Chapter 4. Concentrated Solutions and Phase Separation Behavior

Chapter 4. Concentrated Solutions and Phase Separation Behavior

4.1 Phase Separation and Fractionation

4.1.1 Motor Oil Viscosity Example

The viscosity of today’s motor oils bears designations such a SAE 5W-30. According to crankcase oil viscosity specification SAE J300a, the first number refers to the viscosity at -18 oC, and the second number at 99 oC.

4.1.2 Polymer-Solvent Systems

According to thermodynamic principles, the condition for equilibrium between two phases requires that the partial molar free energy of each component be equal in each phase.

This condition requires that the first and second derivatives of △G1 with respect to ν2 be zero.

The critical concentration at which phase separation occurs may be written

For large n, the right-hand side of Eq (4.1) reduces to 1/n0.5.

The critical value of the Flory-Huggis polymer-solvent interaction parameter, 1, is given by

which suggests further that as n approaches infinity, 1c

approaches 1/2

The critical temperature is the highest temperature of phase separation.The equation for the critical temperature is given by

Ψ1 is constant

Plot 1/Tc versus 1/n0.5 + 1/2n should yield the -temperature at n = infinity

fractionation

The -temperature for PS/cyclohexane was 34.5 oC.

The phase separation curve called binodal line.

4.1.3 Vitrification Effects

The effect of the solvent at high polymer volume fraction is to plasticize the polymer. However, if the polymer is below its glass transition temperature, the concentrated polymer solution may vitrify, or become glassy.

The vitrification line generally curves down to lower temperatures from pure polymer as it becomes more highly plasticized.

Concentration vs. solubility?

The interception of these two curves is known as Berghmans’ point (BP) and defined as the point where the liquid-liquid phase separation binodal line is intercepted by the vitrification curve.

4.2 Regions of the Polymer-Solvent Phase Diagram

A polymer dissolves in two stages:

1. solvent molecules diffuse into the polymers, swelling it to a gel state.

2. Then the gel gradually disintegrates, the molecules diffusing into the solvent-rich regions.

In this discussion, linear amorphous polymers are assumed.

Daoud and Jannink and others divided polymer-solvent space into several regions, plotting the volume fraction of polymer, φvs. (excluded volume parameter)

: screening lengthdilute solution regime, = Rg.

Semidilute regime, measures the distance between chain contacts.

Cross-linked, provides a measure of the net size.

φvs. (excluded volume parameter)

The screening length, , first introduced by Edwards. This quantity takes slightly different meanings in different regimes

In the dilute solution regime, = Rg.

In the semidilute regime, measures the distance between chain contacts.

If the polymer is crosslinked, x provides a measure of the net size.

For semidilute solutions, the dependence of onφfollows the scaling law s ~ φ-3/4

For semidilute solutions, the dependence of on follows the scaling law

Another quantity of interest in semidilute solutions is called the blob. It contains a number of mers on the same chain defined by the mesh volume s

3, inside of which excluded volume effects are operative.

Some texts define the blob as the number of mers between adjacent entanglements, distance s apart.

These blobs are large enough to be self-similar to the whole polymer chain coiling characteristics; they are coil within coil.

4.3 Polymer-Polymer Phase Separation

When two polymers are mixed, the most frequent result is a system that exhibits almost total phase separation. Qualitatively, this can be explained in terms of the reduced combinatorial entropy of mixing.

LCST

UCST

4.3.1 Phase Diagram

Lower critical solution temperature(LCST)

Phase separation and dissolution are controlled by three variables: temperature, pressure, and concentration.

Solid line : binodal curveDash line : spinodal curve

Ex: HIPS & ABS

4.3.2 Thermodynamics of Phase Separation

The basic equation for mixing of blends reads

V : the volume of the sampleVr : the volume of one cellz : the lattice coordination numberNc : the number of cells in 1 cm3

The first term on the right being the heat of mixing term △HM. The second term on the right is the statistical entropy of mixing term, △SM.

4.3.3 An Example Calculation: Molecular Weight Miscibility Limit

4.3.4 Equation of State Theories

At equilibrium, an equation of state is a constitutive equation that relates the thermodynamic variable of pressure, volume, and temperature.

Imagine that a multicomponent mixture is mixed with No holes of volume fraction υo. Then the entropy of mixing is

Noting that the fractional free volume is given by 1-, the entropy of mixing vacant sites with the molecules in equation of state terminology is given by

Where is less than unity. When all the sites are occupied, = 1, and the right hand side is zero.

The Gibbs free energy of mixing is given by

Where the quantity * is a van der Waals type of energy of interaction.

Note that = (P,T); 1 as T 0; 1 as P ∞

By taking △Gm/ = 0, the equation of state via the lattice fluid theory is obtain

Where r is the number of sites in the chains, and

For high polymers, r goes substantially to infinity, yielding a general equation of state for both homopolymers and miscible polymer blends,

The corresponding equation of state derived by Flory is

Workers in the field prefer to state the equations in terms of density relations, because for condensed systems, density is easier to measure than volume. Again, = /* = V*/V

This information may be used to determine miscibility criteria

The quantity T* and P* represent theoretical values at close packing.

4.3.5 Kinetics of Phase Separation

Nucleation and growth Spinodal decomposition

Spinodal decomposition

4.3.6 Miscibility in Statistical Copolymer Blends

As stated previously, most homopolymer blends are immiscible due to the negative entropy of mixing and negative heats of mixing. Sometimes, however, miscibility can be achieved with the introduction of comonomers.

Karasz and MacKnight approached the problem through mean field thermodynamic considerations, arguing that negative net interactions are necessary to induce miscibility.

Where 1 and 2 are volume fractions, n1 and n2 are degrees of polymerization, and blend is a dimensionless interaction parameter defined as

Where the coefficient cij are functions of the copolymer compositions, with 0 ≦ cij ≦ 1.For An/(BxC1-x)n’ blends,

“Windows of miscibility” result when △GM < 0.

4.3.7 Polymer Blend Characterization

Very small size (20 nm) serve to make good damping compositions, while domains of the order of 100 nm make better impact-resistant materials.

Polymer blends

photophysics

4.3.8 Graft Copolymers and IPNs

SBR/PS

Block Copolymer (microphase separation)

volume fraction

< 0.20 0.20 ~ 0.35 > 0.35

disorder order

Block Copolymer phase diagram

disorder

Representative phase diagram of diblock copolymers(Khandpur et al., Macromolecules 1995, 28, 8796)

4.3.9 Block Copolymers

K is the experimental constant relating the unperturbed root-mean-square end-to-end distance to the molecular weight.

Idealized triblock copolymer thermoplastic elastomer morphology

SBS

4.3.11 Ionomers

Ionomers are polymers that contain 5% to 15% ionic groups. While these materials are statistical copolymers, the ionic groups usually phase separate from their hydrocarbon-like surroundings thus providing properties resembling multiblock copolymers.

4.4 Diffusion and Permeability in Polymers

Permeation is the rate at which a gas or vapor passes through a polymer.

The mechanism by which permeation takes place involves three steps:

(a)Absorption of the permeating species into the polymer

(b) diffusion of the permeating species through the polymer, traveling, on average, along the concentration gradient

(c) desorption of the permeating species from the polymer surface and evaporation or removal by other mechanisms.

Factors affecting permeability include the solubility and diffusivity of the penetrant into the polymer, polymer packing and side-group complexity, polarity, crystallinity, orientation, fillers, humidity, and plasticization.

4.4.1 Swelling Phenomena

If the polymer is glassy, the solvent lowers the Tg by a plasticizing action. Polymer molecular motion increases. Diffusion rates above Tg are far higher than below Tg.

4.4.2 Fick’s Laws

Fick’s first law governs the steady-state diffusion circumstance:

Fick’s second law controls the steady state:

The permeability coefficient, P, is defined as the volume of vapor passing per unit time through unit area of polymer having unit thickness, with a unit pressure difference across the sample. The dolubility coefficient, S, determines the concentration. For the simple case

A study of vapor solubility as a function of temperature allows the heat of solution △Hs to be evaluated.

The permeability coefficients depend on the temperature according to the Arrhenius equation,

Where △E is the activation energy for permeation

The temperature dependence of the solubility obeys the Clausius-Clapeyron equation

4.4.3 Permeability Units

4.4.4 Permeability Data

4.4.5 Effect of Permeate Size

4.4.6 Permselectivity of Polymeric Membranes and Separations

4.4.6.1 Types of Membranes

1. Passive transport

2. facilitated transport

3. Active transport

4.4.6.2 Gas Separations

Gas selectivity is the ratio of permeability coefficients of two gases

4.4.7 Gas Permeability in Polymer Blends

4.4.8 Fickian and Non-Fickian Diffusion

4.5 Latexes and Suspensions

4.5.1 Natural Rubber Latex

4.5.2 Colloidal Stability and Film Formation

4.6 Multicomponent and Multiphased Materials