8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
1/17
http://hip.sagepub.com/High Performance Polymers
http://hip.sagepub.com/content/12/3/445Theonline version of this article can be found at:
DOI: 10.1088/0954-0083/12/3/307
2000 12: 445High Performance PolymersAlexander A Kuznetsov
One-Pot Polyimide Synthesis in Carboxylic Acid Medium
Published by:
http://www.sagepublications.com
can be found at:High Performance PolymersAdditional services and information for
http://hip.sagepub.com/cgi/alertsEmail Alerts:
http://hip.sagepub.com/subscriptionsSubscriptions:
http://www.sagepub.com/journalsReprints.navReprints:
http://www.sagepub.com/journalsPermissions.navPermissions:
http://hip.sagepub.com/content/12/3/445.refs.htmlCitations:
What is This?
- Sep 1, 2000Version of Record>>
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/content/12/3/445http://hip.sagepub.com/content/12/3/445http://www.sagepublications.com/http://www.sagepublications.com/http://hip.sagepub.com/cgi/alertshttp://hip.sagepub.com/cgi/alertshttp://hip.sagepub.com/subscriptionshttp://hip.sagepub.com/subscriptionshttp://www.sagepub.com/journalsReprints.navhttp://www.sagepub.com/journalsReprints.navhttp://www.sagepub.com/journalsPermissions.navhttp://www.sagepub.com/journalsPermissions.navhttp://hip.sagepub.com/content/12/3/445.refs.htmlhttp://hip.sagepub.com/content/12/3/445.refs.htmlhttp://online.sagepub.com/site/sphelp/vorhelp.xhtmlhttp://online.sagepub.com/site/sphelp/vorhelp.xhtmlhttp://hip.sagepub.com/content/12/3/445.full.pdfhttp://hip.sagepub.com/content/12/3/445.full.pdfhttp://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://online.sagepub.com/site/sphelp/vorhelp.xhtmlhttp://hip.sagepub.com/content/12/3/445.full.pdfhttp://hip.sagepub.com/content/12/3/445.refs.htmlhttp://www.sagepub.com/journalsPermissions.navhttp://www.sagepub.com/journalsReprints.navhttp://hip.sagepub.com/subscriptionshttp://hip.sagepub.com/cgi/alertshttp://www.sagepublications.com/http://hip.sagepub.com/content/12/3/445http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
2/17
High Perform. Polym. 12(2000) 445460. Printed in the UK PII: S0954-0083(00)14912-8
One-pot polyimide synthesis in carboxylic acid medium
Alexander A Kuznetsov
Institute of Synthetic Polymeric Materials, Russian Academy of Science, 70, Profsoyuznaya ul.,Moscow, 117393, Russia
Received 23 June 2000
Abstract. The melts of aromatic carboxylic acids such as benzoic acid (BA) at 130160 Cwere shown to be excellent media for the one-pot synthesis of high molecular weight, completelycyclicized polyetherimides (PEIs) from the corresponding diamines and tetracarboxylic aciddianhydrides. According to the data on the cyclodehydratation (CD) kinetics of oligomeric amic
acid model compounds, the rate of cyclicization of transient polyamic acids in BA at 140 C isveryhigh, and the polymer chain growth proceeds via the polyaddition of completely cyclicized PEIoligomers withaminoand anhydride endgroups. Tetracarboxylicacids in BAat 140 C were shownto react with aromatic diamines to obtain high molecular weight PEIs as well as the correspondingdianhydrides. The effect of the total concentration of comonomers and the presence of an inertdiluent on the kinetics of the growth of the inherent viscosity in the polycyclocondensation ofdiaminesand dianhydridesis discussed fromthe point of viewof the mechanism of the process. Theprospectof a novel synthetic approachin polyimide synthesis is discussed, including obtaining newhomopolyimides based on extremely-low-reactivity monomers; new statistical, regular, alternatingcopolyimides and block copolyimides; two-component blends with one glass transition point, andPEIs based on AB-type heteromonomers.
1. Introduction
Carboxylic acids are known to be catalysts in a large variety of organic reactions, including
the two reactions which are of great importance for polyimide chemistry, namely: (a) the
acylation of diamines with tetracarboxylic acid dianhydrides and (b) the cyclodehydratation
(CD) ofo-carboxyamide (amic acid) moieties. In this connection, the idea of using carboxylic
acids in polyimide synthesis as a catalytic agent and the reaction medium simultaneously seems
to be attractive.
The kinetics and thermodynamics of the acylation of aromatic diamines with carboxylic
acid dianhydrides has been investigated in detail [15]. Acid catalysis in the acylation of
aromatic diamines was probably first demonstrated by Litvinenko et al in the 1960s [6, 7]
and it was then studied in detail [810]. Thus, it was shown that addition of a small quantity
of chloroacetic acid (CAA) to a chloroform solution containing equimolar concentrations of
p-substituted anilines and phthalic anhydrides (PAs) results in the strong acceleration of thereaction (see scheme 1) due to appearance of a catalytic channel [9].
In the absence of CAA, a clear autocatalytic behaviour occurs in CHCl 3and acectonitrile
(AcCN) because of the catalysis of the reaction by phenylphthalamic acid (PPA), the reaction
product, the rate constant of the direct reaction via the catalytic channel being an order
of magnitude greater than that via ordinary reaction [10]. In more basic solvents such as
dimethylacetamide (DMAA), the autocatalytic regime does not occur because of the strong
interaction of the amic acid with the solvent, and the overall acylation rate is not too large.
0954-0083/00/030445+16$30.00 2000 IOP Publishing Ltd 445
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
3/17
446 A A Kuznetsov
Scheme 1.
On the other hand, the strong interaction of the amic acids with the solvent leads to the
largest values of the acylation equilibrium constant (and connected with the latter, the degree
of polymerization of the polyamic acids) being achieved in just the amic solvents. A very
specific feature of the acid-catalysed acylation reaction in CHCl3 and AcCN is the extreme
dependence of the overall rate of the process versus the content of acid catalyst added, caused
by the protonation of amino groups with an excess of the catalyst. This fact probably explains
why high concentrations of carboxylic acid have not been used in one-pot polyimide synthesis.Acid catalysis in the CD reaction of polyamic acid (PAA) was demonstrated first in 1977
by Vinogradovaet al [11] and Lavrov et al [12, 13]. In the absence of acid additives, clear
second order was found for the CD reaction of PAA by Lavrov et al[13] and Kim et al [14].
The self-catalysis of the CD reaction of model amic acids in concentrated solutions in amic
solvents was demonstrated by Kuznetsovet al [15], amic acid being the reagent and catalyst
simultaneously, and the solvent playing the role of co-catalyst.
Recently, we have discovered that the melts of aromatic carboxylic acids such as benzoic
acid (BA) at 130160 C can be used as the reaction media in catalytic one-pot syntheses
of high molecular weight completely cyclicized polyimides from corresponding diamines and
tetracarboxylic acid dianhydrides [1619]. This article is a development of the novel approach.
2. Experimental details
2.1. Starting materials
2,2-bis[(4-aminophenoxy)phenyl]propane (BAPP, technical grade product, Russia) was
purified by crystallization from isopropanol, Tm = 129C. m-phenylenediamine (PDA,
Tm = 6466C) and hexamethylenediamine (HMDA, Tm = 4445
C) were purified by
distillation in vacuo. 2,6-diaminopyridine (DAP, Aldrich) was purified by sublimation
in vacuo,Tm =122C.4,4-oxydianiline (ODA) (Russia) was purified by sublimation invacuo,
Tm = 190C. 4,4-diaminodihenyl sulfone (Russia) was crystallized from isopropanol,
Tm =175C.
3,3,4,4-biphenyltetracarboxylic acid (BPTA) was obtained by the dehydration of the
corresponding acid dihydrate (BPTA.2H2O) at 200C for 30 min. BPTA.2H2O was
synthesized by Professor E L Vulah of the Research and Technical Design Institute ofMonomers (Tula, Russia) and it was kindly presented for our disposal. The 3,34,4-
biphenyltetracarboxylic acid dianhydride (BPDA) was obtained by heating BPTA at 270 Cfor
2 h. BPDA displays only one peak in the differential scanning calorimetry (DSC) thermogram
at 300 C (literature data Tm = 286C [20]). 4,4-oxydiphthalic anhydride (technical
grade, Russia) was crystallized from acetic dianhydride and sublimated at 200 C in vacuo,
Tm = 221C. 2,2-bis[(3,4-dicarboxyphenoxy)phenyl]propane dianhydride (BPADA) and 4-
aminophenoxyphthalic acid (APPA) were synthesized by Professor M V Dorogov of the
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
4/17
One-pot polyimide synthesis in carboxylic acid medium 447
Department of Organic Chemistry, State Yaroslavl Technical University (Russia) and used
as received;Tm =188189C (BPADA).
BA was purified by distillation under ambient pressure and an inert atmosphere,
Tm =122C; diphenylsulfone was crystallized from isopropanol, Tm = 126128
C; and
m-cresol was distilled under vacuum before use.
2.2. Synthesis of polyetherimide
The synthesis of polyetherimides (PEIs) from diamines and tetracarboxylic acid dianhydrides
in the melt of BA is described below by the example of PEI-2. 0.5825 g (1.42 mmol) of
BAPP, 0.4175 g (1.42 mmol) BPDA and 9.0 g of BA were loaded into a glass reaction vessel
equipped with a stirrer under a slow flow of argon. The reactor was placed into an oil bath at
140 C. After melting the BA a stirrer was turned on. The time to reach 140 C was less than
3 min. The reaction was carried out under an argon atmosphere for 1 h. At a definite time
after reaching 140 C, the probes were removed from the reaction medium. After cooling each
probe was treated with acetone to remove the BA; the polymer residue was dried and analysed
by Fourier-transform infrared (FTIR) spectroscopy and viscometry. The FTIR spectra wereobtained using a Nicollett FTIR, Impact 410 spectrometer; the samples for the FTIR were
made of CsI. The conversion of the CD reaction for PEI-2 was measured using the peaks at
1370 cm1 (CN vibration in the imide cycle) and 1500 cm1 (CC vibration in an aromatic
cycle; the internal standard). In the case of PEI-1 and other polymers based on BPADA, the
region of 1370 cm1 is not available because of its own absorption related to the isopropylidene
moiety. So, for the PEI of this group, the conversion of the CD reaction was estimated using
the intensity ratio of the peaks at 620 cm1 (imide cycle) and 690 cm1 (internal standard)
using a previously obtained calibration curve. The inherent viscosity () was measured for
solutions containing 0.5 g of polymer in 100 ml in N-methylpyrrolidone (N-MP) using an
Ubellode viscometer at 25 C. The PEIs on the basis of all other monomer pairs (diamine,
dianhydride) were obtained analogously.
2.3. Synthesis of PEI-2 from diamine and tetracarboxylic acid (BAPPBPTA)
0.583 g (1.42 mmol) of BAPP and 0.463 g (1.42 mmol) BPDA and 9.0 g of BA were loaded
into a glass reactor. The process was carried out for 3 h at 140 C, analogously to that for the
dianhydride.
2.4. The kinetics of the CD of the model compound PAA-1 in the melt of BA
Oligomeric amic acid PAA-1 with = 0.13 dl g1 (Mw = 3000) was obtained as described
earlier [18]. For the goal of the measurement of the CD reaction rate, 30 mg of solid PAA-1
and 270 mg of BA were loaded into 10 identical thin-walled glass microtest-tubes which were
all placed into the oil bath simultaneously. In a control experiment, the time to reach 140 C inevery test-tube was estimated, by thermocouple, to be the same: 10 s. At a definite time after
reaching 140 C, the first, second, etc, test-tube was removed and cooled quickly to 20 C. The
BA was extracted with diethyl ether and the polymer residue was analysed by means of FTIR
spectroscopy (in a pellet of CsI). The conversion by CD was measured from the intensity ratio
of the peaks at 620 cm1 (imide cycle) and 690 cm1 (internal standard) using a previously
obtained calibration curve. The completely cyclicized oligomeric PEI was obtained by heating
the PEI-1 sample in a DSC cell at 300 C at a heating rate of 16 C min1.
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
5/17
448 A A Kuznetsov
2.5. Preparation and analysis of two component polyimidepolyimide formulations
The formulations madeex situwere prepared by dissolution of solid PEI-1 and PEI-7 in the
melt of BA at 140 C. PEI-1 and PEI-7 samples were synthesized separately in the melt of BA
at 140
C for 1 h, each at a 10% load and a 1:1 molar ratio of diamine and dianhydride in thepresence of 1.0% PA as an endcapping agent. The PEI-7/PEI-1 ratio in the mixture was varied
from 0.1:0.9 to 0.9:0.1; the total concentration was equal to 10 wt%. The inherent viscosity
was equal to = 0.35 dl g1 (PEI-7) and = 0.42 dl g1 (PEI-1). After the loading of the
polymers, the mixture was stirred for 1 h, the reaction mixture was then poured into a crucible
and then treated as described above.
The in situ-made formulations were prepared by carrying out the catalytic synthesis of
PEI-7 from HMDA and BPADA (1:1 molar ratio) in the melt of BA at 140 C for 1 h, without
adding any PA. Then PDA and BPADA (1:1) were loaded into the hot reaction medium and
after 1 h PEI-1 was obtained in the presence of PEI-7. The PEI-7:PEI-1 ratio was varied. The
total concentration of PEI-7 and PEI-1 in the reaction mixture was held constant and equal to
10 wt%. The other details of the preparation the sample were the same.
Polymer formulations of both types were hot pressed at 280 C to give pellets. TheTg
values were determined by DSC (DTAP-4, Russia) at a heating rate of 16 C min1. The dataobtained in a second scan were used to determine theTg values to elucidate the possibility of
the influence of a thermal prehistory on the results.
3. Results and discussion
3.1. The melt of BA as a non-toxic catalytic medium for the one-pot synthesis of PEI
BA is known to possess a useful combination of properties: (1) it is a powerful catalyst of the
CD reaction of PAA; (2) as a melt at 140160 C, it is a good solvent for many aromatic PEIs.
Therefore, we propose the melt of BA as alternative solvent for one-pot polyimide synthesis
[18, 19]. An additional advantage of BA appears from consideration of the toxicity data. It is
well known thatm-cresol ando-dichlorobenzene (DCB), which are commonly used as high-
boiling-point organic solvents in high-temperatureone-pot polyimide synthesesat 130180 C,
are known to be very toxic substances: the minimal toxic concentrations ofm-cresol and DCB
are 5 and 20 mg m1, respectively. In contrast, BA at ambient temperature is a non-toxic
solid; moreover, in small quantities it is used as a preserving additive for tinned food. Besides
the superiority over m-cresol in toxicity, BA can be easily separated from the polymer after
completing the process. On cooling, the reaction mixture solidifies and microphase separation
takes place, BAforming its own crystalline phase. The latter can be easily removed by repeated
washing with acetone.
In figure 1 and figure 2 (curve 1) the kinetics of the inherent viscosity growth of PEI-1
and PEI-2 from a one-pot synthesis in the melt of BA is shown; the starting monomer pairs
were PDABPADA and BAPPBPDA, respectively. The macromolecules PEI-1 and PEI-2
contain the same two hinge fragments of bis-phenol A (BPA) in the elementary chain unit,
but differ from each other by its location: PEI-1 contains a BPA fragment in the anhydride
moiety, whereas PEI-2 contains it in the diamine moiety. In both cases PEI synthesis proceedsas a homogeneous process throughout all the time of synthesis. In a typical experiment, the
reaction of equimolar quantities of PDA and BPADA at a total of 10% comonomer mixture
load takes about 1 h to give a completely cyclicized product (according to FTIR data) with
= 0.78 dl g1. The structure and characteristics of several PEIs obtained by us in one-pot
syntheses in the melt of BA are collected together in table 1.
In all cases, values of the inherent viscosity () of about 0.40.5 dl g1 and more were
achieved in 1 h. It should be noted that the level of = 0.5 dl g1 seems to be optimal for a
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
6/17
One-pot polyimide synthesis in carboxylic acid medium 449
Figure 1. Kinetics of the growth of the inherent viscosity of PEI-1 from PDA and BPADA in theone-pot synthesis at 140 C in the melt of BA (total monomer concentration 10 wt%).
Figure 2.Kineticsof thegrowth of theinherent viscosityof PEI-2 from BAPP andBPDA at 140 Cin different media: (1), the melt of BA; and (2), the melt of BA:DPS, 1:1 mixture (total monomerconcentration 10 wt%).
PEI intended for further melt processing of the PEI. If necessary, the molecular weight of the
PEI can be controlled by the choice of the stoichiometric ratio or by monofunctional additives
such asp-anisidine and PA (figure 3).
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
7/17
450 A A Kuznetsov
O
O
C
CO
CH3
CH3
CO
O
O
C
COO
OO
OO
O
C
C
O
C
C
C
C
O
O
O
C
C
O
O
O
Structure 1.
Table 1. Characteristicsof PEIs obtained from dianhydrides (structure 1) and diamines of common
formulae H2NXNH2 in the melt of BA, (140C for 1 h). Note that the glass transition
temperatures and the melting pointsare given for the amorphous and crystallinephase, respectively.
Viscosity () in Tg Tm
X Diamine Dianhydride PEI N-MP (dl g1) (C) (C)
PDA BPADA PEI-1 0.78 220
BAPP BPDA PEI-2 0.50 240
BAPP ODPA PEI-3 0.40 220
BAPP BPADA PEI-4 0.48 200
ODA ODPA PEI-5 0.42 265 340
ODA BPADA PEI-6 0.52 220
(CH2)6 HMDA BPADA PEI-7 0.40 120 165
SO2 DDS BPADA PEI-8 0.5 230
DAP BPADA PEI-9 0.56 220
+
NPDA: BPDA PEI-10 0.50 220
DAP
(1:1)
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
8/17
One-pot polyimide synthesis in carboxylic acid medium 451
Figure 3. The influence of the addition of (1) PA and (2) anisidine as endcapping agents on theinherent viscosity of PEI-1 (140 C for 1 h).
It is believed that the one-pot polyimide synthesis in BA includes two chemical reactions,
thefirst being the acylation of the diamine with the tetracarboxylic acid dianhydrides to give
PAAs, the second being the CD of transient o-carboxyamide moieties to give imide cycles
(scheme 2). The peculiarity of the process in BA is that the rate of CD of transient PAAs
is very high under the conditions chosen. To demonstrate this, we tried to estimate the
CD rate of a model oligomeric amic acid PAA-1 in the melt of BA at 140 C. PAA-1 was
previously synthesized by us for this experiment. The data obtained are presented infigure 4
(curve 1). It is seen that the CD kinetics of PAA-1 in the melt of BA at 140 C is very
fast, too fast for us to calculate accurately the CD rate. However, these data are enough to
conclude that the chain growth in the one-pot synthesis proceeds basically via a polyaddition
reaction of thefully cyclicized oligomerswith amino andanhydrideendgroups. Dueto thefast
disappearance of theo-carboxyamide moieties in thecourse of theCD reaction, theequilibrium
of the polycondensation is shifted continuously to the side of polymer chain growth, and high
molecular weight completely cyclicized PEIs can be obtained in the melt of BA; contrast this
to that in amic solvents at comparable temperatures.
In contrast to the high rate of the CD, the growth rate of the inherent viscosity of PDA
BPADA in BA at 140 C is about the same order of magnitude as that in polycondensation
at 20 C that results in PAA. Taking into account the large difference in temperature (120 C)between the conditions of polycondensation and the one-pot synthesis in BA, it should be
concluded that diamines in the melt of BA are strongly deactivated, probably due to hydrogen
bonding with BA. As a result, the efficient acylation rate in the melt of BA at 140 C is about
the same as that in the polycondensation reaction in an amic solvent at 20 C. The acylation
rate in the melt of BA is probably much lower than that of the CD reaction; the acylation rate
only is thought to determine the time necessary to obtain completely cyclicized polyimide of
a definite molecular weight.
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
9/17
452 A A Kuznetsov
Scheme 2.
0 2 4 6 8 1 0
0
2 0
4 0
6 0
8 0
1 0 0
T i me, mi n
P ,% 2
1
Figure 4.Kinetics of the CD of PAA-I at 140 C: (1) in the solid state; and (2) in the melt of BA.
To confirm the correctness of the proposed mechanism for the process, we investigated
the one-pot synthesis in the melt of BA in the presence of a co-solvent. In figure 2 (curve 2)
the kinetic curve of the inherent viscosity growth in mixtures of BA/diphenylsulfone (DPS)
(50:50 by weight) is shown. The appearance of the viscosity maximum at the start of the
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
10/17
One-pot polyimide synthesis in carboxylic acid medium 453
Figure 5. Dependence of the 10 min inherent viscosity value of PEI-2 against the total weight
concentrationCof mononers in BA, at 140 C.
process can be explained by the presence of a considerable quantity ofo-carboxyamide (amic
acid) moieties in the growing polymer chain, which afford higher hydrodynamic radius to
macromolecules in comparison with that for PEI for an equal degree of polymerization. In
turn, the increased concentration of the transient product in a case of BA/DPS can only be a
result of changing the ratio of the cyclicization/acylation rates in comparison with that in pure
BA. Indeed, the addition of any inert diluent to BA is expected to retard the CD because of the
decrease of the concentration of the cyclicization agent (BA). At the same time, the dilution
will lead to a decrease of the hydrogen bonding of the diamine and BA and, as intended, to
the acceleration of the acylation stage. Moreover, in BA/DPS mixtures, the balance of the
acylation/CD rates is shifted considerably in favour of acylation in comparison with that in
pure BA.
In figure 5, the experimental dependence of the rate of the initial inherent viscosity growth
of PEI-2 against the total monomer concentration is shown. The true reason for the decrease
of the rate at high monomer concentration is not clear. The preliminary supposition is that
this effect is connected with the change of any of the medium characteristics influencing the
balance of the acylation/CD rates.
3.2. New polyimides and statistic copolyimides from low-reactivity diamines
It can be seen from table 1 that high molecular weight PEIs were obtained successfully
even from low-reactivity diamines such as 4,4-diaminodiphenylsulfone (DDS) and 2,6-
diaminopyridine (DAP). The low reactivityof the DDS in polycondensation is connected
with its low basicity. DAP is known to possess extremelylow reactivityas a nucleophylic
reagent due to occurrence of the aminoimine tautomerism. Furthermore, DAP is known to
give no polyimides under conditions of high-temperature one-pot synthesis in cresol. To check
this, in a control experiment, the reaction between DAP with BPADA (1:1 molar ratio, 10%
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
11/17
454 A A Kuznetsov
total monomer load) was carried out by us in m-cresol: after 1 h at 170 C no polymer was
precipitated after adding an excess of methanol. In contrast to this, the high molecular weight
polymer PEI-9 was isolated in quantitative yield after synthesis in BA at 140 C for 1 h.
According to the inherent viscosity data (table 1), the difference in efficient reactivity of
low- and high-reactivity diamines is not observed in the melt of BA, in contrast to that in amicsolvents at ambient temperature. The equal reactivity of highly basic ODA and low basicity
DDS in the melt of BA can be explained by the phenomenon of theequal basicityof strong
and weak bases in acidic media. As concerns the high reactivity of DAP in the BA medium,
the effect observed maybe connectedwith the ability of BA to coordinate thepyridine nitrogen
atom through hydrogen bonding and prevent the aminoimine tautomerism and, hence, lead
to an increase in the reactivity of the amino groups in DAP. Besides, the reactivity equalization
phenomenon in the melt of BA can be useful for obtaining new statistical copolyimides.
To demonstrate this, we made experiments on copolycyclocondensation of BPADA with the
mixture of PDA and DAP (1:1 molar ratio). As can be seen from table 1, a high molecular
weight co-PEI was successfully obtained with =0.50 dl g1 for 1 h at 140 C. The large
value of the inherent viscosity is evidence for the comparable reactivity of the two diamines
in BA, otherwise the more reactive of these two must be in a large excess of the dianhydride,resulting in an oligomeric product.
3.3. Regular and alternating copolyimides and block copolyimides
The new approach makes it possible to obtain new regular, alternating and block copolyimides
in the one-pot process. In this work, by means of two-step chain growth in the course of an
in situconsequent catalytic polycyclicization, a series of novel regular PEIs was synthesized.
They consist of two types of polyimide blocks: A and B. Block A being a fragment of PEI-
1 (an amorphous, thermoplastic and soluble polymer) and block B being a product of the
cyclopolycondensation of PDA and BPDA (a non-thermoplastic and non-soluble polymer, see
structure 2).
As a first step, the oligomer of the PEI-1 structure with amino end groups was obtained
by cyclopolycondensation of PDA and BPADA taken at molar ratios of 1:0.9, 1:0.85, 1:0.7
and 1:0.6. As a second step, BPDA was added in a quantity corresponding to the overall 1:1
stoichiometric ratio of all amino and anhydride groups, and reaction was continued for 1 h
more (table 2). Theoretically, the synthesis strategy chosen must lead to a so-called regular
copolymer, i.e. to the polymer containing individual fragments of the first type (in our case
PDABPDAPDA)separatedfrom each otherby longersequences of theothertype (inourcase
(PDABPADA)n). Characteristics of the polymeric products obtained are given in table 2.
The values of the glass transition temperature Tg increase smoothly with increasing
numbers of BPDA fragments, from 220 C (PEI-1, sample 1) to 245 C (sample 5). The
samples 24 are soluble in N-MP, sample 5 is soluble only in H2SO4. Theoretically, further
increases of the BPDA content in a regular copolymer upto 50:50 BPADA:BPDA ratio mustlead to strongly alternating structures. In this series we met a solubility limitation. However,
it is believed that by the use of appropriate monomers, alternating copolymers are achievable
through thesynthesis strategyoffered. It shouldbe noted that thefragment(PDABPDAPDA)
which is present in the copolyimides (samples 25) is a long enough rigid block consisting
of six aromatic and heteroaromatic moieties connected without hinge atoms. Therefore, the
regular copolyimides obtained can also be considered as block copolymers. In the future we
intend to apply this strategy to obtain other types of block copolyimides.
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
12/17
One-pot polyimide synthesis in carboxylic acid medium 455
Structure 2.(a) Block A, PEI-1 and (b) block B, poly-(PDABPDA).
Table 2.Characteristics of regular copolyimides based on PDA(BPDA + BPADA) obtained by atwo-step one-pot synthesis in the melt of BA at 140 C (1 + 1 h)
BPDA/BPADA ratio Tgby DSC Solubility in Inherent viscosity in
SampleN (mol:%) (C) N-MP H2SO4(dl g1)
1 0:100 (PEI-1a, control) 220 + 0.40
2 10:90 225 + 0.35
3 15:85 230 + 0.33
4 30:70 235 + 0.34
5 40:60 245 + 0.34
6 0:100 (control)b 0.28
a In the presence of 0.5% PA.b The polymer precipitates from the reaction medium.
3.4. Two-component polyimidepolyimide systems with one glass transition temperature
An interesting application of the new synthesis method is the preparation of polyimide
polyimide blends with one glass transition temperature via consequent one-pot polyimide
synthesis in situ of twopartially compatible polyimides [21]. Two types of the two-component
formulations (PEI-7/PEI-1) were prepared: thein situ-madeformulations and the ex situ-
made formulations. The in situ-made formulations were prepared by carrying out therespective catalytic synthesesof PEI-7 andPEI-1 in BA. The mechanically-made formulations
were prepared by the dissolution of separately synthesized PEI-7 and PEI-1 (each in the
presence of PA as an endcapping agent) in the melt of BA. All other details of the preparation
of the samples were kept the same. The phase diagrams were designed for all the formulations
on the basis of the DSC data. In the case of an ex situ-made formulation (figure 6), a clear
microphase separation occurs in a wide interval of PEI-7:PEI-1 ratios from 80:20 to 10:90,
the Tg values for each phase being equal to 140 and 210C, respectively. In contrast, the
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
13/17
456 A A Kuznetsov
Figure 6. Phase diagram of binary polyimidepolyimide formulations (PEI-1/PEI-7):mechanically-made formulations (a and b branches); in situ-made formulations (points AE);andin situ-made formulations with complete endcapping of PEI-7 (points G and F). See text for
further details.
experimentalTgvalues of the in situformulations depend on the content; the corresponding
points AE in figure 6 for the in situ-made formulations are located inside the region of the
phase separation of the ex situ-made blends. Thus, thein situformulations behave as systems
with a molecular level of compatibilization. At the same time, by means of turbidimetry
analysis, the in situ-made formulations were identified as a mixture of homopolymers (or
a long-chain diblock copolymer), but not as a statistical copolymer. In a course of special
experiments using completely end-capped PEI-7, it was shown that the quasi-one-component
morphology behaviour observed in the in situformulation was caused by the formation of
small quantity of a diblock copolymer playing the role of stabilizer of the polymerpolymer
microemulsion particles and retarding the phase separation. More details will be given in a
separate paper [22].
3.5. Direct polycondensation of diamines and tetra-acids
It is well known that a high quality of comonomers is a very important factor in fluencingthe molecular weight of thefinal polyimides. In the long-term storage of dianhydrides, the
hydrolysis productsthe corresponding di- and tetra-acidscan accumulate as impurities.
Tetra-acids are not reactive as acylating agents. Therefore, the purification of dianhydrides
and the current control of the quality are strong requirements in usual polyimide chemistry. As
was shown above, the melt of BA can act as a powerful dehydrating agent in relation to amic
acid moieties. Hence, it was suggested that it could serve as an in situdehydrating agent for
tetracarboxylic acids. In this work we investigated the possibility of using the tetracarboxylic
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
14/17
One-pot polyimide synthesis in carboxylic acid medium 457
Figure 7.DSC thermograms of (1) BPTA.2H2O, (2) BPTA and (3) BPDA.
acid BPTA instead of the dianhydride BPDA in the catalytic synthesis of PEI-2 in the melt
of BA. As can be seen from DCS thermograms of BTPA (figure 7 (curve 2)), anhydridization
of solid BPTA on heating occurs in a region of 250270 C (wide endo peak); the second
endo peak at 300 C corresponds to the melting of the BPDA formed in situ. The second
scan obtained after cooling sample 2 (figure 7 (curve 3)) contains only a peak at 300 C which
coincides with the melting peak of pure BPDA. The temperature of the beginning of the BPTA
anhydridization is much higher than that of the loss of the coordinated water molecules by
BPTA.2H2O (140170C) (figure 7 (curve 1)) and higher than the optimal temperature of the
one-pot synthesis in the melt of BA (140 C).To check thesuggestion offered above,a seriesof
experiments were carried out on polyimide synthesis in BA using the tetra-acid BPTA instead
of the corresponding dianhydride (BPDA).
Infigure 8 (curve 2) the kinetics of the growth of the inherent viscosity of PEI-2 obtained
from BAPPBPTA at 140 C is shown. It is seen that a high molecular weight PEI-2 with an
inherent viscosity of 0.5 d l g1 wasobtained after 3 h, although thechain growth is slower than
that in the case of BPDA (figure 7 (curve 1)). Obviously, the cyclopolycondensation process
of BTDA with BAPP includes the stage of formation of BPDAin situ(scheme 3), the latter
reaction being the rate-determining step in the process as a whole.
3.6. Polycondensation of heteromonomers (AB-type monomers)
The opportunity demonstrated above for the direct polycyclocondensation of diamines and
tetra-acids has reinitiated our interest in AB-type heterocomonomers for polyimides, such as
APPA. According to the data of IR spectroscopy [23], APPA exists in the form of a zwitter ion
(the equilibrium structures in scheme 4).Intramolecular proton transfer makes AB-type heterocomonomers extremely low in
reactivity in polycondensation reactions. According to [23], they can be converted to
polyimides only by a two-stage synthesis, thefirst stage beingthedirect homopolycondensation
in the presence of (Ph)3P=O, and the second being chemical imidization. Infigure 9 FTIR
spectra areshown of theinitial APPA (spectrum1) andof theoligomeric product (0.20dlg1 in
H2SO4solution)obtained byheating APPA in themelt of BAat 140C for 45min (spectrum 2).
The absorption near 16001660 cm1 related to the zwitter-ion structure of APPA disappears
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
15/17
458 A A Kuznetsov
Figure 8. Kinetics of the growth of the inherent viscosity of PEI-2 obtained in the melt of BA
starting from pairs of (1) diaminedianhydride (BAPPBPDA) and (2) diaminetetracarboxylicacid (BAPPBPTA) (140 C, total monomer concentration 10 wt%).
Scheme 3.
Scheme 4.
and the imide peaks at 1720 and 1790 cm 1 appear instead. The spectrum of the oligomeric
product obtained in BA is similar to that obtained by polymerization on heating of solid APPA
up to 250 C (figure 9 (spectrum 3)). So, it can be concluded that treatment of AB compounds
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
16/17
One-pot polyimide synthesis in carboxylic acid medium 459
Figure 9. FTIR spectra of (1) APPA, (2) the oligomeric product ( =0.20 dl g1 in H2SO4)
obtained by heating the APPA in the melt of BA at 140 for 45 min; and (3) the product (insoluble
in H2SO4) obtained after heating solid APPA at 250C for 5 min.
in the presence of an acid catalyst at 140 C results in the corresponding PEI (poly-APPA,
figure 9 (scheme 4)), although the molecular weight is not too large. Even more interesting
opportunities appear for the synthesis of linear and star-shaped block copolymers. This work
is also in progress.
4. Conclusion
The main conclusions are as follows.
(1) The meltof BA at140160 C is showntobeanadvancedreactionmediumfor thecatalytic
one-pot process for obtaining high molecular weight, completely cyclicized polyimide
products, including:
(a) thermoplastic PEIs known from the literature;
(b) new polyimides based on low-reactivity diamines;
(c) new statistic copolyimides, containing both high- and low-reactivity diamine
moieties;(d) new regular, alternating and, probably, block copolyimides;
(e) two-component polyimidepolyimide blends with one glass transition temperature;
(f) PEIs based on AB-type heteromonomers.
(2) The direct polycyclocondensation of diamines with tetracarboxylic acids is demonstrated
to occur in the melt of BA at 140160 C to give high molecular weight completely
cyclicized polyetherimides.
at CICY - Parent on June 11, 2014hip.sagepub.comDownloaded from
http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/http://hip.sagepub.com/8/12/2019 2000 - One-Pot Polyimide Synthesis in Carboxylic Acid Medium
17/17
460 A A Kuznetsov
Acknowledgments
The work was supported by the General Electric Plastics Co. and also by RFBR, grant
97-03-32740. The author also express his thanks to Dr S V Lavrov, Dr V I Berendyaev,
A Yu Tsegelskaya, Dr N V Kozlova, I D Egorov (all from the Karpov Institute of PhysicalChemistry, Moscow), Dr G K Semenova, M Yu Yablokova, L V Ryabova (ISPM RAN), Dr
Belov M Yu (Institute of Problem of Chemical Physics, Chernogolovka) for their participation
in the experimental work; to Professor E L Vulah and Professor M V Dorogov for the synthesis
of the starting materials; and Professor B V Kotov for fruitful discussions of the results.
References
[1] Sroog C E 1991Prog. Polym. Sci16561694
[2] Bessonov M I, Koton M M, Kudryavtsev V V and Layus L A 1987Polyimides: High Thermostable Polymers
(New York: Plenum)
[3] Ardashnikov A Ya, Kardash I E and Pravednikov A N 1971Vysokomol. Soyed. (Polym. Sci. USSR)A131863
(in Russian)
[4] Svetlichny V M, Kudryavtsev V V, Kalninsh K K and Koton M M 1977Rep. Sov. Acad. Sci. 3693[5] Pebalk D V, Kotov B V and Neiland O Ya 1977Rep. Sov. Acad. Sci. 6236
[6] Litvinenko L M, Alexandrova D M and Zhilinskaya A A 1960Ukr. Chim. Z. 26476 (in Russian)
[7] Litvinenko L M and Alexandrova D M 1961Ukr. Chim. Z. 27212
[8] Solomin V A, Kardash I E, Snagovski Yu S, Messerle P E, Zhubanov B A and Pravednikov A N 1977Dokl.
Acad. Nauk USSR236139 (in Russian)
[9] Sadovnikov A I and Kuritsin L V 1981Izv. Vuzov, ser. Chim. i chim. Tehnologiia24316 (in Russian)
Sadovnikov A I and Kuritsin L V 1981 Izv. Vuzov, ser. Chim. i chim. Tehnologiia24847 (in Russian)
[10] Kalninsh K K 1987Izv. Acad. Nauk USSR, ser. Chim 19871978 (in Russian)
[11] Vinogradova S V, Vigodskii Ya S, Churochkina N A and Korshak V V 1977 Vysokomol. Soyed. B 1993
(in Russian)
[12] Lavrov S V, Ardashnikov A Ya, Kardash I E and Pravednikov A N 1977 Vysokomol. Soyed.A 1910527
(in Russian)
[13] Lavrov S V, Talankina O B, Vorobiev V D, Iziumnikov A L, Kardash I E and Pravednikov A N 1980Vysokomol.
Soyed.A22188690 (in Russian)
[14] Kim Y J, Glass T E, Lyle G D and McGrath J E 1993Macromolecules26134458[15] KuznetsovA A, Tsegelskaya A Yu andBelovM Yu 1999 Proc. 5th European Technical Symp. on Polyimides and
High Performance Functional Polymers (ISIM-Mon tpellier, France, Ma y 35, 1999)Abstracts and Posters,
PI.14
[16] Laurov S V, Kuznetsov A A, Berendyaev V I, Kotov B V, Tsegelskaya A Yu and Kotina N B Russian patent
specification1809612
[17] Laurov S V, Kuznetsov A A, Berendyaev V I and Kotov BRussian patent specification2070210
[18] Kuzetsov A A, Tsegelskaya A Yu, Belov M Yu, Berendyaev V I, Lavrov S V, Semenova G K, Izyumnikov A L,
Kozlova N V and Kotov B V 1998Macromol. Symp.28203
[19] Kuznetsov A A, Lavrov S V, Berendyaev V I and Kotov B VProc. 5th European Technical Symp. on Polyimides
and High Performance Functional Polymers (ISIM-Montpellier, France, May 35, 1999)Abstracts and
Posters, PI.7
[20] Stille J K 1972Condensation Monomersed J K Stille and T W Kempbell (New York: WileyInterscience)
[21] Kuznetsov A A, Semenova G K, Egorov I D, Berendyaev V I and Kotov B V Proc. 5th European Technical
Symp.on Polyimidesand HighPerformanceFunctionalPolymers (ISIM-Montpellier, France, May 35, 1999)
Abstracts and Posters, PII.4[22] Kuznetsov A A, Semenova G K, Egorov I D, Berendyaev V I, Ahmetieva E I and Kotov B V 2000Vysokomol.
Soyed.42453 (in Russian)
[23] Nosova G I, Koton M M, Mikhailova N V, Lyubimova G V and Denisov V M 1987Izv. Akad. Nauk USSR 1987
1810 (in Russian)
Recommended