Class23

Shaping Processes of Polymer

ElastomersIt contains long chain molecules that are cross linked. They owe their impressive elastic properties to combination of two features:(i) Long molecule tightly kinked when unstretched(ii) Degree of cross‐linking is substantially below that of thermosets

Curing is required to effect cross –linking in the elastomers. The term curing is known as VULCANIZATION  involving the formation of chemical cross‐linking of polymer chains .

Elastomers

• ViscosityViscosity is defined as resistance to fluid flowMeasure of internal friction

• ViscoelasticityCombination of viscosity and elasticityStrain gradually increases under applied stress and also decays gradually whenthe stress is removed

Properties of polymer melts

Elastomers

Natural Rubber ‐High molecular weight of ISOPRENE (C5H8)n‐ Sticky in hot weather‐Brittle in cold weather

VULCANIZATION leads to improvement of the property‐ High tensile strength‐Resilience‐Tear strength‐Resistance to wear and tear

Synthetic Rubber‐STYRENE –BUTADINE rubber : (C8H6)n(C4H6)m‐Predominant raw material is PETROLIUM

Extrusion

Normal Extrusion

Polymer Extrusion

Extruded Products

Extruded Product

Blown Film Extrusion

Polymer Fibre: Melt Spinning

Injection Moulding

Injection Moulding

Injection Moulding

Screw type

Plunger type 

Compression Moulding

Compression Moulded Products

Blow Moulding

Stretch Blow Moulding

Rotational Blow Moulding

Rotational Blow Moulding

Rotational Blow Moulding

Mobile Phone Shells

Thermoforming

Thermoforming

Semiconductor, consumer electronics and electrical, data storage, telecommunications, and medical industries.

Polymer Sheet

Chill Rolling

Transfer Moulding

Polymer Foams

Polymer Foaming