donors (S1) and shallow traps (S2) influence whether light induced absorption ( S2 >
S1 ) or transparency ( S2 < S1 ) will occur. From this equation, it is evident that the
shallow traps have no effect on the absorption in thermal equilibrium, or the dark
absorption.
The light induced absorption in the two centre model is related to the relative
concentrations of the charge carrier densities at the deep and shallow sites, or a
redistribution of free charges between energy levels in the band gap[67]. However, if
the charges are redistributed to different energy levels at roughly the same location,
they will have no effect on the space charge field and therefore on the change in
refractive index. Under these circumstances, the redistribution of free charge carriers
will only influence the intensity dependent absorption[59].
The light induced absorption of photorefractive materials is a function of both
the incident wavelength, and the impurity levels in the material. In Ce:BaTiO3, an
increase in Cerium levels leads to an increase in the light induced absorption at a
wavelength of 514.5nm[68]. Increasing the Cerium concentration from 30 ppm to 50
ppm leads to an increase in the light induced absorption of approximately two
times[61]. In the same material, the light induced absorption decreases as a function
of increasing wavelength in the visible spectrum when pumped at 514.5nm[68]. The
same trend is also observed in undoped BaTiO3 when pumped at the probe
wavelength between 450nm and 500nm[27]. In Rh:BaTiO3, the light induced
absorption spectrum peaks at approximately 800nm, with a local minimum about
600nm[26, 28]. Interestingly, the local minimum observed in the light induced
30
absorption in Rh:BaTiO3 is negative around 600nm[26, 28], indicating light induced
transparency. Similar trends are observed in Cerium doped Lead Barium Niobate
crystals[66]. These results suggest that various PR materials can display both a light
induced increase in absorption or transparency, depending on the incident
wavelength[26, 28].
2.3.5 Complex refractive index
The refractive index of a dispersive medium can be written in terms of real and
imaginary parts[35];
n = nR + iκ (2.33)
where κ is the attenuation coefficient and is related to the absorption coefficient, α
through the relationship[35];
(2.34)
where λ0 is the wavelength in a vacuum. When a dispersive medium exhibits both a
light induced change in refractive index and absorption, the change in refractive
index can be expanded to include both real and imaginary parts[69]
Δn = n2R + in2 I (2.35)
31
where n2R and n2I are the change in the real and imaginary parts of the refractive
index respectively. In this case, the light induced change in absorption is related to
the imaginary part of the refractive index, n2I[69];
Δα =4πn2 Iλ0
(2.36)
Photorefractive materials are an example of dispersive materials that exhibit a
light induced change in refractive index and absorption. Therefore, photorefractive
materials have a refractive index, n, that can be described by;
n = n0 + n2R + in2 I (2.37)
where n0 is the dark component of the refractive index and n2R and n2I are the change
in the real and imaginary parts of the refractive index respectively.
2.4 Photorefractive materials
Photorefractive materials are electrooptic materials that display a change in refractive
index that is dependent on both the intensity and wavelength of the incident
light[21]. When a beam with an inhomogeneous spatial intensity profile is incident
on a photorefractive medium, the resulting change in the refractive index also has an
inhomogeneous spatial profile. For a beam with a Gaussian, or similar, spatial
intensity profile, the greatest change in refractive index is on the beam axis,
decreasing as the distance from the beam axis increases.
32
2.4.1 Self-focusing photorefractive media
In a material where the change in refractive index is positive, the areas of the
Gaussian beam close to the beam axis will encounter a larger refractive index than
the areas further from the beam axis. Under these circumstances, the areas close to
the beam axis will slow relative to the areas further from the beam axis, according
to[35];
(2.39)
where v is the velocity of the light in the medium, c is the speed of light in a vacuum,
and n is the refractive index of the medium. According to Snell’s Law, the areas of
the beam not on the beams axis will bend towards the beam axis, with the net result
being an overall focusing of the beam, as illustrated in Figure 2.4.
Figure 2.4: Phase fronts of a normally diffracting Gaussian beam (dashed lines), and
a Gaussian beam propagating in self-focusing media (solid line).
33
As the beam becomes more focused, the intensity increases and the beam focuses
further. This process can continue to a point where the intensity is so great that
permanent damage can be caused to the photorefractive material.
2.4.2 Self-defocusing photorefractive media
In photorefractive materials where the change in refractive index is negative, the
spatial refractive index profile created in the medium has a minimum on the beam
axis, with the refractive index increasing as a function of the distance from the beam
axis. Therefore, the centre of the beam speeds up relative to the edges, and according
to Snell’s Law, the beam will bend away from the beam axis. As a result, the beam
expands or defocuses as it propagates, as seen in Figure 2.5.
Figure 2.5: Phase fronts of a normally diffracting Gaussian beam (dashed lines), and
a Gaussian beam propagating in self-defocusing media (solid line).
34
Unlike self-focusing media, a Gaussian beam propagating in a self-defocusing
photorefractive medium will decrease in intensity as the beam expands, and the
resulting change in refractive index will also decrease. Therefore, the rate at which
the beam expands as it propagates decreases as it propagates. Examples of nominally
self-defocusing photorefractive materials are LiNbO3 and BaTiO3. Recently, a self-
focusing effect was observed in unbiased self-defocusing photorefractive media[13].
The mechanism behind this effect is currently unexplained, and is examined in
Chapter 5.
2.4.3 Biased photorefractive media
Photorefractive materials where the photorefractive effect is due to the bulk
photovoltaic current or the diffusion current can be biased with an external field.
This external field gives rise to the drift current described in Section 2.3.11. If the
applied field is large enough, then the drift current can become the dominant current
in the photorefractive material. In this case, the change in refractive index becomes a
function of the applied external field, and both the strength and direction of the space
charge field can be externally controlled and can become independent on the
intensity of the incident beam. Therefore, by applying a sufficient external field, self-
defocusing media can behave as self-focusing and vice-versa.
The external field required for biasing photorefractive materials can be found
in a variety of forms. By applying a DC bias voltage of the order of 1 kV, BaTiO3
has been observed to display a stationary self-focusing photorefractive effect at an
incident wavelength of 633nm[70]. Similar results have been reported when the
photorefractive material is illuminated with a homogeneous background beam at a
different wavelength in LiNbO3[71, 72].
35
2.6 Gaussian Beam Optics
Laser beams are examples of electromagnetic fields that can be described as having
an intensity distribution concentrated on the beam axis, decreasing as the distance
from the beam axis increases. As the beam propagates from the minimum spot size
where the wavefront is planar, the beam energy spreads out, and the wavefront
curvature becomes finite. The output from many laser systems have been engineered
so that the electromagnetic field distribution has a TEM00 Gaussian spatial profile
that is given by[14];
E r, z( ) = E0w0w z( ) exp i kr2
2q z( ) + kz − tan−1 z
zR
⎧⎨⎩
⎫⎬⎭
⎡
⎣⎢
⎤
⎦⎥
⎧⎨⎪
⎩⎪
⎫⎬⎪
⎭⎪ (2.40)
where E0 is the maximum field amplitude, w(z) is the radius of the beam, defined at
the radial (transverse to the beam propagation direction) distance where the beam
intensity is of the maximum intensity. The minimum beam radius, w0, is the
radius of the minimum spot size, called the beam waist and occurs at the position z =
0. The variable k is the wavenumber in the medium, defined as;
k = 2πnλ
(2.41)
36
where n is the refractive index of the medium, and λ is the wavelength of the
electromagnetic field, and q(z) is the complex beam parameter, defined as[14, 18, 73,
74]:
1q z( ) =
1R z( ) − i
λnπw2 z( ) (2.42)
The complex beam parameter describes the profile of the Gaussian beam as a
function of z position in terms of the wavefront curvature, R(z), and the beam radius,
w(z). At the beam waist, the beam has a planar wavefront, and the complex beam
parameter reduces to[73]:
q0 = inπw0
2
λ (2.43)
After propagating a distance z from the beam waist, the complex beam parameter is
given by[73];
q = q0 + z = inπw0
2
λ+ z (2.44)
37
Combining equations (2.42) and (2.44), and equating real and imaginary parts, gives
the evolution of the beam as a function distance from the beam waist in terms of the
beam radius and the wavefront curvature[14, 73];
w z( ) = w0 1+zzR
⎛⎝⎜
⎞⎠⎟
2⎡
⎣⎢⎢
⎤
⎦⎥⎥
1 2
(2.45)
R z( ) = z 1+ zRz
⎛⎝⎜
⎞⎠⎟2⎡
⎣⎢⎢
⎤
⎦⎥⎥
(2.46)
where zR is the Rayleigh range and is defined by[14]:
zR =nπw0
2
λ (2.47)
For large distances from the beam waist, z » zR, both the beam radius and the
wavefront curvature can be approximated as linear functions of the z position[75],
with a divergence angle in the far field equal to:
(2.48)
However, within the Rayleigh range, geometrical optics is no longer valid, and the
beam radius is approximately constant and the wavefront curvature becomes a
strongly dependent on z, having a minimum value at z = zR, before rapidly
approaching infinity at the beam waist[75]. The evolution of a Gaussian beam can
be seen in Figure 2.6.
38
Figure 2.6: Profile and phase fronts of a Gaussian beam as functions of the
propagation distance, z, from the waist position, w(0). The beam divergence in the
far field is given by θ[73].
2.6.1 Lenses
When a Gaussian beam is incident on an ideal thin lens, the wavefront curvature is
transformed, producing a new beam waist location and position. An ideal thin lens is
one where the transverse field distribution is not altered by the lens element.
However, the transformation of a Gaussian beam by a thin lens also introduces a
focal shift[75-79] which is different to what is predicted by geometrical optics. For
thin lenses, the beam size on either side of the lens are equal[18, 76];
w1 = w2 (2.49)
39
and the wavefront curvature of the beam at the incident (R1) and exit (R2) faces of the
lens are related to the focal length of the lens (f) through the equation[18, 73, 76];
(2.50)
In terms of the complex beam parameters, the Gaussian beam at each face of the thin
lens is defined as[18, 73];
(2.51)
If the beam waist of the incident beam is a distance d1 from the thin lens, then the
beam waist after propagating through the lens will be at a position d2. The complex
beam parameters in this case can be found by combining equations (2.51) and
(2.44)[73];
q20 =1− d2 f( )q10 + d1 + d2 − d1d2 f( )
− q10 f( ) + 1− d1 f( ) (2.52)
where q10 and q20 define the waist of the incident and exit Gaussian beams
respectively. Equation (2.52) therefore describes the transformation of a Gaussian
beam by a thin lens, which is illustrated in Figure 2.7.
40
Figure 2.7: Transformation of a Gaussian beam due to a thin lens, where q10 and q20
are the complex beam parameters before and after propagating through the thin lens.
Equation (2.52) can be applied multiple times when a Gaussian beam encounters
multiple thin lenses. More complicated lens elements can be thought of as multiple
thin lenses. In these cases, Equation (2.52) can be generalised to[18, 73];
q2 =Aq1 + BCq1 + D
(2.53)
where A, B, C, and D are elements of the ray transfer matrix. Therefore, providing
the elements of the ray transfer matrix are known, the form of the Gaussian beam
after propagating through the medium can be calculated. The ray transfer matrices
for several optical structures can be found in [73]. As well as thin lenses and
combinations of thin lenses, some other common lens elements are optically thick, or
transform the field by having a Graded Refractive Index (GRIN). These will be dealt
with separately.
41
2.6.1.1 Thick Lenses
A thick lens is one where the thickness of the lens is sufficient that equation (8) no
longer holds, and these are widely used for optical fibre coupling[80]. The focal
length of a thick lens is given as[81];
1f= n −1( ) 1
r1−1r2+n −1( )dnr1r2
⎡
⎣⎢
⎤
⎦⎥ (2.54)
where r1 and r2 are the radii of the incident and exit faces, d is the lens thickness, and
n is the refractive index of the lens material, as depicted in Figure 2.8.
Figure 2.8: Transformation of a Gaussian beam due to a thick lens, where q10 and
q20 are the complex beam parameters before and after propagating through the thick
lens.
The properties of a Gaussian beam after transmission through a thick lens are
therefore dependent on the curvature of each surface and thickness of the lens[80-
83]. When both surfaces of the lens have the same curvature, the dependence on the
thickness of the lens is significant when the focal length of an equivalent thin lens is
larger than the Rayleigh length[83]. When one surface of the thick lens is planar,
then the transmitted beam parameters are highly dependent on the incident
surface[82, 83]. If the incident surface is concave or convex, then the position of the
42
transmitted beam waist is particularly dependent on the lens thickness, while the
beam waist magnitude is only a function of the incident waist magnitude and
effective focal length[83]. If the incident surface is flat, then both the position and
magnitude of the transmitted beam waist are functions of the lens thickness[83].
Detailed expressions for the transformation of Gaussian beams by thick lenses are
presented in reference [83].
2.6.1.2 GRIN Lenses
A GRIN lens is a thick lens with a refractive index profile given by[73, 84-86];
n r( ) = n0 1−A0r
2
2⎛⎝⎜
⎞⎠⎟
(2.55)
where r is the transverse coordinate, and A0 is a positive constant defining the
refractive index gradient.
Figure 2.9: Transformation of a Gaussian beam due to a GRIN lens, where q10 and
q20 are the complex beam parameters before and after propagating through the thick
lens.
43
Due to their flat input and output surfaces, GRIN lenses are widely used to couple
radiation to and from optical fibres and other optical components[84, 85]. The
transformation of the complex beam parameter as a function of propagation distance,
z, of such a system is[86];
q z( ) =cos z A0( )q0 + 1
n0 A0sin z A0( )
−n0 A0 sin z A0( )q0 + cos z A0( ) (2.56)
Giving the beam radius w(z) and wavefront curvature R(z) using equation (2.42)
as[86];
1R z( ) =
AC + BD zR2
A2 + B zR( )2 (2.57)
λnπw2 z( ) = −
1 zR2
A2 + B zR( )2 (2.58)
where A, B, C, and D are found by comparing equations (2.56) and (2.42);
(2.59)
Therefore, the transmitted beam properties of the Gaussian beam after propagating
through a GRIN lens is determined by the GRIN lens parameter, A0, and the
44
propagation length z[86]. It is evident from equations (2.56-2.59) that as the beam
propagates within the medium, the radius of the Gaussian beam fluctuates
sinusoidally between maximum and minimum values determined by the GRIN lens
parameter, A0. The period of these fluctuations, P, is[86];
(2.60)
When the beam radius is at its maximum and minimum values, the wavefront of the
field is planar, analogous to a converging Gaussian beam passing through its beam
waist, and a diverging Gaussian beam being focused by a positive lens[86].
2.7 Gaussian beam propagation in inhomogeneous
media
In some cases, inhomogeneous media can act in a way that is similar to a lens[87]. In
such an inhomogeneous medium, where the variation in the wavevector, k, is equal
to k2, the complex beam parameter after a propagation length z, is equal to[18, 73]:
q z( ) =cos k2
kz
⎛⎝⎜
⎞⎠⎟q0 +
kk2sin k2
kz
⎛⎝⎜
⎞⎠⎟
− sin k2kz
⎛⎝⎜
⎞⎠⎟
k2kq0 + cos
k2kz
⎛⎝⎜
⎞⎠⎟
(2.61)
By comparing this equation to the ray transfer matrix given in equation (2.53), the
lens-like properties of an inhomogeneous medium can be seen. In addition, it can be
45
seen that the propagation of the Gaussian beam in inhomogeneous media is
dependent on the profile of the variation of the wavevector within the medium, k2.
In PR and other nonlinear optical media, the inhomogeneities, k2, become
functions of the incident light, and thus so are the lens-like properties of the medium.
In nonlinear self-focusing media, the medium can be modelled as a combination of a
positive thin lens, and a negative propagation distance[88]. The analysis was
however only valid for a narrow range of low incident beam powers, where self-
focusing effects are minimal[88]. More recently, a wavefront study of converging
Gaussian beams propagating in a self-focusing medium found that the radius of
curvature of the wavefronts increased after propagating through the medium[89].
The same study also found that the radius of curvature of the wavefronts decreased
for diverging incident beams, and that the opposite effect is observed for self-
defocusing media[89]. Recently, it has also been found that nominally self-
defocusing BaTiO3 can exhibit a self-focusing effect under intense illumination[13],
acting analogously to a positive focal length lens.
As discussed previously, most nonlinear media display an intensity dependent
absorption or gain. In 2006, the intensity dependent absorption or gain, related to the
imaginary part of the change in refractive index, in the propagation of optical beams
in nonlinear media was shown to be of great importance[90]. Including these
absorption effects, an initially converging Gaussian beam in nonlinear Kerr media
will continue to converge, and then either diverge or self-focus, depending on the
initial beam parameters and the maximum intensity[91]. The beam divergence occurs
as either the propagation distance or absorption cause the beam to lose sufficient
intensity, reducing the self-focusing effect that stops the beam from diverging. On
46
the other hand, if the incident beam is sufficiently intense, the self-focusing effect
continues to balance diffraction in the presence of further losses [91].
With no transverse refractive index variation, the general case of the
propagation of a Gaussian beam in a lens-like medium with either gain or absorption
variation reveals that the beam radius and wavefront curvature will fluctuate
according to[92];
1q2
=1q1
sinh 2 zR1
− δ⎛⎝⎜
⎞⎠⎟
⎡
⎣⎢
⎤
⎦⎥ − i sin 2
zR1
−ϕ⎛⎝⎜
⎞⎠⎟
⎡
⎣⎢
⎤
⎦⎥
cosh 2 zR1
− δ⎛⎝⎜
⎞⎠⎟
⎡
⎣⎢
⎤
⎦⎥ + cos 2
zR1
−ϕ⎛⎝⎜
⎞⎠⎟
⎡
⎣⎢
⎤
⎦⎥
(2.62)
where R1 is the incident wavefront curvature and δ and ϕ are determined by the
initial conditions of the beam. Here we can see that the addition of absorption or gain
to the nonlinear medium has resulted in the inclusion of hyperbolic trigonometric
functions which cause the beam to either expand or collapse, due to gain or
absorption, depending on the material and incident beam parameters[92]. In a
material with a quadratic gain profile, it is possible to theoretically realise a beam
which propagates with a finite wavefront curvature and beam radius given by[92];
(2.63)
(2.64)
47
where α2 is equal to the variation in the gain of the medium. Inspection of these
parameters reveals that this occurs at the Rayleigh range, where the wavefront
curvature is at a minimum. In this case, the gain profile of the medium counteracts
the expected divergence from this point, and the beam will propagate with no spatial
divergence as a spatial soliton[92]. Thus, spatial optical solitons are predicted in both
self-focusing nonlinear media, and in lens-like media with a quadratic gain profile.
2.8 Spatial optical solitons
Spatial optical solitons are optical beams that propagate without spatial divergence[7,
11]. In addition, they are stable to small perturbations, and capable of phase
dependent particle-like interactions[93]. In photorefractive media, they are formed
when a plane wave, such as the beam waist of a Gaussian beam, is incident on a self-
focusing (or biased self-defocusing) PR medium. If the self-focusing nature of the
PR medium exactly matches the beams natural divergence, then the beam will
propagate without divergence as a spatial soliton[10]. The comparison between an
optical spatial soliton and a normally diffracting Gaussian beam is illustrated in
Figure 2.10. An optical spatial soliton is a solution to the appropriate nonlinear
Schrodinger equation[14];
∂A∂z
−i2k
∂2A∂x2
= i 2n2kn0
A 2 A (2.65)
where A is the amplitude of the wave. The solution for a soliton, which propagates
without spatial variation, takes the form;
48
(2.66)
where the transverse field profile of the beam is described by a sech function, with a
peak magnitude equal to;
A02 =
n02n2
1kw
⎛⎝⎜
⎞⎠⎟2
(2.67)
where k is equal to the wavevector in the medium.
Figure 2.10: Comparison between a spatial optical soliton (a) and a normally
diffracting beam (b)[29]
Spatial solitons can also be formed in optical Kerr media with the same field
as PR spatial solitons[8, 29], although in this case, beam powers in excess of 10
orders of magnitude larger than for PR spatial solitons are required[94]. In addition,
49
two dimensional Kerr spatial solitons can not exist in bulk media, requiring a slab
waveguide to contain the beam in one transverse direction[8, 29, 94].
Photorefractive spatial solitons can be either bright, dark, or gray[95-98].
While bright spatial solitons possess a maximum intensity at the centre of the
propagating beam, dark spatial solitons are dark areas in a constant background
intensity[96]. Dark PR spatial solitons are the opposite of bright spatial solitons, and
are therefore formed in material that is either nominally self-defocusing, or in a self-
focusing medium with a reversed external biasing field[96, 98, 99]. Gray solitons are
related to dark solitons, however, they do not have a constant phase across the soliton
width[96].
The required space charge field and resultant change in refractive index for
the formation of PR spatial solitons can be a result of an external biasing field (PR
screening solitons), or due to background illumination (photovoltaic solitons)[11]. In
the absence of either of these influences, PR spatial solitons can be formed when the
natural self-focusing effect of the PR crystal exactly balances the beam divergence.
The observation of apparent self-focusing in unbiased self-defocusing PR media
could lead to the possibility of PR spatial solitons forming in unbiased self-
defocusing media. These types of spatial solitons, and the conditions required for
their formation are discussed in Chapters 3 and 5. PR screening solitons and
photovoltaic solitons will be discussed separately in the following sections.
50
2.8.1 PR screening solitons
PR screening solitons were first predicted in the early 1990’s[10, 100] and observed
soon after[94, 95, 101]. They are formed when a self-defocusing PR media is biased
with an external electric field, allowing careful manipulation of the change in
refractive index, according to equations 2.9 and 2.10, to exactly counteract beam
divergence, with a negative refractive index change that is a function of the incident
intensity, applied voltage, and dark irradiance[94-96, 99]. In this case, the dark
irradiance is defined as the ratio of the dark thermal regeneration rate to the photon
absorption cross section[99]. The space-charge field created is due to charge
migration as a result of the drift current, and is therefore a function of the applied
voltage rather than the incident light intensity[94, 102]. As a result, the profile of a
PR screening soliton is maintained in the presence of either gain or loss in the
medium[10, 101].
In 1993, PR screening solitons were first observed in Strontium Barium
Niobate (SBN), with an external voltage in the order of 100 V/cm. These screening
solitons were found to be temporally unstable, or transient[101]. The following year,
steady-state PR screening solitons were observed in Barium Titanium Oxide
(BTO)[102]. Due to the weaker electro optic nature of BTO compared to SBN, a
biasing voltage in the order of kilovolts per centimetre was required for the
formation of PR screening solitons[102]. At high biasing voltages (kV/cm) and with
homogenous background illumination in SBN, two-dimensional PR screening spatial
solitons were first observed in 1995[94]. In this case, the homogenous background
illumination is used to create an artificial dark irradiance, thus allowing the relative
difference between this and the peak soliton intensity to be controlled, and reducing
the required applied biasing voltage[94]. This process allowed solitons with widths
51
less than 10 µm in both dimensions to propagate in the steady-state, with a change in
refractive index ofΔn = −13.5 ×10−4 [94]. In all these cases, the incident power of the
beam was low enough to ensure that beam fanning, and other PR effects detrimental
to the formation of PR screening solitons were not observed[101, 102]
PR screening solitons are stable against small perturbations[93], and can be
formed at incident intensities ranging from microwatts to hundreds of Megawatts per
square centimetre[99]. However, regardless of the intensity of the incident light, the
ratio of the peak soliton intensity to the background and dark irradiance is relatively
constant from two times at low intensities, and up to five times at high intensities[94,
99]. The shape of a PR screening soliton is unique, and dependent on the material,
irradiance, and applied voltage[93, 95, 96, 99].
2.8.2 Photovoltaic solitons
PR photovoltaic spatial solitons are formed in PR media where the charge migration
process is a result of the bulk photovoltaic current[98]. Due to the nature of the bulk
photovoltaic current, which according to equation 2.11 is proportional to the
intensity of the incident light, these type of solitons are dependent on the incident
intensity[98], and were first predicted in 1994[103]. Similarly to PR screening
solitons, the ratio between the intensity of the incident beam and the dark irradiance
is an important factor, with the dark irradiance manipulated with incoherent
illumination[103].
In 1995, photovoltaic spatial solitons were first observed in LiNbO3[104]. As
unbiased LiNbO3 is self-defocusing, displaying a negative refractive index
perturbation, these photovoltaic solitons were dark in nature, and the relatively weak
electo-optic coefficients led to steady state being reached in approximately 15
52
minutes[104]. The first two-dimensional bright photovoltaic spatial solitons were
observed in self-focusing Cu:KNSBN[105]. As the elecro-optic coefficient is
significantly larger than LiNbO3, steady state was reached in less than 0.5 s, with
incident intensities as low as 3 W/cm2[105].
In a way analogous to the applied electric field in PR screening solitons, the
background illumination can be used to influence the crystal parameters to change
from self-defocusing, to self-focusing[72]. As a result, both dark and bright
photovoltaic spatial solitons have been found in PR materials with a positive, and a
negative refractive index perturbation[71, 97]. In these cases, the wavelength of the
background illumination was used to manipulate the refractive index
perturbation[71].
2.8.3 Soliton Waveguides
A bright PR spatial soliton is formed in a refractive index profile that is greatest on
the beam axis, and decreasing towards the edges. The result is that the incident beam
is trapped in a self-induced waveguide[11]. Since the PR effect is wavelength
dependent, the waveguide formed by the soliton can be used to guide light at a
wavelength to which the material is less sensitive[30, 31, 106, 107]. As the material
is less sensitive to the guided beam, it can have much higher intensities than the
soliton beam[102, 108]. In addition, the beam will continue to be guided once the
soliton beam and background beam (or applied field) are turned off, until the
waveguide is erased due to dark decay or incoherent illumination[94, 108, 109].
Dark PR spatial solitons can also be used as waveguides to guide beams at
less sensitive wavelengths in one transverse dimension[104, 110]. In addition to
guiding cw beams, soliton waveguides can be used to guide femtosecond pulsed
53
light[111, 112]. In this case, the soliton was written with cw light, and the guided
pulses propagated with low temporal dispersion[109], making the waveguides
suitable for efficient optical interconnects[111].
Analogous to optical fibres, soliton waveguides can be used to guide a
number of different modes. Bright one dimensional soliton waveguides have been
reported to guide TEM00, TEM10, and TEM20 Gaussian modes, with each mode
requiring a different ratio between the peak soliton intensity and the sum of the dark
irradiance and background illumination[31]. For the case of the TEM20 mode, only
the central lobe is guided, while the outer lobes were diffracted[31]. On the other
hand, dark one dimensional soliton waveguides were only capable of guiding TEM00
beams, regardless of the intensity ratio[31]. In two dimensional bright soliton
waveguides, similar trends are observed, with TEM00, TEM10, TEM01, and TEM20
modes being guided with a dependence on the intensity ratio of the incident soliton.
2.8.4 Soliton Interactions
Of great interest to photonic applications of spatial solitons is their particle-like
interactions[17]. Soliton interactions can be attractive and repulsive, depending on
the relative phase of the interacting solitons[17, 32, 113-117]. The strength of the
interaction is a function of the relative amplitude of the solitons[93], their
separation[117], diameter[115, 118], and interaction angle[32, 113, 114, 116].
Bright spatial solitons display particle-like collisions[116], with each beam
maintaining its properties following the collision[7, 119]. In the case of bright
solitons, two in-phase solitons will attract each other, while out of phase bright
solitons will repel[7, 93, 116]. As the two spatial solitons interact, the beams begin to
overlap, causing the intensity in the region between the two beams to change[7].
54
When the two solitons are in-phase, the intensity increases, causing the refractive
index to increase, drawing the two beams together. Conversely, for out of phase
solitons, the opposite occurs, and the two beams are repelled[7].When the phase of
the two solitons is not completely in or out of phase, the solitons interact somewhat
repelling each other, with some energy transfer between the solitons[17, 115].
Experimental observations of these interactions are illustrated in Figure 2.11.
Figure 2.11: Images and beam profiles illustrating one-dimensional PR screening
soliton interactions in a 6 mm long SBN crystal; a, parallel input beams with 18 µm
separation; b, output under normal diffraction; c, output when beams launched
separately; d, output for in-phase soliton collision showing soliton fusion; e, output
for soliton collision with phase difference showing energy transfer and slight
repulsion, with separation equal to 35 µm; f, output for out of phase soliton collision
showing repulsion, with separation equal to 46 µm[115].
In addition, the interaction angle between the two solitons greatly effects the
outcome of the soliton collision[11]. When the interaction is small (crossing angle
inside the crystal less than 0.5°), the attraction between in-phase solitons causes them
to fuse together, as seen for solitons launched parallel to each other in Figure 2[32,
55
115, 116]. On the other hand, at large interaction angles (crossing angle inside the
crystal greater than 1.5°), no interaction is seen, with the solitons passing through
each other unaffected[116]. The interaction strength within the PR media is
dependent on the relative diameter and separation of the two spatial solitons[93]. It
has been found that the strength of the interaction increases exponentially as the
soliton separation decreases[17].
Spatial solitons propagating in PR media can also be bent due to the factors
such as PR diffusion, drift and applied electric fields[93, 120, 121]. Increases in the
applied electric field result in monotonic increases in the soliton deflection, while
increasing the ratio of the peak soliton intensity to the dark irradiance influenced
bending up to a maximum value of approximately six times the soliton
diameter[121]. Limits to the self-bending of solitons in this way are found when the
soliton becomes unstable and filamentation occurs[121]. PR drift and diffusion
mechanisms cause the soliton to bend in a way analogous to PR beam fanning
discussed previously, with no apparent filamentation occurring[93, 120].
Combining the waveguide and interaction properties of spatial solitons allows
for all rewritable optical switches to be created[114]. Spatial solitons will continue to
guide the probe beam through an interaction, creating an ‘X’ junction, or splitting or
combining the probe beam into two parts, creating a ‘Y’ junction[11, 32-34]. Thus,
configurable optical switches can be created by varying the relative phase of the two
soliton writing beams[11].
56
2.9 Methods of analysis
In this section, the experimental, analytical, and numerical methods will be
introduced. These methods are employed throughout the project to analyse the
propagation of Gaussian beams through self-defocusing PR media. Far field
measurements were taken to determine the profile of the Gaussian beam after
propagation through the PR medium under various circumstances. The intensity
distribution of the far field images was analysed, comparing the measured intensities
to theoretical derived profiles. Least squares data fitting was used extensively in
analysing the far field images. Measurements of the intensity dependent absorption
of the PR medium at a variety of wavelengths were conducted by comparing the
beam intensity before and after passing through the PR medium. Analytically and
numerically, the problem of a low power Gaussian beam propagating in PR medium
can be simplified in two ways. Firstly, at low beam powers, the intensity dependent
refractive index profile can be treated as quadratic, approximated by;
n r( ) ≈ n0 − 2n2I0w2 r
2 (2.68)
Secondly, an incident low power Gaussian beam maintains its Gaussian profile at all
times during propagation. These two simplifications allowed both analytical results
to be possible, and a detailed numerical analysis to be conducted.
57
2.9.1 Far field image analysis
Far field images depict the beam a distance significantly larger than the Rayleigh
length after it has propagated through the PR material. In the far field, the evolution
of the beam radius is a linear function of the distance from the beam waist, and the
wavefront curvature is approximately equal to the propagation distance. Far field
images were captured with a CCD array as colour bitmap images, and analysed using
Scilab software. The CCD arrays used were commercially available, Thorlabs®
DCU223C, with a resolution of 1024 × 768 pixels, and a pixel size of 4.65 µm × 4.65
µm.
Initial far field images were taken with the PR medium at various distances
relative to the incident beam waist to determine if a low power Gaussian beam
maintained its Gaussian spatial profile after propagating through the medium. In this
case, the intensity profile of the image was analysed, and a Gaussian spatial profile
was least squares fitted to the data. Results of this analysis are presented in Chapter
3, and confirm that the Gaussian spatial profile is maintained for the field intensities
considered.
Subsequent far field images were taken at two different propagation
distances. A 50 / 50 beam splitter was used to capture the two images simultaneously
with two CCD arrays placed at different distances after a beam splitter. By obtaining
the spatial profile of the far field at two different propagation distances, the profile of
the Gaussian beam can be completely described using equations (2.45 - 2.48) and
elementary trigonometry. Far field images were used in a z-scan experimental setup
(discussed in Section 2.9.2). This enabled the effect of the PR medium on a Gaussian
beam with different incident parameters to be measured.
58
During the course of this PhD, over 50,000 far field images were analysed.
To ensure repeatability and consistency in the measured far field profiles, Scilab
code was written to automatically calculate the horizontal Gaussian beam radius,
w(z), together with an estimate of the uncertainty. A series of steps were carried out
to produce this result. The code loaded a bitmap file, and identified the area of
highest intensity. Next, five vertical cross sections of the image were taken around
the previously identified area, separated by 5 pixels. Gaussian spatial profiles were
least squares fitted to these five cross sections, with the peak value of the five plots
taken as the peak intensity value of the image. A total of 41 adjacent horizontal cross
sections were then taken about this point, comprising of the cross section at the peak
value, and the 20 cross sections above and below. Gaussian spatial profiles were
least squares fitted to these 41 cross sections. From these 41 sets of data, the
Gaussian beam radius, w(z), and the standard deviation were calculated.
Figure 2.12 shows a typical far field image, with a cross section and fitted
Gaussian beam profile. The horizontal line on the far field image represents where
the cross section was taken from in this case. From the cross section, the associated
noise in the image can be seen. In addition to sampling a large area of each image for
analysis, the z-scan (discussed in Section 2.9.2) was repeated numerous times. This
aided in ensuring the methods used were repeatable, and eliminating the effects of
noise as much as possible. In the case of a far field interference pattern, as is the case
in Chapter 6, a similar process was done, except that a Gaussian spatial profile was
least squares fitted to each peak, with the horizontal co-ordinate of each peak with a
corresponding error recorded.
59
Figure 2.12: Sample far field image (left) with the cross section (dots) taken at the
horizontal line, and fitted Gaussian profile (line, right).
2.9.2 Z-scan
A z-scan technique involves translating an optical medium along the direction of
propagation, z, of an incident Gaussian beam[89, 122-124]. Under these
circumstances the total beam energy is constant, however, by varying the distance
from the beam waist, the beam is incident on the medium with a different complex
beam parameter[124]. As a result, a z-scan enables the variation of both the
wavefront curvature and beam radius simultaneously. Different combinations of
wavefront curvature and beam radius are obtained by varying the incident beam
waist, w0, according to equations (2.45) and (2.46). The intensity of the incident
beam can be adjusted via the total beam power, or the incident beam waist.
60
2.9.3 Numerical wavefront study
A numerical wavefront study of the Gaussian beam propagating through the PR
medium allowed the complete properties of the beam to be determined during
propagation. With the incident beam parameters known, the initial wavefront can be
decomposed into numerous point sources, as in a geometrical optics approach. The
intensity, I0, and the beam radius, w(z), allows the quadratic refractive index profile
to be calculated through equation (2.68). The effect of this refractive index profile on
each individual point source can then be calculated using Snell’s Law;
n1 sinθ1 = n2 sinθ2 (2.69 )
where θ1 and θ2 are the angles of incidence and refraction, and n1 and n2 are the
relative refractive indices of the two effective media. Thus, after propagation through
the section of PR media with thickness, Δz, each point source will be refracted by the
quadratic refractive index profile. The point sources can then be reconstructed to
form a new wavefront, which is then incident on the next section of PR media with
thickness, Δz.
To eliminate the propagation and amplification of numerical noise, the
wavefronts after propagating through each section of the PR media were least
squares fitted to a Gaussian spatial beam profile. The fitting parameters for the least
squares fit were the maximum field amplitude, E0, and the beam radius, w(z).
Therefore, after each section of PR media, the transmitted field can be uniquely
described by its own complex beam parameter, q, and as a result, the Gaussian beam
can be completely described at all times within the PR medium and in the far field.
61
Comparison between far field measurements of both the numerical model and the
experimental z-scan allowed the validity of this numerical approach to be confirmed.
62
3. Theoretical description of low divergence Gaussian
fields in self-defocusing photorefractive media
Esa Jaatinen1, Michael W. Jones1
1School of Physical and Chemical Sciences, Queensland University of Technology, 2
George Street, Brisbane QLD 4000, Australia
Published in: Optics Communications 281, 3201 (2008)
Corresponding Author
Dr E. Jaatinen
School of Physical and Chemical Sciences
Queensland University of Technology
2 George Street
Brisbane QLD 4000, Australia
Fax: +61 7 3138 9079
Email: e.jaatinen@qut.edu.au
63
The authors listed below have certified* that; 1. they meet criteria for authorship in that they have participated in the
conception, execution, or interpretation, of at least that part of the publication in their field of expertise;
2. they take public responsibility for their part of the publication, except for the responsible author who accepts overall responsibility for the publication;
3. there are no other authors according to these criteria; 4. potential conflicts of interest have been disclosed to (a) granting bodies, (b)
the editor or publisher of journals and their publications, and (c) the head of the responsible academic unit, and
5. they agree to the use of the publication in the student’s thesis and its publication on the Australasian Digital Thesis database consistent with any limitations set by publisher requirements.
In the case of this chapter: Theoretical description of low divergence Gaussian fields in self-defocusing photorefractive media E. Jaatinen, M. W. Jones Optics Communications 281, 3201 (2008)
Contributor Statement of contribution*
Esa Jaatinen Original idea, conducted analysis (numerical and analytical),
paper writing, discussion
Michael W. Jones
Signature
Date
Undertook experiments, conducted experimental analysis,
discussion, paper writing
Principal Supervisor Confirmation
I have sighted email or other correspondence from all Co-authors confirming their
certifying authorship
______________________ _____________________________ ____________
Name Signature Date
64
Theoretical description of low divergence Gaussian fieldsin self-defocusing photorefractive media
Esa Jaatinen *, Michael W. Jones
Applied Optics Program, Queensland University of Technology, GPO Box 2434, Brisbane Qld 4001, Australia
Received 14 December 2007; received in revised form 28 January 2008; accepted 8 February 2008
Abstract
Experimental evidence is presented that shows that low intensity optical fields preserve their Gaussian transverse amplitude distribu-tion as they propagate through self-defocusing Ce:BaTiO3 photorefractive media. The Gaussian nature of the field is used in a theoreticaltreatment to derive conditions under which bright solitons are formed in photorefractive media that have a light induced refractive indexthat is approximately quadratic. This analysis shows that while it is not possible to produce a single bright soliton in self-defocusingmedia that it is possible to minimize the field’s divergence such that the change in beam radius is small (<1%) over large propagationdistances (!1 m). An imaginary light induced refractive index component is necessary to generate the low divergence fields in bothself-focusing and self-defocusing media when illuminated with Gaussian fields that have a non-planar wavefront.! 2008 Elsevier B.V. All rights reserved.
www.elsevier.com/locate/optcom
Available online at www.sciencedirect.com
Optics Communications 281 (2008) 3201–3207
71
4. Transition from intensity dependent absorption to
transparency in Ce:BaTiO3
Michael W. Jones1, Esa Jaatinen1
1School of Physical and Chemical Sciences, Queensland University of Technology, 2
George Street, Brisbane QLD 4000, Australia
Published in: Optical Materials 31, 122 (2008)
Corresponding Author
Michael W. Jones
School of Physical and Chemical Sciences
Queensland University of Technology
2 George Street
Brisbane QLD 4000, Australia
Fax: +61 7 3138 9079
Email: mw.jones@qut.edu.au
Keywords: Ce:BaTiO3, Intensity dependent transparency, Intensity dependent
absorption
72
The authors listed below have certified* that; 1. they meet criteria for authorship in that they have participated in the
conception, execution, or interpretation, of at least that part of the publication in their field of expertise;
2. they take public responsibility for their part of the publication, except for the responsible author who accepts overall responsibility for the publication;
3. there are no other authors according to these criteria; 4. potential conflicts of interest have been disclosed to (a) granting bodies, (b)
the editor or publisher of journals and their publications, and (c) the head of the responsible academic unit, and
5. they agree to the use of the publication in the student’s thesis and its publication on the Australasian Digital Thesis database consistent with any limitations set by publisher requirements.
In the case of this chapter: Transition from intensity dependent absorption to transparency in Ce:BaTiO3 M. W. Jones, E. Jaatinen, Optics Materials 31, 122 (2008)
Contributor Statement of contribution*
Michael W. Jones
Signature
Date
Original idea, undertook experiments, conducted analysis
(experimental and numerical), paper writing, data analysis,
discussion
Esa Jaatinen Interpretation of results, discussion, paper writing
Principal Supervisor Confirmation
I have sighted email or other correspondence from all Co-authors confirming their
certifying authorship
______________________ _____________________________ ____________
Name Signature Date
73
Transition from intensity dependent absorptionto transparency in Ce:BaTiO3
Michael W. Jones *, Esa Jaatinen
Applied Optics Program, Queensland University of Technology, GPO Box 2434, Brisbane QLD 4001, Australia
Received 27 September 2007; received in revised form 2 February 2008; accepted 3 February 2008Available online 19 March 2008
Abstract
The intensity dependent absorption and transparency of Ce:BaTiO3 is examined in relation to the two trap model of the photorefrac-tive e!ect. At wavelengths of both 532 nm and 633 nm, the material exhibits intensity dependent absorption, while at a wavelength of790 nm, intensity dependent transparency is observed, with a transition between absorption and transparency at approximately650 nm. Experimental data is matched to the two trap theoretical model with good agreement. Analysis of this match shows that thelight excitation cross-section of the shallow traps are the main contributors to the observed intensity dependent transition.! 2008 Elsevier B.V. All rights reserved.
PACS: 78.20.C; 42.70.N
Keywords: Ce:BaTiO3; Intensity dependent transparency; Intensity dependent absorption
www.elsevier.com/locate/optmat
Available online at www.sciencedirect.com
Optical Materials 31 (2008) 122–125
77
5. Propagation of low-intensity Gaussian fields in
photorefractive media with real and imaginary
intensity-dependent refractive index components
Michael W. Jones1, Esa Jaatinen1, G. W. Michael
1School of Physical and Chemical Sciences, Queensland University of Technology, 2
George Street, Brisbane QLD 4000, Australia
Published in: Applied Physics B. doi: 10.1007/s00340-010-4309-7
Corresponding Author
Michael W. Jones
School of Physical and Chemical Sciences
Queensland University of Technology
2 George Street
Brisbane QLD 4000, Australia
Fax: +61 7 3138 9079
Email: mw.jones@qut.edu.au
Keywords: Photorefractive optics, spatial solitons
78
The authors listed below have certified* that; 1. they meet criteria for authorship in that they have participated in the
conception, execution, or interpretation, of at least that part of the publication in their field of expertise;
2. they take public responsibility for their part of the publication, except for the responsible author who accepts overall responsibility for the publication;
3. there are no other authors according to these criteria; 4. potential conflicts of interest have been disclosed to (a) granting bodies,
(b) the editor or publisher of journals and their publications, and (c) the head of the responsible academic unit, and
5. they agree to the use of the publication in the student’s thesis and its publication on the Australasian Digital Thesis database consistent with any limitations set by publisher requirements.
In the case of this chapter: Propagation of converging low-intensity Gaussian fields in photorefractive media with real and imaginary intensity-dependent refractive index components M. W. Jones, E. Jaatinen, G. W. Michael, Applied Physics B. doi: 10.1007/s00340-010-4309-y
Contributor Statement of contribution*
Michael W. Jones
Signature
Date
Undertook experiments, conducted analysis (experimental
and numerical), paper writing, data analysis, discussion
Esa Jaatinen Conducted analysis (numerical and analytical), discussion,
paper writing
Greg W. Michael Data analysis
Principal Supervisor Confirmation
I have sighted email or other correspondence from all Co-authors confirming their
certifying authorship
______________________ _____________________________ ____________
Name Signature Date
79
Appl Phys BDOI 10.1007/s00340-010-4309-y
Propagation of low-intensity Gaussian fields in photorefractivemedia with real and imaginary intensity-dependent refractiveindex components
M.W. Jones · E. Jaatinen · G.W. Michael
Received: 23 June 2010 / Revised version: 11 October 2010© Springer-Verlag 2010
Abstract A theoretical analysis of a low power Gaussianfield propagating in unbiased self-defocussing photorefrac-tive media that includes both real and imaginary componentsof the intensity-dependent refractive index is presented. Theanalysis, which is in excellent agreement with experimen-tal observations, shows that the imaginary component of theintensity-dependent refractive index can have a focussing ef-fect independent of the focussing or defocussing effect ofthe real component of the intensity-dependent refractive in-dex. These findings suggest that the imaginary componentof the intensity-dependent refractive index is the cause ofthe previously observed apparent self-focussing in unbiasedself-defocussing photorefractive media.
6. Soliton-like interactions of bright, low power, low-
divergence Gaussian fields in unbiased self-
defocusing photorefractive BaTiO3 crystal
Michael W. Jones1, Esa Jaatinen1, G. W. Michael
1School of Physical and Chemical Sciences, Queensland University of Technology, 2
George Street, Brisbane QLD 4000, Australia
Published in: Optical Engineering 50, 019701-1 (2011)
Corresponding Author
Michael W. Jones
School of Physical and Chemical Sciences
Queensland University of Technology
2 George Street
Brisbane QLD 4000, Australia
Fax: +61 7 3138 9079
Email: mw.jones@qut.edu.au
Keywords: Photorefractive optics, spatial solitons
87
The authors listed below have certified* that; 1. they meet criteria for authorship in that they have participated in the
conception, execution, or interpretation, of at least that part of the publication in their field of expertise;
2. they take public responsibility for their part of the publication, except for the responsible author who accepts overall responsibility for the publication;
3. there are no other authors according to these criteria; 4. potential conflicts of interest have been disclosed to (a) granting bodies, (b)
the editor or publisher of journals and their publications, and (c) the head of the responsible academic unit, and
5. they agree to the use of the publication in the student’s thesis and its publication on the Australasian Digital Thesis database consistent with any limitations set by publisher requirements.
In the case of this chapter: Soliton-like interactions of bright, low power, low-divergence Gaussian fields in unbiased self-defocusing photorefractive BaTiO3 crystal M. W. Jones, E. Jaatinen, G. W. Michael, Optical Engineering 50, 019071-1 (2001)
Contributor Statement of contribution*
Michael W. Jones
Signature
Date
Original idea, undertook experiments, conducted analysis
(experimental and numerical), paper writing, data analysis,
discussion
Esa Jaatinen Conducted numerical analysis, discussion, paper writing
Greg W. Michael Data analysis
Principal Supervisor Confirmation
I have sighted email or other correspondence from all Co-authors confirming their
certifying authorship
______________________ _____________________________ ____________
Name Signature Date
88
C O M M U N I C A T I O N S
Soliton-like interactions of bright,low-power, low-divergenceGaussian fields in an unbiasedself-defocusing photorefractiveBaTiO3 crystal
Michael W. JonesEsa JaatinenGreg W. MichaelQueensland University of TechnologyFaculty of Science and TechnologyApplied Optics and Nanotechnology2 George StreetBrisbane, 4000, AustraliaE-mail: mw.jones@qut.edu.au
Abstract. The soliton-like interactions of two low divergencefields propagating in unbiased self-defocusing photorefractivemedia are examined. The interactions appear to be a resultof factors that are not dissimilar to those between two steadystate screening solitons. Analysis of the conditions for theinteractions show a cutoff for the degree of beam divergencerequired for the soliton-like interactions to occur. The analysisalso indicates that the strength of the interaction increases asthe beam divergence decreases. C!2011 Society of Photo-OpticalInstrumentation Engineers (SPIE). [DOI: 10.1117/1.3526683]
Subject terms: self-defocusing photorefractive media; unbiased pho-torefractive media; low divergence interactions.
Paper 100538CR received Jun. 29, 2010; revised manuscript re-ceived Nov. 2, 2010; accepted for publication Nov. 10, 2011; pub-lished online Jan. 13, 2011.
1 IntroductionOne of the key motivations for the study of photorefractive(PR) optical spatial solitons lies in the properties of their in-teractions, which allow for the creation of all optical switches.Two main types of steady state PR spatial solitons exist: PRscreening solitons and PR photovoltaic soliton. The formerrequires a large external biasing electric field on the orderof kilovolts, whereas the latter is formed due to the photo-voltaic space-charge field and is dependent on the intensityof the incident light. Bright PR screening solitons and theirinteractions are well known, having been studied intensivelyfor a number of years.1–5 Bright photovoltaic PR spatial soli-tons however are a more recent observation, having beenformed in both self-focusing6 and in self-defocusing PR me-dia with the aid of a high-powered background beam in bothcases.7 Interactions of these types of PR spatial solitons havealso been investigated and found to behave similarly to PRscreening solitons.5 However, the requirement of an exter-nal biasing field in the form of either an external electrical
0091-3286/2011/$25.00 C! 2011 SPIE
field or high-power background illumination “is the hurdlefor realisation of applications” (see p. 1923 of Ref. 5). In astep toward overcoming this hurdle, the recent observation offocusing in unbiased self-defocusing PR crystals8, 9 has leadto the prediction of the formation of bright, low-divergencephotovoltaic soliton-like fields in self-defocusing PR mediawithout an external field or background illumination.10 Inthis approach, the real and imaginary components of the re-fractive index required for the formation of these fields is10
n2R = n0
I0
!1
k2w2 (z)! w2 (z)
4R2 (z)
", (1)
n2I = n0
I0k R (z), (2)
where n0 is equal to the background refractive index, I0 isequal to the incident beam intensity, k is the modulus ofthe wave vector, and w(z) and R(z) represent the beam ra-dius and wavefront curvature at a distance z from the beamwaist w0. However, in order to be applicable for use asall optical switches, these low-divergence soliton-like fieldsmust be capable of interactions. Therefore, this letter seeksto experimentally determine if two low-divergence soliton-like fields created from initially converging beams in unbi-ased self-defocusing Ce:BaTiO3 are capable of soliton-likeinteractions.
2 MethodTwo beams, ! = 532 nm, propagating with a relative angleof 2" = 0.2 deg and radius at the beam waist, w0 = 30 µm,were created from reflections off the front and back faces ofa thin wedge. Under this arrangement, the beam waists ofeach beam were at approximately the same z distance, andthe two beams intersected "10 cm before the beam waists.The PR Ce:BaTiO3 crystal with 50 ppm cerium concentrationwas translated in a z-scan arrangement at distances betweenthe intersection point of the two beams and the Rayleighlength, zR = 5.3 mm, with the optical c-axis perpendicularto the direction of translation. Therefore, within the crystal,the beams were diverging from each other at an angle of0.2 deg, while each individual beam was converging, as canbe seen in Fig. 1. The beam power for each beam was set inturn to 0.8, 1.0, and 1.3 mW per beam.
After the beams had propagated through the PR crystal,images of the far field were taken where the Gaussian beamscan be approximated as plane waves. Because the divergenceof each individual beam was greater than the angle betweenthem, the beams were superimposed in the far field, resultingin an interference pattern. The spatial intensity profile of theinterference pattern formed by the two beams in the far fieldis described by
I = 4I0 cos2 [k sin (" )] , (3)
where I0 is the intensity of each beam, k is the modulus of thewave vector of each beam, and " is the half angle betweenthe two beams (i.e., the beams intersect at an angle of 2" ).
Optical Engineering January 2011/Vol. 50(1)019701-1
89
COMMUNICATIONS
Fig. 1 Experimental setup showing the width of the two beams(shaded area) as they intersect. The solid lines within the shadedarea represents beam axis of each beam and inset (a) represents atypical far field profile recorded from the CCD camera.
Therefore, in air the period of maxima in the interferencepattern is equal to
! = "
2 sin #. (4)
Intensity profiles of the far-field interference pattern wereleast squares fitted to Eq. (3). From this, the period of themaxima [given by Eq. (4)] and therefore the angle that thetwo beams intersected the plane of the CCD array, # , wasdetermined.
3 Results and DiscussionA change in the angle that the beam exits the PR crystal forsome positions under a z-scan would indicate that the twobeams are interacting under those specific incident-beam pa-rameters. Figure 2 shows the angle that the beams exit thecrystal increases by 3–5% for a narrow range of incidentbeam areas, with the position of the interaction occurringover a similar range of incident beam areas for each of thetwo cases. The maximum relative increase in the exit angleof between the two beams was 5% for the 1.0 mW case and4% for the 1.3 mW case. No interaction was evident for thecase of two 0.8-mW beams, and the results are therefore notpresented. These results suggest that the two beams interact,with a resulting divergence between the two beams. This in-dicates that the two low-divergence fields are repelled fromeach other. In terms of bright-soliton interactions, this resultcan be interpreted as the refractive index between the twobeams decreases (self-defocusing PR media) and the beamsare steered away from this area. The interactions in Fig. 2 areobserved when the required changes in the real and imagi-nary parts of the refractive index are between –9.6!10" 6 <n2R < –1.5!10" 5 and –3.4!10" 11 < n2I < –4.7!10" 11,respectively, as given by Eqs. (1) and (2). Although this rangeof values for the change in the real part of the refractive indexis typical for this material at this wavelength and intensity,Ce:BaTiO3 has a positive change in the imaginary part of therefractive index at this wavelength11, 12 and thus will resultin a beam with divergence greater than the ideal case, wherebeam divergence is equal to zero.10
Numerical simulations of the divergence of each beamwere undertaken and found that at a power of 1.0 mW perbeam, the beam diverges by 1.77% over the length of the
Fig. 2 Results for the relative change in exit angle between the twobeam as a function of the incident beam area for individual beampowers of (a) 1.0 mW and (b) 1.3 mW. The solid line in each caserepresents a relative change equal to 1.0 (i.e., no change).
medium in the area that the interactions were observed. Forthe beams at 1.3 mW each, the beam divergence is predictedat 1.84%. Figures 2(a) and 2(b) show that at the higher beampower, the beam interaction is weaker, and this could be dueto the greater divergence of the beam. For beams at 0.8 mWeach, numerical simulations predict that the beam divergesby 1.96% over the length of the medium. For comparison,in a homogeneous medium, the same beam will diverge by#17% over the same length. Table 1 shows the beam powers,theoretical divergences, and whether or not an interaction wasobserved. From Table 1, it is clear that under these circum-stances, beam divergence must be <1.96% over the lengthof the medium (5 mm) in order for a soliton-like interac-tion to occur. The relatively small change in the interactionstrength between the two case where soliton-like interactionsoccurs suggest there must be a beam divergence limit for theobservation of soliton-like interactions.
Table 1 Beam powers, theoretical divergences, and interactions forthe three cases, ordered by beam divergence.
Beam power (mW) Theoretical divergence (%) Interaction (%)
1.0 1.77 5
1.3 1.84 4
0.8 1.96 0*
*No change in the relative exit angle between the two beams wasevident.
Optical Engineering January 2011/Vol. 50(1)019701-2
90
COMMUNICATIONS
4 ConclusionThese results show that soliton-like collisions are possible forlow power Gaussian beams propagating with low divergence.The divergence cutoff for the interaction has been found tobe between 1.84 and 1.96%, which is far greater that the idealcase of divergence outlined in the literature.10 This suggeststhat, although the interactions observed were weak, strongerinteraction should be possible for beams propagating withdivergence closer to the ideal theoretical value.
References1. A. Keshavarz and Z. Khalifeh, “One-dimensional optical bright screen-
ing photovoltaic photorefractive solitons, soliton pairs and incoher-ent interaction between them in BaTiO3 crystal,” Optik 120, 535–542(2009).
2. G. S. Garcia-Quirino, M. D. Iturbe Casitillo, V. A. Vysloukh,J. J. Sanchez-Mondragon, S. I. Stepanov, G. Lugo-Martinez, andG. E. Torres-Cisneros, “Observation of interaction forces between one-dimensional spatial solitons in photorefractive crystals,” Opt. Lett. 22,154–156 (1997).
3. H. X. Meng, G. Salamo, M. Shih, and M. Segev, “Coherent collisonsof photorefractive solitons,” Opt. Lett. 22, 448–450 (1997).
4. J. A. Andrade-Lucio, B. Alvarado-Mendez, R. Rojas-Laguna, O. G.Ibarra-Manzano, G. E. Torres-Cisneros, R. Jaime-Rivas, and E. A.Kuzin, “Optical switching by coherent collison of spatial solitons,”Electron. Lett. 36, 1403–1405 (2000).
5. W. K. Lee and T. S. Chan, “Experimental investigation of phase depen-dent interactions of photovoltaic bright spatial solitons in photorefrac-tive Fe:LiNbO3,” J. Opt. Soc. Am. B 23, 1920–1924 (2006).
6. W. L. She, K. K. Lee, and W. K. Lee, “Observation of two-dimensionalbright photovoltaic spatial solitons,” Phys. Rev. Lett. 83, 3182–3185(1999).
7. W. L. She, C. C. Xu, B. Guo, and W. K. Lee, “Formation of photovoltaicbright spatial soliton in photorefractive LiNbO3 crystal by a defocusedlaser beam induced by a background laser beam,” J. Opt. Soc. Am. B23, 2121–2126 (2006).
8. A. Rausch, A. Kiessling, and R. Kowarschik, “Self-focusing withoutexternal electric field in BaTiO3,” Opt. Express 14, 6207–6212 (2006).
9. M. W. Jones, E. Jaatinen, and G. Michael, “Propagation of low in-tensity Gaussian fields in photorefractive media with real and imagi-nary intensity-dependent refractive index components,” Appl. Phys. B(2010).
10. E. Jaatinen and M. W. Jones, “Thoeretical model of non-divergingGaussian beam propagation in self-defocusing photorefractive media,”Opt. Commun. 281, 3201–3207 (2008).
11. M. W. Jones and E. Jaatinen, “Transition from intensity dependentabsorption to transperancy in Ce:BaTiO3,” Opt. Mater. 31, 122–125(2008).
12. C. Yang, Y. Zhang, X. Yi, P. Yeh, Y. Zhu, M. Hui, and X. Wu, “Intensity-dependent absorption and photorefractive properties in cerium-dopedBaTiO3 crystals,” J. Appl. Phys. 78, 4323–4330 (1995).
Optical Engineering January 2011/Vol. 50(1)019701-3
91
7. Conclusion
This PhD thesis studied the propagation of low-power Gaussian fields in unbiased
self-defocusing photorefractive media with low spatial divergence. The main goals
were to theoretically investigate and experimentally verify the existence of these
fields, and to produce soliton-like interactions between two such fields. This research
is important for the application of rewritable all optical interconnects in nonlinear
media, where current alternatives require large applied voltages or high power
background illumination, thus making them unsuitable for replacing existing
electrical circuitry. This research outlines a case where this additional voltage or
background illumination is not required, opening up the possibility to create
rewritable optical circuitry.
To realise these aims, a variety of methods were utilised. Far field images
were used to determine the evolution of the complex beam parameter, q, of the
Gaussian beam after it had passed through the PR medium. By comparing the
complex beam parameter before and after the beam had propagated through the
medium, the effect that the medium had on the beam was determined. By translating
the PR medium in a z-scan arrangement the beam is incident on the medium with a
different complex beam parameter without altering the optical power of the beam.
Numerical wavefront studies were coupled with experimental observations to gain an
understanding of the evolution of the beam within the PR medium. A combination of
these techniques allowed a complete picture of the evolution of a low powered
Gaussian beam as it propagates through PR media.
In Chapter 3, an analytical model was developed for the conditions required
in order for a low power Gaussian beam to propagate in self-defocusing PR media
92
with low divergence. This approach relies on the finding that at low powers, a
Gaussian beam propagating in PR media maintains its Gaussian spatial profile. This
result allows the refractive index profile to be treated as a quadratic function from the
beam axis, allowing simple solutions to the wave equation. Numerical analysis of
this model showed that under ideal conditions, a Gaussian beam could propagate in
unbiased self-defocusing PR media with a divergence of approximately 0.2 % after 1
m. However, these ideal conditions require a PR medium that is self-defocusing,
whilst also displaying intensity dependent transparency.
In Chapter 4, the wavelength dependence of the intensity dependent
absorption of a Ce:BaTiO3 crystal was examined to determine if the ideal conditions
for low divergence fields outlined in Chapter 3 were physically realisable. It was
found that as the wavelength of the incident light increase, the intensity dependent
absorption decreases, with intensity dependent transparency observed at an incident
wavelength of 790 nm. Theoretical fits to the data obtained revealed that it was the
shallow traps in the two centre model that were responsible for the wavelength
dependence of the intensity dependent absorption of the Ce:BaTiO3 crystal.
Chapter 5 outlined a theoretical approach to the evolution of the complex
beam parameter in PR media with a quadratic beam parameter. Unlike the model
discussed in Chapter 3, this model allowed for the change in the real and imaginary
parts of the refractive index to be functions of the propagation distance through the
medium. A numerical wavefront study of this model was applied to several
scenarios. Of particular interest was the apparent self-focusing, and the propagation
of low divergence Gaussian beams in unbiased self-defocusing PR media. With
respect to low divergent Gaussian fields, the study showed that under the ideal
conditions, the divergence of the beam will be less that 0.003 % over a 5 mm long
93
crystal. In addition, in a self-defocusing PR medium that displays intensity
dependent absorption, the divergence will be less than 0.02 %. These results suggest
that it is possible to create a low divergence field in Ce:BaTiO3 at an incident
wavelength of 532 nm, where the medium is self-defocusing and displays intensity
dependent absorption.
Spatial optical solitons interact with each other when the interaction angle is
small. Although the interaction that occurs is dependent on a variety of factors, a
repulsive interaction of this type suggests that the field is propagating in a way that is
analogous to a spatial soliton. Therefore, Chapter 6 aimed to determine if two low
divergence fields with a wavelength of 532 nm could interact in a Ce:BaTiO3 crystal.
The results showed that although far from the ideal low divergence being realised, a
weak interaction was observed. In addition, the strength of the interaction increased
as the divergence decreased, indicating that stronger interactions should be possible
with lower divergence fields. To be of practical use, these interactions would have to
occur at an angle greater than the divergence angle to ensure the two beams could be
separated downstream.
This research outlined the possibility that low power, low divergence
Gaussian fields could propagate in unbiased self-defocusing PR media. Further to
that, this research illustrated that although these fields are not perfect spatial solitons,
i.e., they still diverge to a degree, they are capable of spatial soliton-like interactions.
In this respect, several questions are left unanswered;
1. Is it possible to achieve an interaction with sufficient strength to enable
complete separation of the exit beams?
2. Are the low divergent fields described capable of guiding a second beam at a
second wavelength?
94
3. As with spatial soliton interactions, are the interactions of two of these fields
capable of manipulation? For example, can two repulsive beams be attracted
as a result of a relative phase shift between the two beams?
4. Could a guided beam be guided through an interaction, making a true all
optical interconnect?
The answers to these questions will reveal the feasibility of low power, low divergent
Gaussian fields in quadratic nonlinear media as all optical interconnects, replacing
electronic circuitry.
95
References
1. Y. Kivshar, "Spatial solitons: Bending light at will," Nat. Phys. 2, 729-730
(2006).
2. A. W. Snyder and F. Ladouceur, "Light guiding light: Letting light be the
master of its own destiny," Optics & Photonics News 10, 35-36 (1999).
3. M. Segev, "Optical spatial solitons," Opt. Quantum Electron. 30, 503-533
(1998).
4. L. B. Kish, "End of Moore's law: Thermal (noise) death of integration in
micro and nano electronics," Physics Letters A 305, 144-149 (2002).
5. M. Tokushima, H. Yamada, and Y. Arakawa, "1.5-µm-wavelength light
guiding in waveguides in square-lattice-of-rod photonic crystal slab," Applied
Physics Letters 84, 4298-4300 (2004).
6. L. Risch, "The end of the CMOS roadmap - new landscape beyond,"
Materials Science and Engineering C` 19, 363-368 (2002).
7. G. Stegeman and M. Segev, "Optical spatial solitons and their interactions:
Universality and diversity," Science 286, 1518-1523 (1999).
8. M. Segev and G. Stegeman, "Self-trapping of optical beams: Spatial
solitons," Physics Today 51, 42-48 (1998).
9. J. T. Verdeyen, Laser Electronics, 3rd ed. (Prentice Hall, New Jersey, 1995).
10. M. Segev, B. Crosignani, A. Yariv, and B. Fischer, "Spatial Solitons in
Photorefractive Media," Physical Review Letters 68, 923-926 (1992).
11. W. Krolikowski, B. Luther-Davies, and C. Denz, "Photorefractive solitons,"
IEEE Journal of Quantum Electronics 39, 3-12 (2003).
96
12. M. Segev, G. C. Valley, M. C. Bashaw, M. Taya, and M. M. Fejer,
"Photovoltaic spatial solitons," Journal of the Optical Society of America B.
14, 1772-1781 (1997).
13. A. Rausch, A. Kiessling, and R. Kowarschik, "Self-focusing without external
electric field in BaTiO3," Optics Express 14, 6207-6212 (2006).
14. R. L. Sutherland, Handbook of Nonlinear Optics, 2 ed. (Marcel Dekker, New
York, 2003).
15. J. Y. Chang, M. H. Garrett, H. P. Jenssen, and C. Warde, "Intensity-
dependent photorefractive properties in an n-type BaTiO3," Journal of
Applied Physics 75, 43-48 (1994).
16. G. A. Brost, R. A. Motes, and J. R. Rotge, "Intensity-dependent absorption
and photorefractive effects in barium titanate," Journal of the Optical Society
of America B. 5, 1879-1885 (1988).
17. G. S. Garcia-Quirino, M. D. Iturbe Casitillo, V. A. Vysloukh, J. J. Sanchez-
Mondragon, S. I. Stepanov, G. Lugo-Martinez, and G. E. Torres-Cisneros,
"Observation of interaction forces between one-dimensional spatial solitons
in photorefractive crystals," Optics Letters 22, 154-156 (1997).
18. A. Yariv, Quantum Electronics, 3rd ed. (Wiley, New York, 1989).
19. F. S. Chen, "A laser-induced inhomogeneity of refractive indicies in KTN,"
Journal of Applied Physics 38, 3418-3420 (1967).
20. F. S. Chen, "Optically induced change of refractive indices in LINbO3 and
LiTaO3," Journal of Applied Physics 40, 3389-3396 (1969).
21. A. M. Glass, "The photorefractive effect," Optical Engineering 17, 470-479
(1978).
97
22. D. A. Temple, R. S. Hathcock, and C. Warde, "Intensity dependent
photorefractive properties of BaTiO3," Journal of Applied Physics 67, 6667-
6670 (1990).
23. H. Song, S. X. Dou, and P. Ye, "Origin of the wavelength-dependence of
efective trap density in photorefract BaTiO3:Ce," Journal of Applied Physics
88, 6981-6986 (2000).
24. S. X. Dou, J. Kim, S. Yi, J. Yi, S. Cha, S. H. Shin, Y. Zhu, and P. Ye,
"Determination of wavelength dependence of the effective charge carrier
density of photorefractive crystals," Optics Communications 163, 212-216
(1999).
25. P. Tayebati and D. Mahgerefteh, "Theory of the photorefractive effect for
Bi12SiO20 and BaTiO3 with shallow traps," Journal of the Optical Society of
America B. 8, 1053-1064 (1991).
26. M. Chi, S. X. Dou, and P. Ye, "Wavelength dependence of the effective trap
density in Rh-doped BaTiO3: a comparison between theory and experiment,"
Optics Communications 170, 115-120 (1999).
27. A. Motes and J. J. Kim, "Beam coupling in photorefractive BaTiO3 crystals,"
Optics Letters 12, 199-201 (1987).
28. H. Song, S. X. Dou, M. Chi, H. Gao, Y. Zhu, and P. Ye, "Studies of shallow
levels in undoped and rhodium-doped barium titanate," Journal of the Optical
Society of America B. 15, 1329-1334 (1998).
29. G. Stegeman, D. N. Christodoulides, and M. Segev, "Optical spatial solitons:
Historical perspectives," IEEE Journal on Selected Topics in Quantum
Electronics 6, 1419-1427 (2000).
98
30. S. Lan, M. Shih, and M. Sergev, "Self-trapping of one-dimensional and two
dimensional optical beams and induced waveguides in photorefractive
KNbO3," Optics Letters 22, 1467-1469 (1997).
31. M. Shih, Z. Chen, M. Mitchell, M. Segev, H. Lee, R. S. Feigelson, and J. P.
Wilde, "Waveguides induced by photorefractive screening solitons," Journal
of the Optical Society of America B. 14, 3091-3101 (1997).
32. W. Krolikowski and S. A. Holmstrom, "Fusion and birth of spatial solitons
upon collison," Optics Letters 22, 369-371 (1997).
33. J. Petter and C. Denz, "Guiding and dividing waves with photorefractive
solitons," Optics Communications 188, 55-61 (2001).
34. M. Taya, M. C. Bashaw, M. M. Fejer, M. Segev, and G. C. Valley, "Y
junctions arising from dark-soliton propagation in photovoltaic media,"
Optics Letters 21, 943-945 (1996).
35. D. J. Griffiths, Introduction to electrodynamics, 3rd ed. (Prentice-Hall
International, New Jersey, 1999).
36. A. Ashkin, G. Boyd, J. Driedzic, R. Smith, A. Ballman, J. Levinstein, and K.
Nassau, "Optically-induced refractive index inhomogeneities in LiNb)3 and
LiTaO3," Applied Physics Letters 9, 72-74 (1966).
37. F. S. Chen, J. T. LaMacchia, and D. B. Fraser, "Holographic storage in
Lithiun Niobate," Applied Physics Letters 13, 223-225 (1968).
38. J. Feinberg, "Asymmetric self-defocusing of an optical beam from the
photorefractive effect," Journal of the Optical Society of America 72, 46-51
(1982).
99
39. K. Buse, "Light-induced charge transport processes in photorefractive
crystals I: Models and experimental methods," Applied Physics B 64, 273-
291 (1997).
40. S. H. Wemple, "Electro-optic materials," in Laser Handbook, F. T. Arecchi
and E. O. Schulz-Dubois, eds. (North-Holland Publishing, Amsterdam,
1972).
41. G. C. Valley and M. B. Klein, "Optimal properties of photorefractive
materials for optical data processing," Optical Engineering 22, 704-711
(1983).
42. G. C. Valley, "Short-pulse grating formation in photorefractive materials,"
IEEE Journal of Quantum Electronics QE-19, 1637-1645 (1983).
43. J. J. Amodei, "Analysis of transport processes during holographic recording
in insulators," RCA Review 32, 185-198 (1971).
44. V. L. Vinetskii and N. V. Kukhtarev, "Theory of the conductivity induced by
recording holographic gratings in non-metallic crystals," Soviet Physics Solid
State 16, 2414-2415 (1975).
45. N. Huot, J. M. C. Jonathan, G. Pauliat, D. Rytz, and G. Roosen,
"Characterization of a photorefractive rhodium doped barium titanate at
1.06um," Optics Communications 135, 133-137 (1997).
46. G. C. Valley, "Erase rates in photorefractive materials with two photoactive
species," Applied Optics 22, 3160-3164 (1983).
47. M. B. Klein and G. C. Valley, "Beam coupling in BaTiO3 at 442nm," Journal
of Applied Physics 57, 4901-4905 (1985).
100
48. M. Esselbach, G. Cedilnik, A. Kiessling, and R. Kowarschik, "Dependence of
the refractive index grating in photorefractive barium titanate on intensity,"
Optical Materials 14, 351-354 (2000).
49. Z. Hong, M. Zhang, H. Zheng, and J. Chen, "Dark decay behaviors of
photorefractive gratings in self-pumped phase conjugation with Ce:BaTiO3 at
532nm and 790nm wavelengths," Optics Communications 238, 157-262
(2004).
50. R. Orlowski and E. Kratzig, "Holographic method for the determination of
photo-induced electron and hole transport in electro-optic crystals," Solid
State Communications 27, 1351-1354 (1978).
51. F. P. Strohkendl, J. M. C. Jonathan, and R. W. Hellwarth, "Hole-electron
competition in photorefractive gratings," Optics Letters 11, 312-314 (1986).
52. G. C. Valley, "Simultaneous electron/hole transport in photorefractive
materials," Journal of Applied Physics 59, 3363-3366 (1986).
53. M. C. Bashaw, T.-P. Ma, and C. Barker, "Comparison of single- and two-
species models of electron-hole transport in photorefractive media," Journal
of the Optical Society of America B. 9, 1666-1672 (1992).
54. A. Motes and J. J. Kim, "Intensity-dependent absorption coefficient in
photrefractive BaTiO3 crystals," Journal of the Optical Society of America B.
4, 1379-1381 (1987).
55. A. Rose, Concepts in Photoconductivity and Allied Problems (Interscience,
New York, 1963).
56. J. K. Tyminiski and R. C. Powell, "Analysis of the decay dynamics of laser-
induced gratings in LiNbO3," Journal of the Optical Society of America B. 2,
440-446 (1985).
101
57. F. P. Strohkendl, "Light-induced dark decays of photorefractive gratings and
their observations in Bi12SiO20," Journal of Applied Physics 65, 3773-3780
(1989).
58. I. Biaggio, M. Zgonik, and P. Gunter, "Build-up and dark decay of transient
photorefractive gratings in reduced KNbO3," Optics Communications 77,
312-317 (1990).
59. R. S. Cudney, R. M. Pierce, G. D. Bacher, and J. Feinberg, "Absorption
gratings in photorefractive crystals with multiple levels," Journal of the
Optical Society of America B. 8, 1326-1332 (1991).
60. P. Delaye, L. A. de Montmorillon, I. Biaggio, J. C. Launay, and G. Roosen,
"Wavelength denpentent effective trap density in CdTe: evidence for the
presence of two photorefractive species," Optics Communications 134, 580-
590 (1997).
61. C. Yang, Y. Zhang, X. Yi, P. Yeh, Y. Zhu, M. Hui, and X. Wu, "Intensity-
dependent absorption and photorefractive properties in cerium-doped BaTiO3
crystals," Journal of Applied Physics 78, 4323-4330 (1995).
62. C. Yang, Y. Zhang, P. Yeh, Y. Zhu, and X. Wu, "Photorefractive properties
of Ce:BaTiO3 crystals," Optics Communications 113, 416-420 (1995).
63. A. Mazur, U. van Stevendaal, K. Buse, M. Weber, O. F. Schirmer, H. Hesse,
and E. Kratzig, "Light-induced charge transport processes in photorefractive
barium titanate crystals doped with iron," Applied Physics B 65, 481-487
(1997).
64. B. K. Kim, G. Y. Kang, J. K. Yoon, and J. H. Ro, "The photorefractive
effects of Fe and Fe + Ce doped LiTaO3 single crystal," Journal of Physics
and Chemistry of Solids 61, 637-646 (2000).
102
65. C. Yang, Y. Zhao, R. Wang, and M. Li, "Studies of photorefractive crystals
of double-doped Ce,Fe:LiNbO3," Optics Communications 175, 247-252
(2000).
66. A. Liu, M. Lee, L. Hesselink, S.-H. Lee, and K.-S. Lim, "Light-induced
absorption of cerium-doped lead barium niobate crystals," Optics Letters 23,
1618-1620 (1998).
67. J. Y. Chang, M. H. Garrett, H. P. Jenssen, and C. Warde, "Intensity
dependent absorption/transparency of a reducing BaTiO3," Applied Physics
Letters 63, 3598-3600 (1993).
68. H. Song, S. X. Dou, M. Chi, H. Gao, Y. Zhu, and P. Ye, "Light-induced
absorption and properties of shallow impurity levels in undoped and Ce-
doped BaTiO3," Journal of the Optical Society of America B. 15, 1850-1855
(1998).
69. X. Deng, Z. Cao, Q. Shen, and W. Yuan, "Measurement of electrically
induced change in complex refractive index of nonlinear polymer by
improved attenuated-total-reflection technique," IEEE Photonics Technology
Letters 15, 1755-1757 (2003).
70. J. A. Andrade-Lucio, M. D. Iturbe-Castillo, P. A. Marquez-Aguilar, and R.
Ramos-Garcia, "Self-focusing in photorefractive BaTiO3 crystal under
external DC electric field," Opt. Quantum Electron. 30, 829-834 (1998).
71. W. L. She, C. C. Xu, B. Guo, and W. K. Lee, "Formation of photovoltaic
bright spatial soliton in photorefractive LiNbO3 crystal by a defocused laser
beam induced by a background laser beam," Journal of the Optical Society of
America B. 23, 2121-2126 (2006).
103
72. C. Anastassiou, M. F. Shih, M. Mitchell, Z. G. Chen, and M. Segev,
"Optically induced photovoltaic self-defocusing-to-self-focusing transition,"
Optics Letters 23, 924-926 (1998).
73. H. Kogelnick and T. Li, "Laser beams and resonators," Applied Optics 5,
1550-1566 (1966).
74. W. J. Firth, "Propagation of laser beams through inhomogeneous media,"
Optics Communications 22, 226-230 (1977).
75. W. H. Carter, "Focal shift and concept of effective Frensel number for a
Gaussian laser beam," Applied Optics 21, 1989-1994 (1982).
76. Y. Li, "Propagation of focal shift through axisymmetrical optical systems,"
Optics Communications 95, 13-17 (1993).
77. S. A. Self, "Focusing of spherical Gaussian beams," Applied Optics 22, 658-
661 (1983).
78. S. Nemoto, "Waist shift of a Gaussian beam by a dielectric plate," Applied
Optics 28, 1643-1647 (1989).
79. S. Nemoto, "Waist shift of a Gaussian beam by plane dielectric interfaces,"
Applied Optics 27, 1833-1839 (1988).
80. S. R. Mallinson and G. Warnes, "Optimization of thick lenses for single-
mode optical-fiber microcomponents," Optics Letters 10, 238-240 (1985).
81. Y. Li, "Afocal drum lens as a beam-waist transformer," Applied Optics 33,
709-711 (1994).
82. E. Cojocaru, "Simple expressions for Gaussian-beam-waist parameters
imaged by a thick lens," Applied Optics 34, 2336-2338 (1995).
83. S. Nemoto, "Transformation of waist parameters of a Gaussian beam by a
thick lens," Applied Optics 29, 809-816 (1990).
104
84. K. Zhu, Y. Gao, and H. Tang, "Paraxial propagation of Gaussian beams
through curved tapered graded-index waveguides," Optics Communications
245, 203-210 (2005).
85. J. M. Nowosielski, R. Buczynski, F. Hudelist, A. J. Waddie, and M. R.
Taghizadeh, "Nanostructured GRIN microlenses for Gaussian beam
focusing," Optics Communications 283, 1938-1944 (2010).
86. J. Alda and G. D. Boreman, "On-axis and off-axis propagation of Gaussian
beams in gradient-index media," Applied Optics 29, 2944-2950 (1990).
87. J. Tsai, A. Chiou, T. Hsieh, and K. Hsu, "One-dimensional self-focusing in
photorefractive Bi12SiO20 crystal: theoretical modelling and experimental
demonstration," Optics Communications 162, 237-240 (1999).
88. V. Magni, G. Cerullo, and S. De Silvestri, "ABCD matrix analysis of
propagation of Gaussian beams through Kerr media," Optics
Communications 96, 348-355 (1993).
89. E. Koushki and A. Farzaneh, "Wavefront study in a Gaussian beam passed
through a nonlinear optical medium," Optics Communications 282, 3345-
3348 (2009).
90. B. Zhang, Q. Wen, and X. Gou, "Beam propagation factor of partially
coherent beams in gain or absorbing media," Optik 117, 123-127 (2006).
91. S. K. Agarwal and M. S. Sodha, "Steady-state self-focusing of Gaussian
electromagnetic beams in an inhomogeneous nonlinear medium: Effect of
absorption and initial curvature of the beam," Optik 118, 367-372 (2007).
92. H. Kogelnick, "On the propagation of Gaussian beams of light through
lenslike media including those with a loss or gain variation," Applied Optics
4, 1562-1569 (1965).
105
93. S. R. Singh and D. N. Christodoulides, "Evolution of spatial optical solitons
in biased photorefractive media under steady state conditions," Optics
Communications 118, 569-576 (1995).
94. M. Shih, M. Segev, G. C. Valley, G. Salamo, B. Crosignani, and P. Di Porto,
"Observation of two-dimensional steady-state photorefractive screening
solitons," Electronics Letters 31, 826-827 (1995).
95. M. Segev, G. C. Valley, B. Crosignani, P. Di Porto, and A. Yariv, "Steady-
state spatial screening solitons in photorefractive materials with an external
electric field," Physical Review Letters 73, 3211-3214 (1994).
96. D. N. Christodoulides and M. I. Carvalho, "Bright, Dark, and Gray Spatial
Soliton States in Photorefractive Media," Journal of the Optical Society of
America B. 12, 1628-1633 (1995).
97. W. L. She, C. W. Chan, and W. K. Lee, "Dark and bright photovoltaic spatial
solitons in photorefractive crystals with positive refractive-index
perturbation," Optics Letters 26, 1093-1095 (2001).
98. G. Q. Zhang, S. M. Liu, J. J. Xu, Q. Sun, and G. Y. Zhang, "Optical Dark and
Bright Spatial Solitons in Photorefractive Media," Physics Letters A 204,
146-150 (1995).
99. M. Segev, M. Shih, and G. C. Valley, "Photorefractive screening solitons of
high and low intensity," Journal of the Optical Society of America B. 13,
706-718 (1996).
100. B. Crosignani, M. Segev, D. Engin, P. Diporto, A. Yariv, and G. Salamo,
"Self-Trapping of Optical Beams in Photorefractive Media," Journal of the
Optical Society of America B. 10, 446-453 (1993).
106
101. G. C. Duree, J. L. Shultz, G. J. Salamo, M. Segev, A. Yariv, B. Crosignani, P.
Diporto, E. J. Sharp, and R. R. Neurgaonkar, "Observation of Self-Trapping
of an Optical Beam Due to the Photorefractive Effect," Physical Review
Letters 71, 533-536 (1993).
102. M. D. Iturbe Casitillo, P. A. Marquez Aguilar, J. J. Sanchez-Mondragon, S. I.
Stepanov, and V. A. Vysloukh, "Spatial solitons in photorefractive Bi12TiO20
with drift mechanism of nonlinearity," Applied Physics Letters 64, 408-410
(1994).
103. G. C. Valley, M. Segev, B. Crosignani, A. Yariv, M. M. Fejer, and M. C.
Bashaw, "Dark and Bright Photovoltaic Spatial Solitons," Physical Review A
50, R4457-R4460 (1994).
104. M. Taya, M. C. Bashaw, M. M. Fejer, M. Segev, and G. C. Valley,
"Observation of dark photovoltaic spatial solitons," Physical Review A 52,
3095-3100 (1995).
105. W. L. She, K. K. Lee, and W. K. Lee, "Observation of two-dimensional
bright photovoltaic spatial solitons," Physical Review Letters 83, 3182-3185
(1999).
106. M. Shih, M. Segev, and G. J. Salamo, "Circular waveguides induced by two-
dimensional bright steady-state photorefractive spatial screening solitons,"
Optics Letters 21, 931 (1996).
107. M. Asaro, M. Sheldon, Z. Chen, O. Ostroverkhova, and W. E. Moerner,
"Soliton-induced waveguides in an organic photorefractive glass," Optics
Letters 30, 519-521 (2005).
108. M. Morin, G. Duree, G. J. Salamo, and M. Segev, "Waveguides formed by
quasi-steady-state photorefractive solitons," Optics Letters 20, 2066 (1995).
107
109. E. Fazio, W. Ramadan, A. Petris, M. Chauvet, A. Bosco, V. I. Vlad, and M.
Bertolotti, "Writing single-mode waveguides in lithium niobate by ultra-low
intensity solitons," Applied Surface Science 248, 97-102 (2005).
110. M. D. Iturbe Casitillo, J. J. Sanchez-Mondragon, S. I. Stepanov, M. B. Klein,
and B. A. Wechsler, "(1+1)-Dimension dark spatial solitons in
photorefractive Bi12TiO20 crystal," Optics Communications 118, 515-519
(1995).
111. A. Petris, A. Bosco, V. I. Vlad, E. Fazio, and M. Bertolotti, "Laser induced
soliton waveguides in lithium niobate crystals for guiding femtosecond light
pulses," Journal of Optoelectronics and Advanced Materials 7, 2133-2140
(2005).
112. V. I. Vlad, E. Fazio, M. Bertolotti, A. Bosco, and A. Petris, "Laser generated
soliton waveguides in photorefractive crystals," Applied Surface Science 248,
484-491 (2005).
113. A. V. Mamaev, M. Saffman, and A. A. Zozula, "Phase-dependent collisons of
(2+1)-dimensional spatial solitons," Journal of the Optical Society of
America B. 15, 2079-2082 (1998).
114. J. A. Andrade-Lucio, B. Alvarado-Mendez, R. Rojas-Laguna, O. G. Ibarra-
Manzano, G. E. Torres-Cisneros, R. Jaime-Rivas, and E. A. Kuzin, "Optical
switching by coherent collison of spatial solitons," Electronics Letters 36,
1403-1405 (2000).
115. H. X. Meng, G. Salamo, M. Shih, and M. Segev, "Coherent collisons of
photorefractive solitons," Optics Letters 22, 448-450 (1997).
116. W. K. Lee and T. S. Chan, "Experimental investigation of phase dependent
interactions of photovoltaic bright spatial solitons in photorefractive
108
Fe:LiNbO3," Journal of the Optical Society of America B. 23, 1920-1924
(2006).
117. A. A. Dreischuh, D. Neshev, D. E. Peterson, O. Bang, and W. Krolikowski,
"Observation of attraction between dark solitons," Physical Review Letters
96, 0439011-0439014 (2006).
118. A. Keshavarz and Z. Khalifeh, "One-dimensional optical bright screening
photovoltaic photorefractive solitons, soliton pairs and incoherent interaction
between them in BaTiO3 crystal," Optik 120, 535-542 (2009).
119. W. Krolikowski, C. Denz, A. Stepken, M. Saffman, and B. Luther-Davies,
"Interaction of spatial photorefractive solitons," Quantum and Semiclassical
Optics 10, 823-837 (1998).
120. L. Jinsong and L. Keqing, "Screening-photovoltaic spatial solitons in biased
photovoltaic-photorefractive crystals and their self-deflection," Journal of the
Optical Society of America B. 16, 550-555 (1999).
121. J. Petter, C. Weilnau, C. Denz, A. Stepken, and F. Kaiser, "Self-bending of
photorefractive solitons," Optics Communications 170, 291-297 (1999).
122. P. A. Marquez Aguilar, J. J. Sanchez-Mondragon, S. I. Stepanov, and G.
Bloch, "Z-scan experiments with cubic photorefractive crystal Bi12TiO20,"
Optics Communications 118, 165-174 (1995).
123. S. Bian and J. Frejlich, "Z-scan measurements of photorefractive
nonlinearities for a SBN:Ce crystal," Applied Physics B 64, 539-546 (1997).
124. W.-P. Zang, J.-G. Tian, Z.-B. Liu, W.-Y. Zhou, C.-P. Zhang, and G.-Y.
Zhang, "Variational analysis of z scan of thick medium with an elliptic
Gaussian beam," Applied Optics 42, 2219-2225 (2003).