Research note
Processing induced material interactions determining thereliability of LTCC multichip modules
Ga bor Harsa nyi
Department of Electronics Technology, Technical University of Budapest, Budapest H-1521, Hungary
Received 13 July 1999
Abstract
Metals can exhibit dendritic short-circuit growth caused by electrochemical migration in conductor±insulatorstructures, which may result in failures and reliability problems in microcircuits. The classical model of
electrochemical migration has been well known for several decades. This process is a transport of metal ionsbetween two metallization stripes under bias through a continuous aqueous electrolyte. Due to the electrochemicaldeposition at the cathode, dendrites and dendrite-like deposits are formed. Ultimately, such a deposit can lead to a
short circuit in the device and can cause catastrophic failure. Recent investigations have demonstrated that not onlymetallic components, but also oxides from the isolating layers can take part in the formation of migrated shorts,after a chemical reduction process. Material design aspects need to clarify the correlation between material
composition, processing, chemical bonding state, and electrochemical migration failure rate in isolating compounds:this is the scope of the present study. # 2000 Elsevier Science Ltd. All rights reserved.
1. Introduction
Recently, in connection with the production of high-
density interconnection systems in integrated circuitsand multichip modules (MCMs), the claim to conduc-tor-systems with very high resolution and high re-
liability has emerged. There is also a great demand onintegrating embedded passive components (includingmultilayer capacitors) into the interconnection sub-
strate. The possibilities of integration are determinednot only by the technological bases but also by thosephysical and chemical processes that can cause resistiveshorts between adjacent metallization stripes or layers
during the operation. One of these phenomena is theelectrochemical migration. This can be de®ned as atransport of ions between two metallization stripes or
layers under bias through an aqueous electrolyte. Elec-
trochemical deposition also occurs forming dendrites
or dendrite-like deposits. Ultimately, such a deposit
can lead to a short circuit in the device and can cause
catastrophic failure. The conditions are: a ®lm of polar
liquid (usually water) to form an electrolyte, bias, and
operating time [1].
Migrated resistive shorts occur randomly in practice
and mainly under extreme conditions. A device can op-
erate for many hundreds of hours under normal oper-
ating conditions, and then, after a short exposure to
special environmental conditions, fail [2,3].
The classical model of electrochemical migration has
been well known for four decades [4±6], however, sev-
eral anomalous phenomena have initiated to perform
some revisions and to add supplementary models to
the conventional one. A recent discovery in this ®eld
was that metal ions forming dendrites can originate
not only from the metallic but even from the isolating
Microelectronics Reliability 40 (2000) 339±345
0026-2714/00/$ - see front matter # 2000 Elsevier Science Ltd. All rights reserved.
PII: S0026-2714(99 )00207-3
www.elsevier.com/locate/microrel
E-mail address: harsanyi@ett.bme.hu (G. Harsa nyi).
Fig. 1. In situ X-ray di�raction analysis during heating (source CuKa): (a) Bi2O3/BaTiO3; (b) PbO/BaTiO3; (c) Fe2O3/BaTiO3; (d)
CuO/BaTiO3.
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345340
Fig. 1 (continued)
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345 341
compounds of the layers, assuming that these constitu-
ents can chemically be reduced [7]. In some cases, alsothe reduction site may run through the dielectric ®lmresulting dendrite-like conductive ®laments without
any ion formation and migration processes [8]. Thislatter phenomenon can be called ``virtual migration''.It has a much lower activation energy level than the
former ones because the real ionization and ionicmovement steps are avoided. The failure rates depend
on the reducibility that means the chemical bondingstate of the given compound. Material design aspectsneed to clarify the correlation between them.
In glass±ceramic based electronic components,packages, and interconnection systems, such as thick-
®lm hybrid circuits and low temperature co-®red cer-amic (LTCC) based multichip modules (MCMs), nu-merous composite (conducting and dielectric) materials
are applied containing various secondary constituentssuch as metal oxides for inorganic binder, dye andother purposes. Several types of these oxides can
chemically easily be reduced, for example by hydrogen,thus, they show the ability for metallic dendrite for-
mation. Till now, the materials having been found totake part in dendrite formation corresponding to thismodel are the oxides of copper, bismuth, lead and iron
[9]. Other materials may also show this ability. Mostdangerous are those oxides types that remain in thestate of oxides after the heat treatment (sintering, ®r-
ing) of the structures. Thus, at reactive type oxides,which take part in the physio±chemical reactions
during ®ring, the migration lifetime is determined bythe excess amount of metal-oxide. Lifetime data maybe improved by composition and technology changes.
At non-reactive type oxides, which do not take part inany reaction during ®ring, no improvement of lifetimedata can be expected by changing the composition and
the ®ring parameters.The models of various migration failure mechanisms
and evidences for the ``reduced oxide type'' as well as``virtual'' migration have been described in earlier stu-dies [7±12].
Thick-®lm and LTCC dielectrics for integrated ca-pacitor purposes are compound materials containing
not only a high permittivity ferroelectric powder, suchas BaTiO3 [13], but various secondary constituents asinorganic binders and dyes, respectively. Therefore,
special dielectric materials were produced for the ex-perimental purposes with controlled amounts of Bi2O3,PbO, CuO and Fe2O3 additives for achieving a better
understanding of failure mechanisms and for separ-ating the migration behavior of various oxide constitu-
ents. Originally, they have the following roles in thepastes. Bi2O3 is a common reactive binder componentin conductor pastes and ferroelectric paste or ``tape''
type materials. It provides a good adhesion due to theformation of various compounds during ®ring [14,15].
A similar behaviour is expected from PbO and CuO.On the other hand, Fe2O3 is used as a simple non-reac-
tive dye in these dielectric materials.The present work concentrates on the real chemical
state of critical compounds investigated by in-situ X-
ray di�ractometry during heat annealing. The objectiveis to study the processing induced chemical reactionsof those auxiliary oxide type additives that, after their
processing, are inclined to chemical reduction in moist-ure condensation induced electrochemical processesand subsequent metallic dendritic growth during device
operation. The reliability of the ready structures isdetermined by the chemical interactions during ®ring.The interaction of the additives with the functionaldielectrics, such as BaTiO3, has the greatest import-
ance, since the latter one is used as a ferroelectric com-pound in thick-®lm and embedded-LTCC-capacitordielectrics.
2. Reactivity of additive oxides
In order to get a better understanding of chemicalprocesses, in situ X-ray di�raction spectra have beenperformed during heat annealing on various powder
mixtures. The application of real thick-®lm pastes orLTCC compositions was not possible, because of theirrelatively low additive contents. Real printed thick-®lmsamples were also not suitable for the analysis because
the large X-ray peaks of alumina substrates disturb theevaluation of the spectra. Therefore, 1 : 1 molar ratiohigh-purity Bi2O3/BaTiO3, PbO/BaTiO3, Fe2O3/
BaTiO3 and CuO/BaTiO3 powder samples were pre-pared by mixing. The sample powder was pressed ontoa heated Pt element for making X-ray di�raction (XD)
spectra using a CuKa source. The XD spectra (madeby a Siemens D 500 di�ractometer) are shown in Fig.1. The most important results can be summarized as
follows:
1. In the case of Bi2O3/BaTiO3 powder (see: Fig. 1a),several strong chemical changes can be detected
when heated up from 650 to 8508C, up to the typi-cal thick-®lm ®ring temperature, X-ray peaks of sev-eral new compounds, such as: Bi12TiO20, andBaBi4Ti4O15 can be recognized.
2. In the case of PbO/BaTiO3 powder (see: Fig. 1b),chemical changes can be detected again at 7008C:the peaks of Pb2Ti2O6 can be recognized.
3. In the case of Fe2O3/BaTiO3 powder (see Fig. 1c),no reaction has been found under 9508C.
4. The situation is very similar with the CuO/
BaTiO3 powder mixture (see Fig. 1d): there is noreaction below 9508C.
Accordingly, Bi2O3 and PbO react inside the dielectrics
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345342
with the ferroelectric compound and they may disap-
pear from the ®lm if the temperature program is
appropriate for completing the chemical reaction. The
chemical reaction between Bi2O3 and BaTiO3 was
described already elsewhere [13], however, the postu-
lated compound (Ba2Bi4Ti5O18) was not the same that
has been detected here. On the other hand, no reaction
has occurred in Fe2O3/BaTiO3 and CuO/BaTiO3 mix-
tures, respectively, if applying a conventional thick-®lm
®ring cycle. Thus, any modi®cation of the ®ring par-
ameters can not alter the composition. These XD
analysis results con®rm some preliminary investi-
gations published elsewhere [16].
High temperature chemical reactions of the men-
tioned oxides with Al2O3 may also have an important
role in determining the ®nal composition. There is
enough information in the literature to have an im-
agination about these processes. Bi2O3 starts to form
new compounds with alumina above 6008C resulting
good adhesion between ®lm and substrate [15]. CuO
forms CuAlO2, typically starting at 9508C, but also hy-
pothesized to occur somewhat below this temperature
[17,18]. No reaction has been found in PbO/Al2O3 and
Fe2O3/Al2O3 mixtures [15,17].
3. Capacitor sample fabrication
Thick-®lm capacitors were chosen as model systems
for life test investigations. The samples were produced
by traditional thick-®lm technology using a non-mi-
grating Au conductor composition for electrode pur-
poses. The ®lms were printed onto 96% alumina
substrates using a 200-mesh stainless steel screen for
conductor layers, 160- and 200-mesh screens for the
two layers of the dielectrics, respectively. The ®lms
were dried at 1508C for 15 min and ®red in air within
a conventional belt furnace, at a standard 8508C pro-
®le, over a 60 min cycle time. The time at peak tem-
perature was approximately 10 min. The two printed
layers of the dielectric paste were co-®red, separately
from both conductor layers. The ®red thickness was
about 12±15 mm for the conductor and 50±60 mm for
the dielectric layers. The samples contained traditional
square shaped, 3.32 � 3.32 mm2 (130 mil sq) capacitor
structures.
The components of the pastes used in the exper-
iments were: BaTiO3, the main constituent of most ca-
pacitor dielectrics, a small amount of glass frit, Bi2O3,
PbO, Fe2O3, or CuO additives, respectively in various
concentrations, and organic vehicle.
4. Accelerated life tests
Thermal Humidity Bias (THB) testing was per-
formed on the thick-®lm capacitor samples for up to4000 h which meant an accelerated life test at 95%relative humidity (RH), under 10 V dc bias at the tem-
perature of 408C. The purpose of this experiment wasto estimate mean time to failure data of the sampleswith various materials and to ®nd a correlation
between their composition, processing, and migrationshort circuit failure formation ability. The empiricaltime dependency of the migration failure rates showedstatistically a close correlation with a log-normal distri-
bution, according to the expectations [5,11]. Thus,main time to failure data were estimated using leastsquare ®tting in a log-normal scale.
Fig. 2 shows main time to failure data as a functionof the metal-oxide content of the dielectrics. It isobvious that migration processes are strongly depen-
dent on the Bi2O3, CuO and PbO concentrations, butless in¯uenced by the Fe2O3 content.A similar behavior was found when examining the
in¯uence of the high temperature processing par-
ameters. Table 1 summarizes failure rate results after a1000 h THB test as a function of the ®ring pro®le:peak temperature and peak time. For Bi2O3, CuO and
Fig. 2. Thick-®lm capacitor lifetime values as a function of
the composition of the dielectrics (THB test performed at
95% RH, 408C, 10 V dc)
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345 343
PbO, the migration behavior can be improved byincreasing the peak temperature and time. On theother hand, changing these ®ring parameters can notin¯uence the migration behavior of Fe2O3.
From these results, considering also the XD analysisspectra, a general conclusion can be drawn:
. At reactive type oxides (e.g. at Bi2O3, CuO, and
PbO), which take part in the physio±chemical reac-tions during ®ring, the migration lifetime is deter-mined by the excess amount of metal-oxide
(remaining in the form of oxide after ®ring). Life-time data can be improved by composition and pro-cessing changes.
. At non-reactive type oxides (e.g. at Fe2O3), whichare not involved in any reaction during ®ring, life-time data can not be improved signi®cantly by chan-ging the composition and ®ring parameters,
respectively. The use of these oxide-types in practicalstructures should be avoided.
5. Conclusions
. Investigating short circuit failure processes causedby the electrochemical migration of reduced isolatingcompounds in thick-®lm capacitors, a strong in¯u-
ence of the composition and processing parametershas been found.
. In situ XD spectra during heat annealing indicate
that the determining factor is the availability andcompleteness of those chemical reactions, in whichthe critical, easily reducible compound may partici-
pate.. Thus, there are two types of metal-oxide constitu-
ents
Reactive type oxides, which take part in the phy-sio±chemical reactions during ®ring. The migrationlifetime is determined by the excess amount ofmetal-oxide (remaining in the form of oxide after ®r-
ing). Lifetime data can be improved by compositionand technology parameter changes (e.g. Bi2O3, CuO,and PbO).
Non-reactive type oxides do not take part in anyreaction during ®ring. Lifetime data can not beimproved by changing the composition and the ®r-
ing parameters. The use of this oxide-types in thepractical structures should be avoided (e.g. Fe2O3).
. A wide range of materials and processes should beinvestigated in the near future to understand their
behavior in this aspect to optimize compositions andprocessing parameters in order to improve the re-liability of the structures where they are used. For
example, the low decomposition energy experiencedat laser annealed AlN ceramics [19] suggests to in-vestigate the possibility of virtual migration on these
substrate types as well.
Acknowledgements
This work was supported by the Hungarian
National Scienti®c Research Fund, OTKA, projectNo. F007365, T030574 and in part by the EU foundedINCO-COPERNICUS project No. ERBIC 15C
960743. The X-ray di�raction investigations were per-formed at the Florida International University in theframe of the COBASE program (an NSF grant coordi-
nated by the National Research Council, USA). Theauthor greatly appreciates the help of Prof. W. KinzyJones and Liana Pernes in connection with this work.
Table 1
Failure rates of thick-®lm capacitors after THB test with various dielectrics and ®ring parameters
Oxide type Metal-oxide/ BaTiO3 ratio
(%)
Failure rates (%) (1000 h, 408C, 95% RH, 10 V dc)
Firing peak temperature (8C) / peak time (min)
800/5 800/10 850/5 850/10 900/5 900/10
Bi2O3 1 90210 80215 1022 0 0 0
0.5 50210 1525 0 0 0 0
PbO 3 100 9525 2024 0 0 0
6 100 100 100 9525 4025 0
CuO 6 9921 9822 3025 0 0 0
12 9921 9921 100 9921 60210 2023
Fe2O3 1.25 100 9822 100 100 9524 9822
0.6 80215 90210 80210 80215 90210 90210
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345344
References
[1] Kohman GT, Hermance HW, Downes GH. Silver mi-
gration in electrical insulation. Bell System Technical
Journal 1955;34:1115±47.
[2] Shumka A, Piety RR. Migrated-gold resistive shorts in
microcircuits. In: Proc. Int. Reliability Physics Symp.
1975. p. 93±8.
[3] Benson RC, Romenesko BM, Weiner JA, Nall BH,
Charles Jr HK. Metal electromigration induced by solder
¯ux residue in hybrid microcircuits. IEEE Trans Comp,
Hybrids, Manuf Technol 1988;CHMT-10:363±70.
[4] DerMarderosian A. The electrochemical migration of
metals. In: Proc. Int. Society of Hybrid Microelectronics.
1978. p. 134±6.
[5] Ripka G, Harsa nyi G. Electrochemical migration in
thick-®lm ICs. Electrocomp Sci Technol 1985;11:281±90.
[6] Coleman MV, Winster AE. Silver migration in thick-®lm
conductors and chip attachment resins. Microelectronics
Journal 1981;4:23±9.
[7] Harsa nyi G. Dendritic growth from dielectric constitu-
ents: a newly discovered failure mechanism in thick-®lm
ICs. Int J Microcircuits and Electronic Packaging
1993;16(3):207±16.
[8] Harsa nyi G. New type short circuits at fritless thick-®lm
conductors Ð formed from reduced oxides. In: Proc.
Intern. Symp. on Microelectronics, ISHM. 1992. p. 140±
3.
[9] Harsa nyi G. Electrochemical processes resulting in
migrated short failures in microcircuits. IEEE Trans
Components Packaging, and Manufacturing Technology,
Part A 1995;18(3):602±10.
[10] Krumbein SJ. Metallic electromigration phenomena. In:
Christou A, editor. Electromigration and electronic
device degradation. New York: Wiley, 1994. p. 139±66.
[11] Sbar NL, Kozakiewicz RP. New acceleration factors for
temperature, humidity, bias testing. IEEE Trans Electron
Devices 1979;ED-26(1):56±71.
[12] Peck S, Trapp O. Accelerated testing handbook. Portola
Valley, CA: Technology Associates, 1989.
[13] Bolton PJ, Velasquez R, Manson RC. Construction,
characterization, and reliability of BaTiO3-based buried
thick ®lm capacitor materials sets, 1200 < K< 1600. In:
Proceedings of the Int. Conf. on Multichip Modules and
High Density Packaging. 1998. p. 484±9.
[14] Ho�man LC, Nakamaya T. Screen printed capacitor
dielectrics. Microelectronics and Reliability, 1968;131±
135.
[15] Ogawa T, Ootani M, Asai T, Hasegawa M, Ito O. E�ect
of inorganic binders on the properties of thick-®lm cop-
per conductor. IEEE Trans Components Packaging, and
Manufacturing Technology, Part A 1994;17(4):625±30.
[16] Harsa nyi G. Illyefalvi-Vite z Zs, Jones WK. Correlation
between material composition, processing, chemical
bonding state, and electrochemical migration failure rate
in isolating compounds of high density microelectronics
systems. In: Proceedings of the 46th Electronic
Components and Technology Conference (IEEE-CPMT),
Orlando. 1996. p. 765±71.
[17] Levin EM, Robbins CR, McMurdie HC. editors, Phase
diagrams for ceramists, National Bureau of Standards.
The American Ceramist Society, 1964.
[18] Horowitz SJ, Felten JJ, Gerry J, Larry JR, Rosenberg
RM. Recent developments in gold conductor bonding
performance and failure mechanisms, solid state technol-
ogy, March, 1979, pp. 37±51.
[19] Illyefalvi-Vite z Zs. Laser processing in MCM-C
Technologies MCM-C/Mixed technologies and thick ®lm
sensors, Jones WK et al. editors, NATO ASI Series, 3.
High technology, vol. 2, 1995, pp. 69±78.
G. HarsaÂnyi / Microelectronics Reliability 40 (2000) 339±345 345